Polihalojenli organik moleküllerin elektrokimyasal indirgenmesi ile karbon nanoyapıların sentezi ve elektrokimyasal kapasitör uygulamaları
Synthesis of carbon nanostructures by electrochemical reduction of polyhalogenated organic molecules and their electrochemical capacitor applications
- Tez No: 532363
- Danışmanlar: PROF. DR. DUYGU EKİNCİ
- Tez Türü: Doktora
- Konular: Kimya, Chemistry
- Anahtar Kelimeler: Polihalojenli organik moleküller, elektrokimyasal indirgeme, termal tavlama, karbon nanoyapılar, süperkapasitör, Polyhalogenated organic molecules, electrochemical reduction, thermal annealing, carbon nanostructures, supercapacitor
- Yıl: 2018
- Dil: Türkçe
- Üniversite: Atatürk Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Kimya Ana Bilim Dalı
- Bilim Dalı: Analitik Kimya Bilim Dalı
- Sayfa Sayısı: 252
Özet
Bu tez çalışmasında, aşağıdan-yukarıya yöntemi temelince küçük moleküllerden yola çıkarak büyük molekül ağırlığına sahip karbon nanoyapıları sentezlemeyi amaçladık. Bu doğrultuda karbon nanoyapıların sentezi için üç farklı yaklaşım izlendi. (i) Öncelikle, hekzagonal polihalojenli aromatik moleküllerin (hekzaflorobenzen (HFB), hekzaklorobenzen (HCB) ve hekzabromobenzen (HBB)) aprotik çözücülerde elektrokimyasal indirgenmesi sonucunda açığa çıkan aril radikallerinin, aril radikal-aril radikal kaplingi ile Au ve Si elektrotlar üzerinde karbon temelli polimer filmler sentezlendi. (PHFB, PHCB ve PHBB). Daha sonra polimer film kaplı elektrotlar, 400°C'de 30 dakika tavlanarak grafen benzeri film oluşumu sağlandı (PHFB-400, PHCB-400 ve PHBB-400). (ii) Pentagonal hekzaklorosiklopentadien (HCP) organik molekülünün elektrokimyasal indirgenmesi ile karbon nanoyapıların sentezi Au elektrot üzerinde gerçekleştirildi (PHCP). Polimer film kaplı Au elektrot, 400°C'de 30 dakika tavlanarak ince karbon film örgüsüne ulaşılabildi (PHCP-400) (iii) Hekzagonal ve pentagonal polihalojenli organik moleküllerin elektrokimyasal indirgenmesi ile nanoçiçek ve nanomantar benzeri karbon nanoyapıların sentezi gerçekleştirildi. Bu bölümde pentagonal halkaların sonuç karbon yapılarının morfolojik ve kimyasal karakteristiklerine etkisini ortaya koyabilmek için hekzagonal ve pentagonal polihalojenlenmiş halkaların eş zamanlı elektrokimyasal redüksiyonu ile karbon filmleri hazırlandı. Bu amaç doğrultusunda, hekzagonal hekzaklorobenzen ve pentagonal hekzaklorosiklopentadien (HCP) molekülleri elektrokimyasal sentezler için öncü moleküller olarak kullanıldı. HCB ve HCP organik moleküllerinin molar oranları değiştirilerek (2/2, 2/1.2, 2/0.6) elektrokimyasal indirgenme ile farklı karbon filmleri hazırlandı (PHCB/PHCP:2/2, PHCB/PHCP:2/1.2 ve PHCB/PHCP:2/0.6) ve filmler 400°C'de 30 dakika tavlanarak, kararlı film yapısına ulaşıldı (PHCB/PHCP:2/2-400, PHCB/PHCP:2/1.2-400 ve PHCB/PHCP:2/0.6-400). Bu polihalojenli moleküllerden sentezlenen karbon filmlerin karakterizasyonu için taramalı elektron mikroskopi (SEM), taramalı tünelleme mikroskopi (STM), geçirimli elektron mikroskopi (TEM), Raman spektroskopi, X-ışını fotoelektron spektroskopi (XPS), X-ışını difraksiyon (XRD) teknikleri kullanıldı. Ayrıca bütün karbon filmlerin kapasitans performansı, dönüşümlü voltametri (CV), galvanostatik şarj-deşarj (GCD) ve elektrokimyasal empedans spektroskopisi (EIS) ile değerlendirildi. 2018, 227 sayfa
Özet (Çeviri)
In this thesis, we aimed to synthesize large molecular weight carbon nanostructures starting from small molecules based on the bottom-up method. Accordingly, three different approaches were developed for the synthesis of carbon nanostructures. (i) First, carbon-based polymer films were synthesized on the Au or Si electrodes with the aryl radical-aryl radical coupling of the aryl radicals resulting from the electrochemical reduction of hexagonal polyhalogenated aromatic molecules (hexafluorobenzene (HFB), hexachlorobenzene (HCB) and hexabromobenzene (HBB)) in aprotic solvents. Then the polymer film (PHFB, PHCB and PHBB) coated Au electrodes were annealed at 400°C for 30 minutes to produce graphene-like film. (PHFB-400, PHCB-400 and PHBB-400). (ii) Synthesis of carbon nanostructures by electrochemical reduction of pentagonal hexachlorocyclopentadiene (HCP) organic molecule was performed on Au electrode (PHCP). The polymer film-coated Au electrode was annealed at 400°C for 30 minutes to yield a thin carbon film lattice (PHCP-400). (iii) By electrochemical reduction of hexagonal and pentagonal polyhalogenated organic molecules, synthesis of nano-flower and nanomushroom-like carbon nanostructures was performed. Carbon films were prepared by simultaneous electrochemical reduction of hexagonal and pentagonal polyhalogenated rings in order to demonstrate the effect of pentagonal rings on the morphological and chemical characteristics of the resulting carbon structures. For this purpose, hexagonal hexachlorobenzene and pentagonal hexachlorocyclopentadiene (HCP) molecules were used as precursor molecules for electrochemical synthesis. Different carbon films were prepared with electrochemical reduction by various molar ratios of HCB and HCP organic molecules (2/2, 2/1.2, 2/0.6) (PHCB/PHCP:2/2, PHCB/PHCP: 2/1.2 and PHCB/PHCP:2/0.6) and films annealed at 400°C for 30 minutes to achieve stable film structure (PHCB/PHCP:2/2-400, PHCB/PHCP:2/1.2-400 and PHCB/PHCP:2/0.6-400) Characterization of carbon films synthesized from these polyhalogen molecules were carried out by scanning electron microscopy (SEM), scanning tunneling microscopy (STM), transmission electron microscopy (TEM), Raman spectroscopy, X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD) techniques. Also, the capacitance performance of the films was evaluated by means of cyclic voltammetry, galvanostatic charge-discharge, and electrochemical impedance spectroscopy. 2018, 227 pages
Benzer Tezler
- Monoen ve dien yapılı polihalojenli organik bileşiklerden S- ve N- substitue organik bileşiklerin sentezi
The Synthesis of S- and N-substituted organic compounds from monoen and dien structure having polyhalogenated organic compounds
NİHAL YILMAZ BOZKURT
- Halodienlerden yeni tiyoeterlerin sentezi
The synthesis of new thioethers from halodienes
AMAÇ FATİH TUYUN
Yüksek Lisans
Türkçe
2007
Kimyaİstanbul ÜniversitesiKimya Ana Bilim Dalı
PROF.DR. CEMİL İBİŞ
YRD. DOÇ. DR. GÖKŞİN AYDINLI
- The synthesis of S- and N,S-substituted new nitrodienes from 2-nitrodienes with allyl and pyridine thiols
Alil ve piridin tiyollerler 2-nitrodienlerden S- ve N,S--sübstitüe yeni nitrodienlerin sentezi
NEŞE ŞENTÜRK MERMER
- 2-nitrohalobuta-1,3-dien'in merkaptokumarin ile reaksiyonundan S- ve N, S-sübstitüe bileşiklerin sentezi
The synthesis of S-and N,S-substituted compounds from the reactions of 2-nitrohalobuta-1,3-diene with mercapto coumarin
FİLİZ AVCI
Yüksek Lisans
Türkçe
2008
Kimyaİstanbul ÜniversitesiKimya Ana Bilim Dalı
DOÇ. DR. F. GÜLAY KIRBAŞLAR
PROF. DR. CEMİL İBİŞ
- Nitrodienlerin alifatik ve aromatik tiyolatlarla reaksiyonundan yeni mono- ve politiyoeterlerin sentezi
Synthesis of mono- and polythioethers from the reaction of nitrodienes with aliphatic and aromatic thiolates
AMAÇ FATİH TUYUN