Farklı rezin esaslı yapıştırma simanlarının seramik restorasyon altında polimerizasyon miktarının sertlik ölçümü ile değerlendirilmesi
Evaluation of different resin based luting cements degree of conversion by microhardness measurment
- Tez No: 426983
- Danışmanlar: PROF. DR. MİNE BETÜL ÜÇTAŞLI
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Akrilik reçineler, Dental bonding, Dental materyaller, Dental porselen, Dental restorasyon, Dental çimentolar, Kompozit reçineler, Mikrosertlik, Acrylic resins, Dental bonding, Dental materials, Dental porcelain, Dental restoration, Dental cements, Composite resins, Microhardness
- Yıl: 2015
- Dil: Türkçe
- Üniversite: Gazi Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Diş Hastalıkları ve Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu tez çalışmasının amacı, üç farklı kendinden adeziv rezin siman ile bir adet kompozit rezin yapıştırma simanın direkt ve 2mm kalınlıkta seramik materyal üzerinden ışık ile polmerizasyon derecesinin, 24 saat, 1 hafta ve 1 ay sonra yüzey mikrosertlik testi ile değerlendirilmesidir. Gazi Üniversitesi Diş Hekimliği Fakültesi, Diş Hastalıkları ve Tedavisi Ana Bilim Dalı Araştırma Laboratuarında gerçekleştirilen bu çalışmada, LED ışık cihazı kullanılarak, üç farklı kendinden adeziv rezin siman ve bir adethem ışık hem kimyasal sertleşen kompozit rezin yapıştırma simanın direkt ve 2mm kalınlığında feldspatik seramik blok üzerinden 40 sn ışık uygulaması ile polimerizasyon sonrası, 24 saat, 1 hafta ve 1 ay 37°C etüvde bekletildikten sonra mikro sertlik ölçümleri yapıştırma siman örneklerin alt ve üst yüzeylerinde gerçekleştirildi. İstatistiksel analiz, Friedman'ın iki yönlü ANOVA, Mann Whitney U ve Kruscal Wallis-H testleri ile %95 güven aralığında gerçekleştirilmiştir.Kruskal Wallis-H testinde, istatistiksel farklılık bulunan test gruplarına, Pos-Hoc çoklu karşılaştırma testi uygulanmıştır. Bütün test gruplarında, 2 mm seramik blok üzerinden ışık uygulaması sonrası test örneklerin üst yüzeylerinden elde edilen sertik sonuçları alt yüzeylerden elde edilen sertlik sonuçlardan yüksek bulunmuştur. Seramik blok uygulamadan ışık uygulanan test grupları içinden, grup I kendinden adeziv rezin siman grubunda, alt ve üst yüzeyler arasında fark gözlenmez iken (p>0,05) diğer gruplarda üst yüzeylerde daha yüksek sertlik değerleri gözlenmiştir (p<0,05). Test materyalleri karşılaştırıldığında, seramik blok uygulamadan ışık uygulanan gruplar karşılaştırıldığında, en yüksek sertlik değerleri dual sertleşen kompozit rezin yapıştırma siman grubunda, grup III, bulunmuştur. Grup III dual sertleşen kompozit rezin yapıştırma siman grubunda, ışık uygulamadan kimyasal polimerizasyon oluşumu beklenen grupta, simanın sertlik ölçümleri gerçekleştirilecek kadar polymerize olmadığı gözlenmiştir. Ancak, kendinden adeziv rezin siman test gruplarında ışık uygulamadan, kimyasal sertleşmeye bırakılan test örneklerinde yüzey sertlik ölçümleri gerçekleştirilmiştir.
Özet (Çeviri)
The aim of this study was to evaluate the degree of polymerization of three different self adhesive resin cements and a dual cure composite resin luting cement directly and under 2mm ceramic bloc, after 24 hour, 1 week and 1 month time interval at 37°C incubator utilizing with surface microhardness test. The study was performed at University of Gazi, Faculty of Dentistry, Department of Restorative Dentistry laboratory. Three different self adhesive resin cements and a dual cure composite resin luting cement was cured directly and over 2mm ceramic bloc with a LED light curing unit for 40 seconds light irradiation. After 24 hour, 1week and 1 month time interval microhardness tests were performed at upper surface and lower surface of test specimens. Statistical analysis was performed Friedman's two-way ANOVA, Mann Whitney U and Kruskal Wallis-H test at 0.05 significant levels. When significant differences were found at Kruskal Wallis-H test, Pos-Hoc Multiple comparison test were used. When light cured over 2mm ceramic bloc upper surfaces of tested specimens showed higher microhardnessvalues than lower surfaces for all tested groups. When the specimens light cured without a ceramic bloc, group I self adhesive resin cement group showed similar microhardness values at upper and lower surfaces, however upper surfaces of other groups showed higher microhardness values than lower surfaces. Comparing the tested materials, light cured without a ceramic bloc, group III dual cure composite resin luting cement showed the highest microhardnes values. Microhardness test measurement was not able to perform at dual cure composite resin luting cement group III without light curing other means chemically curing alone, however all self adhesive resin cements cured without light application.
Benzer Tezler
- Bazı esterlerin kinetik incelenmesi ve termodinamik parametrelerin belirlenmesi
Kinetic study and detesmination of thermodnamic parameters of some esters
İBRAHİM TAŞ
Yüksek Lisans
Türkçe
1986
Kimya MühendisliğiUludağ ÜniversitesiKimya Ana Bilim Dalı
PROF. DR. MUSTAFA CEBE
- İzmir'de bazı yolların kapatılarak yaya bölgeleri oluşturma da kent peyzajını geliştirme açısından yeniden planlanması üzerinde araştırmalar
Başlık çevirisi yok
BAHAR TÜRKYILMAZ
Yüksek Lisans
Türkçe
1985
Şehircilik ve Bölge PlanlamaEge ÜniversitesiŞehir ve Bölge Planlama Ana Bilim Dalı
- Testosteron dihidrotestosteron ve östrojenin benign prostat hiperplazisindeki etyolojik rolleri
The roles of testosterone, dihydrotestosterone and estradiole on the etiology of benign prostatic hyperplasia
HALUK TOKUÇOĞLU
- Süt formüllerinin tüketim uygulamaları ve süt formüllerinin C vitamini içeriği ile pH değerleri
Başlık çevirisi yok
GÖNÜL VAROL
Yüksek Lisans
Türkçe
1986
Besin Hijyeni ve Teknolojisiİstanbul ÜniversitesiÇocuk Gelişimi Ana Bilim Dalı
DOÇ. DR. TÜRKAN KUTLUAY
- Türkiye'de aile planlaması çalışmalarında erkeklerin önemi, hastane personeli ile fabrika işçilerinin doğum kontrol yöntemlerine karşı tutum ve davranranışlarında farklılığın araştırılması
Başlık çevirisi yok
KAMİL MALKOÇLU
Yüksek Lisans
Türkçe
1987
Demografiİstanbul ÜniversitesiAile Sağlığı Ana Bilim Dalı
DOÇ. DR. DERİN KÖSEBAY