MPS kuşatımlı-CdS nano yapılar içeren ince filmlerin optik özelliklerinin incelenmesi

Investigation of optical properties of MPS-capped CdS nanostructures containing thin films

PDF İndir

  1. Tez No: 442533
  2. Yazar: ANIL KAR
  3. Danışmanlar: DOÇ. DR. MUSTAFA OKUTAN, DR. KENAN KOÇ
  4. Tez Türü: Yüksek Lisans
  5. Konular: Fizik ve Fizik Mühendisliği, Physics and Physics Engineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2016
  8. Dil: Türkçe
  9. Üniversite: Yıldız Teknik Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Fizik Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 58

Özet

Bu çalışmada, kolloidal CdS kuantum noktaları MPS (3-mercaptopropyltrimethoxysilane) molekülünün farklı molar oranları kullanılarak sentezlenmiştir. MPS hem kuşatım ajanı olarak hem de SiO2 ağı üretiminde kullanılmıştır. Döndürme yöntemi kullanılarak kolloidal nanoparçacıkları cam yüzey üzerine kaplanmıştır. Bu çalışmada üretilen öreneklerin söndürme katsayısı, kırılma indisi, dielektrik sabiti, ilk eksiton piki enerji (E¬1s-1s) değerleri ve kalınlık değerleri tespit edilmiştir. Sonuçlara göre filmlerin geçirgenlik değerleri MPS oranının artışı ile artış göstermektedir. Diğer tarftan, filmlerin kırılma indisleri farklı MPS konsantrasyonları ile geniş bir değer aralığında (550nm' de 2.1-1.6 ) değişkenlik göstermektedir. Filmlerin kırılma indisi değerleri bulk CdS yarıiletkeni ile saf haldeki SiO2 filminin kırılma indisi değeri aralığında bulunmuştur. Elde edilen sonuçlara göre, kırılma indisi değerleri MPS konstrasyonun molar oranı artışı ile azalmaktadır. Bunun sebebi MPS' nin molar oranı artışı SiO2 ağında artışa sebeb olmakta ve böylecede karşıt olarak CdS miktarında azalmaya neden olmasıdır. Buda göstermiştirki, MPS konsantrasyonu ayarlanarak, bu filmler istenen optiksel özeliklerine ulaşılabilir. Ayrıca sonuçlar gösteriyorki, söndürme katsayısı ve filmlerin soğruma sınırları, MPS konsantrasyonu artışı ile kuantum sınırlamasının etkisi nedeniyle düşük dalga boylarına doğru kaymaktadır. Dolayısı ile E¬1s-1s değerleri MPS konsantrasyonun artşı ile artmaktadır. Bunun nedeni; daha yüksek MPS molar konsantrasyonlarında daha küçük CdS kuantum noktaların elde edilmesidir.

Özet (Çeviri)

In this study, colloidal CdS quantum dots (QDs) were synthesized with various molar ratios of 3-mercaptopropyltrimethoxysilane (MPS) molecules. MPS was used as a capping agent and also to create a SiO2 network. Spin coating method was used for deposition of the colloidal nanoparticles on a glass substrate. In this study, extinction coefficient, refractive index, dielectric constant, first exciton peak energy (E¬1s-1s) values and thickness of the samples were determined. According to the results, the transmittance values of the films increase with increasing MPS ratio. Additionally, the refractive index values of the films were varied over a large range (2.1-1.6 at 550 nm) by varying the MPS concentration. The refractive index values of the films were found to be between the refractive index of the bulk CdS and that of refractive index of pure SiO2 film. According to the results, the results show that the refractive index values were decreased as the molar concentration of MPS was increased. This is because that increasing the molar ratio of MPS has led to an increase in the network of SiO2 and so conversely has led to a decrease the amount of CdS. It was shown that the films can be obtained in the desired optical properties by tuning MPS concentration. The results also show that, the extinction coefficient and so the absorption edges of the samples shift towards lower wavelengths with the increasing concentration of MPS due to quantum confinement effect. Hence, the E¬1s-1s values increase with the increasing concentration of MPS. It is because that the smaller size of CdS QDs was obtained at the higher molar concentration of MPS.

Benzer Tezler

  1. Tez No

    310587

    II-VI grubu yarıiletken nano yapılı ince filmlerin sol-jel yöntemi ile üretimi

    The production of nanostructured thin films using II-VI group semiconductors by sol-gel method

    KENAN KOÇ

    Doktora

    Türkçe

    Türkçe

    2011

    Fizik ve Fizik Mühendisliğiİstanbul Teknik Üniversitesi

    Fizik Mühendisliği Ana Bilim Dalı

    PROF. DR. FATMA Z. TEPEHAN

  2. Tez No

    343556

    Mukopolisakkaridoz Tip I (MPS I) hastalarında IDUA gen mutasyonlarının analizi

    Analysis of IDUA gene mutations in patients with mucopolysaccharidosis type i (MPS I)

    NAZENTE ATÇEKEN

    Yüksek Lisans

    Türkçe

    Türkçe

    2013

    BiyolojiAksaray Üniversitesi

    Biyoloji Ana Bilim Dalı

    YRD. DOÇ. DR. MEHMET KARACA

    PROF. DR. RIZA KÖKSAL ÖZGÜL

  3. Tez No

    201647

    MPS modüler üretim sisteminin bilgisayar destekli gerçek zamanlı kontrolü ve teknik eğitime uygulanması

    Computer aided real time control of MPS modular production system and technical education application

    SEZAİ TAŞKIN

    Doktora

    Türkçe

    Türkçe

    2007

    Elektrik ve Elektronik MühendisliğiMarmara Üniversitesi

    Elektrik Eğitimi Ana Bilim Dalı

    DOÇ. DR. KORAY TUNÇALP

    YRD. DOÇ. DR. HASAN ERDAL

  4. Tez No

    452785

    Miyofasial ağrı sendromunda radial ekstrakorporal şok tedavisi

    Myofascial pain syndrome radial extracorporeal shock treatment

    KERİME SAVAŞ

    Tıpta Uzmanlık

    Türkçe

    Türkçe

    2011

    Fiziksel Tıp ve RehabilitasyonKocaeli Üniversitesi

    Fiziksel Tıp ve Rehabilitasyon Ana Bilim Dalı

    PROF. DR. ERBİL DIRSUN

  5. Tez No

    118830

    Mukopolisakkaridoz tip IVA mutasyonlarının moleküler genetik analizi

    Molecular genetic analysis of mucopolysaccaridosis type IVA mutations

    MÜGEN TERZİOĞLU

    Doktora

    Türkçe

    Türkçe

    2002

    Tıbbi BiyolojiHacettepe Üniversitesi

    Tıbbi Biyoloji Ana Bilim Dalı

    DOÇ.DR. SERAP EMRE

Geri Dön