Farklı CAD/CAM hibrit materyallerin çiğneme simülatörü sonrası yüzey aşınmalarının incelenmesi
Investigation of surface wear of different CAD/CAM hybrid materials after chewing simulator
- Tez No: 532653
- Danışmanlar: PROF. DR. NURAN YANIKOĞLU
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: CAD/CAM materyaller, çiğneme simülatörü, polimer-infiltre seramik, yüzey aşınması, CAD/CAM materials, chewing simulator, polymer-infiltrated ceramic, surface wear
- Yıl: 2018
- Dil: Türkçe
- Üniversite: Atatürk Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 114
Özet
Amaç: Bu çalışmanın amacı, 3 hibrit ve 1 feldspatik seramikten oluşan 4 CAD/CAM monolitik materyalin çiğneme simülatörü sonrası hem aşınma miktarlarını hem de sebep oldukları karşıt aşınmayı incelemektir. Materyal ve Metot: Çalışmamızda Vita Enamic, Lava Ultimate ve Cerasmart hibrit seramikler ile kontrol grubu olarak feldspatik seramik olan CEREC Blocs CAD/CAM bloklar kullanıldı. Bloklar 2 mm kalınlığında hazırlanarak her gruptan 8 örnek olacak şekilde 4 grup oluşturuldu. Tüm örneklere üretici firma önerilerine göre polisaj işlemi uygulandı. Örnekler bilgisayar kontrollü bir çiğneme simülatörüne (50N, 1.6 Hz, lateral hareket: 1mm, dikey hareket: 2 mm) yüklendi ve her örnek için doğal insan minesi sertlik değerine yakın 6 mm çapında Al2O3 antagonist aşındırıcı bilyelerle 400,000 mekanik yüklemeye eş zamanlı olarak 500 termal döngüye tabi tutuldu. Hibrit seramiklerde ve feldspatik seramikteki aşınma hacmi 3-Boyutlu Optik Profilometre ile ölçülürken antagonist bilyelerdeki aşınma miktarı ise çiğneme simülasyonu öncesi ve sonrası ağırlık farkı hesaplanarak kaydedildi. Antagonist bilyelerdeki ölçümler 3'er dakikalık ultrasonik temizleme işlemlerinden sonra yapıldı. Aşınma yüzeyleri ve aşınma paternlerini belirlemek için Taramalı Elektron Mikroskobu kullanıldı. Sonuçlar tek yönlü varyans analizi (ANOVA) ve sonrasında çoklu karşılaştırma için Tukey HSD ve T-Test analiz yöntemleriyle değerlendirildi (p=0.05). Bulgular: CAD/CAM materyallerin yüzey aşınma sonuçları en düşükten en yükseğe sırasıyla CEREC Blocs (0.311 mm3), Vita Enamic, Cerasmart, Lava Ultimate (0.913 mm3) şeklindedir. CEREC Blocs ile Vita Enamic, Cerasmart ile de Lava Ultimate iki grup oluşturmuşlardır ve gruplar arasındaki fark anlamlı iken (p0.05). Antagonist bilyelerin çiğneme simülasyonu sonrası ağırlık kayıpları değerlendirildiğinde, Cerasmart ile Lava Ultimate arasında anlamlı fark bulunurken diğer gruplarda benzer sonuçlar elde edildi (p˂0.05). Buna göre en fazla Lava Ultimate (0.143 mg) en az ise Cerasmart (0.068 mg) karşıt aşınmaya neden oldu. Sonuç: Hibrit seramikler feldspatik seramiğe göre daha fazla yüzey aşınması gösterdi. Buna karşın Cerasmart ve Vita Enamic hibrit seramiklerin feldspatik seramiğe göre daha az antagonist aşınmaya sebep olduğu gözlendi.
Özet (Çeviri)
Investigation of Surface Wear of Different CAD/CAM Hybrid Materials After Chewing Simulator Aim: The aim of this study is to investigate both the amount of abrasion and the erosive contraction of 4 CAD/CAM monolithic materials consisting of 3 hybrids and 1 feldspar ceramic after the chewing simulator. Material and Method: In our study, we used hybrid ceramics of Vita Enamic, Lava Ultimate and Cerasmart and CEREC Blocs which are feldspar ceramic as control group CAD/CAM blocks. Blocks were prepared in 2 mm thickness and 4 groups were formed as 8 samples from each group. All samples were polished according to the manufacturer's recommendations. The samples were loaded into a computer controlled chewing simulator (50N, 1.6 Hz, lateral motion: 1mm, vertical motion: 2mm) and were loaded with 500 thermal imager, simultaneously with 400,000 mechanical loads of Al2O3 antagonist abrasive balls 6 mm in diameter. The wear volume in hybrid ceramics and feldspar ceramic was measured by 3D Optical Profilometer while the amount of wear in antagonist balls was recorded by calculating the weight difference before and after chewing simulation. The measurements on the antagonist balls were made after 3 minutes of ultrasonic clearance. Scanning Electron Microscopy was used to determine wear surfaces and wear patterns. The results were evaluated by Tukey HSD and T-Test analysis methods for one-way analysis of variance (ANOVA) and multiple comparisons afterwards (p=0.05). Results: Surface abrasion results of CAD/CAM materials are in the form of CEREC Blocs (0.311 mm3), Vita Enamic, Cerasmart, Lava Ultimate (0.913 mm3), respectively. CEREC Blocs and Vita Enamic, Cerasmart and Lava Ultimate formed two groups, while the difference between the groups was significant (p0.05). There was a significant difference between Cerasmart and Lava Ultimate when evaluating weight loss of the antagonist balls after chewing simulation, but similar results were found in other groups (p˂0.05). According to this, Lava Ultimate (0.143 mg) caused the most, Cerasmart (0.068 mg) caused the least antagonistic wear. Conclusion: Hybrid ceramics show more surface wear than feldspar ceramics. On the contrary, Cerasmart and Vita Enamic hybrid ceramics were observed to cause less antagonistic erosion than feldspar ceramics.
Benzer Tezler
- Evaluation of wear and surface roughness after brushing simulator of different CAD/CAM materials
Farklı CAD/CAM materyallerinin fırçalama simülatörü sonrası aşınma ve yüzey pürüzlülüğünün değerlendirilmesi
ÖZGÜR OZAN TANRIKUT
Diş Hekimliği Uzmanlık
Türkçe
2021
Diş HekimliğiVan Yüzüncü Yıl ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DR. ÖĞR. ÜYESİ MEHMET UĞUR
- Farklı hibrit ve seramik materyallerin çiğneme simülatörü ile yaşlandırma sonrası bükülme dirençlerinin değerlendirilmesi
Evaluation of flexural strength of different hybrid and ceramic materials after aging in chewing simulator
ECE BİLDİR ÇAKIN
Diş Hekimliği Uzmanlık
Türkçe
2018
Diş HekimliğiAnkara ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. SEMİH BERKSUN
- Farklı materyaller ile restore edilmiş farklı bağlantı açılarına sahip implant-dayanak sistemlerinin mikro-aralıklarının çiğneme simülatörü ile yaşlandırma sonrası karşılaştırılması
Micro-GAP comparison of implant-abutment systems with different connection angles restored with different materials after aging with chewing simulator
TUĞÇE ÇETİN BİLGİÇ
Doktora
Türkçe
2023
Diş HekimliğiMarmara ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. YILMAZ UMUT ASLAN
- Monolitik cad/cam materyallerinin yapay yaşlandırma sonrası aşınma ve kırılma dayanımlarının araştırılması
Investigation of wear and fracture resistance of monolithic cad/camceramic materials after artificial aging.
ASLIHAN KUTLUK
Doktora
Türkçe
2023
Diş Hekimliğiİstanbul ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. DEĞER ÖNGÜL
- Farklı yüzey işlemlerinin dört farklı monolitik CAD/CAM materyallerinin aşınma miktarına etkisinin in vitro olarak değerlendirilmesi
In vitro evaluation of the effect of different surface treatments on the wear amount of four different monolithic CAD/CAM materials
ZEYNEP ARIKAN
Doktora
Türkçe
2023
Diş HekimliğiMarmara ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. YASEMİN ÖZKAN