Farklı preparasyon şekillerinin porselen laminaların rengine adaptasyonuna ve kırılma dayanımına etkisinin incelenmesi
The evaluation of color adaptation and fracture resistance of laminate veneers with different preparation designs
- Tez No: 443766
- Danışmanlar: PROF. DR. YASEMİN ÖZKAN
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Dental materyaller, Dental mine, Dental porselen, Dental restorasyon, Dental stres analizi, Dental materials, Dental enamel, Dental porcelain, Dental restoration, Dental stress analysis
- Yıl: 2016
- Dil: Türkçe
- Üniversite: Marmara Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Amaç: Bu çalışmanın amacı farklı preparasyon dizaynlarının lamina restorasyonların rengine, adaptasyonuna ve kırılma dayanımına etkisinin incelenmesidir. Gereç ve Yöntem: 75 adet çekilmiş maksiller santral diş 5 farklı preparasyon derinliği grubuna ayrıldı (P) (n:15): P1: 0,3 mm derinliğinde preparasyon, tamamen minede, P2: 0,5 mm derinliğinde preparasyon, mine-dentin kompleksinde, P3: 1 mm derinliğinde preparasyon, tamamen dentinde, P4: preparasyonsuz, yalnızca yüzey pürüzlendirmesi yapılmış ve P5: kontrol grubu olarak belirlenmiştir. Restorasyonlar IPS e.max (Ivoclar, Vivadent) kullanılarak hazırlanmıştır. Restorasyonlara iki farklı renkte deneme pastası uygulanarak (Variolink Veneer Try-in, Ivoclar, Vivadent), spektrofotometre (Vita Easyshade Spectrophotometer) ile renk ölçümleri yapılmış, daha sonra Syntac Classic Adhesive sistem ve Variolink Veneer resin simantasyon sistemi (Ivoclar, Vivadent) kullanılarak simante edilmiş ve tekrar renk ölçümü yapılmıştır. Restorasyonların marjinal adaptasyonları ışık mikroskopu ve 'scanning electron' mikroskop kullanılarak ölçülmüştür. Kırılma dayanımı için, restorasyonlar 900 açıyla, test edilen dişin lingual yüzeyinden kırılma noktasına kadar yüklenmiştir. İstatistiksel analiz Varyans Analizi ve Tukey's Multiple Range Test kullanılarak yapılmıştır. Bulgular: Final renk değerlerinin, restorasyonların kalınlığına ve kullanılan siman rengine göre değiştiği görülmüştür. Marjinal adaptasyon değerlerinin karşılaştırılmasında gruplar arasında derinliğe bağlı olarak istatistiksel olarak anlamlı fark görülmemiştir (p<0.05). Kırılma dayanımının incelenmesinde ise, en yüksek kırılma dayanımı değeri P2 (322,86 N) grubunda, en düşük kırılma dayanımı ise P3 (219,21 N) grubunda ölçülmüştür. Sonuçlar: Lamina vener restorasyonlarda seramik kalınlığı arttıkça alttaki diş dokusunun ve rezin simanın rengini maskeleme kapasitesi artmaktadır. Marjinal aralık değerlerinin, preparasyon derinliği ile bir ilişkisi yoktur. Kırılma direnci 0,5 mm preparasyon derinliğinde, 0,3 mm, 1mm ve preparasyonsuz lamina vener restorasyonlara göre daha yüksektir.
Özet (Çeviri)
Purpose: The aim of this study is to examine the marginal adaptation and the fracture load of ceramic veneers with different preparation depths and the evaluation of effects of trial pastes on colour before cementation. Materials and Methods: 75 extracted intact human maxillary central incisors are prepared in 5 different preparation dephts (P) (n: 15): P1: 0,3 mm depth of preparation, preparation is performed entirely in enamel. P2: 0.5 mm. depth of preparation, preparation is performed in enamel and dentin complex. P3: 1 mm. depth of preparation, preparation is performed entirely in dentin. P4: Prepless, only surface roughening is applied. P5: Unrestored, intact teeth as control. Ceramic veneers are fabricated with IPS Empress (Ivoclar, Vivadent). Following this process, the color of restorations is measured with the different colours trial pastes for each group (Variolink Veneer Try-in, Ivoclar Vivadent). Color measurements are performed with an intraoral spectrophotometer (Vita Easyshade Spectrophotometer) before and after preparation. The marginal adaptation of veneers are evaluated by light microscope and scanning electron microscope after cementation with Syntac Classic Adhesive system and Variolink Veneer (Ivoclar) resin cement. Finally, veneers are loaded until fracture at a 90º angle to the lingual surface of the test tooth. Statistical analyses are performed using Variance Analysis and the Tukey's Multiple Range Test. Results: It is observed that the final color of the restoration is affected by the thickness of laminate and the trial paste. In marginal adaptaion measurement, there is not statistical difference between groups according to preparation depht (p<0.05). The highest fracture resistance is found in P2 group (322,86 N) and the lowest value is observed in P3 group (219,21 N). Conclusion: The increase in ceramic thickness of laminate veneer provides better masking ability of underlying tooth and resin cement. There is not a correlation between marginal adaptation and preparation depht. The fracture resistance is found higher in 0,5 mm preparation depht than 0,3 mm, 1 mm preparation dephts and prepless laminate veneers.
Benzer Tezler
- Farklı zirkonya alt yapı tasarım şekillerinin kuron protezlerinin kırılma dayanımı üzerine etkisinin incelenmesi
The influence of different zirconia coping designs on the fracture load of all ceramic restorations
SEDA ERALP
Doktora
Türkçe
2017
Diş Hekimliğiİstanbul ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. MEHMET CUDİ BALKAYA
- CAD/CAM oklüzal vener restorasyonların kırılma dayanımlarının farklı materyal kalınlıklarına ve preparasyon dizaynlarına göre karşılaştırılması
Comparison of the fracture strength of CAD/CAM oclusal venery restorations according to different material thickness and preparation design
PINAR ŞEŞEN
Doktora
Türkçe
2022
Diş Hekimliğiİstanbul ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. OLCAY ŞAKAR
- Preparation of new polymeric sorbents for removal of boron from water
Sudan bor giderilmesi için yeni polimerik reçinelerin hazırlanması
GÜLÇİN TORUNOĞLU TURAN
Doktora
İngilizce
2019
Polimer Bilim ve Teknolojisiİstanbul Teknik ÜniversitesiPolimer Bilim ve Teknolojisi Ana Bilim Dalı
PROF. DR. BAHİRE FİLİZ ŞENKAL
- Farklı kök kanal preparasyon şekillerinin düz ve eğimli köklere sahip mandibular molar dişlerin stres dağılımı üzerindeki etkisi: Sonlu elemanlar stres analizi
Effect of different root canal preparation types on the stress distribution of mandibular molar with straight and curved roots: Finite element analysis
YAPRAK CESUR
Diş Hekimliği Uzmanlık
Türkçe
2019
Diş HekimliğiHacettepe ÜniversitesiEndodonti Ana Bilim Dalı
PROF. DR. AHMET SERPER
- Full kuronlarda farklı preparasyon yaklaşım açıları ve basamak şekillerinin oklüzal siman film kalınlığı üzerine etkinliğinin araştırılması
The Investigation of the cement film thickness beneath full crown restorations prepared by various preparation convergence angles and marginal configurations
ENDER TUKAY