Monolitik zirkonya materyalinde kalınlığın, rengin ve simanın sonuç restorasyonun renk parametreleri üzerine etkisi
Effect of monolithic zirconia thickness and resin cementcolor on the color parameters of final restoration
- Tez No: 556515
- Danışmanlar: PROF. DR. CEMAL AYDIN
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Dental materyaller, Dental porselen, Dental restorasyon, Dental çimentolar, Diş kaplamaları, Diş renk değişikliği, Spektrofotometri, Zirkonyum, Zirkonyum oksit, Dental materials, Dental porcelain, Dental restoration, Dental cements, Dental veneers, Tooth discoloration, Spectrophotometry, Zirconium, Zirconium oxide
- Yıl: 2019
- Dil: Türkçe
- Üniversite: Gazi Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışmanın amacı; yüksek dayanıklılığa sahip ancak kimyasal yapıları ve ışık geçirgenlikleri farklı olan ve monolitik kullanıma uygun iki tam seramik materyali olan monolitik zirkonya (MZ) ve lityum disilikat (LDS) cam seramik restorasyonlarda seramik kalınlığı ve kullanılan rezin siman renginin restorasyonun sonuç rengi üzerindeki etkisinin değerlendirilmesidir. Çalışmada; MZ ve LDS materyallerinden 0,5 mm; 1 mm; 1,5 mm kalınlıklarda ve 10x14 mm boyutlarında dikdörtgen şeklinde örnekler hazırlanarak, her grupta 10 adet örnek olmak üzere 6 seramik grubu oluşturuldu. Seramiklerle birlikte renk ölçümlerinin yapılması için 0,2 mm kalınlıkta 10x14 mm boyutlarında ve A1, A2, A3 ve translüsent (Tr) renklerde olmak üzere 4 rezin siman grubu hazırlandı. Seramik örneklerin renk ölçümleri, siman uygulamadan önce ve sonra gün ışığını taklit eden floresan lamba içeren düzenek içinde CIE D65 aydınlatmasına uygun, nötral gri fon içeren ortamda spektrofotometre ile yapıldı. İki ölçüm arasındaki farkın değerlendirilmesi için CIELab renk sistemi tarafından belirlenen“ΔE”formülü kullanıldı. Gruplara ait ΔE değerleri arasındaki farklar Mann Whitney U ve Kruskal Wallis testleri ile değerlendirildi. (p<0,05) ve ΔE≤3 olduğunda renk farklılıkları klinik olarak kabul edilebilir olarak nitelendirildi. Çalışma sonucunda; 0,5 mm kalınlıkta MZ A2 ve A3, LDS ise tüm siman renklerinde klinik olarak kabul edilemeyecek renk değişimi gösterdi. MZ; 1 ve 1,5 mm kalınlıkta iken farklı siman renkleri ile kullanıldığında ΔE değerleri arasında anlamlı fark bulunmadı (p>0,05) ve ΔE≤3 olarak gözlendi. LDS; 1 mm kalınlıkta iken Tr ve A1 renk simanlar 3'den büyük, 1,5 mm kalınlıkta ise tüm siman renkleri ile aralarında anlamlı fark göstermeyen ve 3 civarında olan ΔE değerleri gösterdi.
Özet (Çeviri)
The aim of this study is; to evaluate the effect of the ceramics thickness and the resin cement color on the resultant color of the monolithic zirconia (MZ) and lithium disilicate (LDS) glass ceramic restorations which are suitable for monolithic use. Both ceramics are high strength but have different chemical structures and light transmittance characteristics. In this study; 0,5 mm; 1 mm; 1,5 mm in thickness and 10x14 mm in size rectangular samples from monolithic zirconia and lithium disilicate ceramic materials were prepared. Six ceramic groups, including 10 samples in each group were formed. For making color measurements with ceramics, 4 cement groups of A1, A2, A3 and translucent (Tr) colors were prepared 0,2 mm in thickness and 10x14 mm in sizes. Color measurements before and after cementation were made by using spectrophotometre device in an apparatus containing a fluorescent lamp that simulate the daylight with neutral gray background suitable for CIE D65 illumination. After the color measurement, the color difference was calculated using“ΔE”formula, which was determined by the CIE Lab color system to evaluate the color difference. Data were assessed by Mann Whitney U and Kruskal Wallis tests (p<0.05). Statistical evaluation revealed that clinically unacceptable color difference were observed for 0,5 mm MZ with A2 and A3 cements and for 0,5 mm LDS with all cement colors. Color difference was not statistically different when 1 mm and 1,5 mm MZ were used with different cement colors (p>0,05) and ΔE≤3 was found. When 1 mm LDS used with Tr and A1 cements color difference was higher than 3 and color difference was not statiscilly different and approximately 3 when 1,5 mm LDS was used with when all cement colors.
Benzer Tezler
- Farklı CAD-CAM seramik materyallerin kalınlıklarının ölçüm yapılan arka zemin tipine göre maskeleme yeteneğine etkisi ve yarı saydamlığın değerlendirilmesi
Effect of thickness of different CAD-CAM ceramic materials on masking ability according of the measured background TYPE and evaluation of translucency
TANSU BURSALI
Diş Hekimliği Uzmanlık
Türkçe
2022
Diş HekimliğiSelçuk ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. İSA YÖNDEM
- Restorasyon kalınlığının ve rezin simanın monolitik zirkonyumun renk ve translüsensliğine etkisinin incelenmesi
Investigation of effect of restoration thickness and cement on color and translucency of monolithic zirconia ceramics
MERVE KÖSEOĞLU
Diş Hekimliği Uzmanlık
Türkçe
2018
Diş HekimliğiAtatürk ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. FUNDA BAYINDIR
- Farklı translusenslikteki monolitik zirkonyumun renk ve translusensliğine kalınlığın ve rezin siman renginin etkisinin değerlendirilmesi
Evaluation of the effect of thickness and resin cement color on color and translucency of monolithic zirconium with different translucency
BERKAY BOZCA
Diş Hekimliği Uzmanlık
Türkçe
2021
Diş HekimliğiRecep Tayyip Erdoğan ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. MURAT ALKURT
- Farklı kalınlık ve translusensideki monolitik zirkonyanın farklı dayanak tipleri ile optik özelliklerinin değerlendirilmesi
Evaluation of the optical properties of monolithic zirconia of different thickness and translusency with different abutment types
GÜZİN GEROĞLU YILMAZ
Diş Hekimliği Uzmanlık
Türkçe
2021
Diş HekimliğiKaradeniz Teknik ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. SEDANUR TURGUT
- INFLUENCE OF THICKNESS, TRANSLUCENCY AND RESIN CEMENT SHADES ON THE FINAL COLOR AND TRANSLUCENCY OF CAD / CAM MATERIALS
KALINLIĞIN, TRANSLÜSENSİNİN VE SİMAN RENGİNİN CAD / CAM MATERYALLERİNİN FİNAL RENGİNE VE TRANSLÜSENSİSİNE OLAN ETKİSİ
SİNEM ALBAYRAK
Doktora
İngilizce
2021
Diş HekimliğiYeditepe ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. PINAR KURSOĞLU