Ostenitik krom-nikel çeliğinde dört karbon içeren bazı alkollerin korozyon inhibitör etkilerinin karbon-karbon bağ türüne bağlı olarak incelenmesi
Başlık çevirisi mevcut değil.
- Tez No: 58341
- Danışmanlar: DOÇ. DR. SEMRA BİLGİÇ
- Tez Türü: Yüksek Lisans
- Konular: Kimya, Chemistry
- Anahtar Kelimeler: Ostenitik çelik, koıo/jon, koru/yon hızı, tılkol, inhibitor, Alkoller, Korozyon, austenitic steel, corrosion, corrosion rate, alcohol, inhibitor, Alcohols
- Yıl: 1997
- Dil: Türkçe
- Üniversite: Ankara Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Kimya Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
ÖZET Yüksek Lisans Tezi OSTENİTİK KROM-NİKEL ÇELİ?İNDE DÖRT KARBON İÇEREN BAZI ALKOLLERİN KOROZYON İNHİBİTÖR ETKİLERİNİN KARBON-KARBON BA? TÜRÜNE BA?LI OLARAK İNCELENMESİ Mükerrem ŞAHİN Ankara Üniversitesi Fen Bilimleri Enstitüsü Kimya Anabilim Dalı Danışman: Doç. Dr. Semra BİLGİÇ 1997, Sayfa: 68 Jüri: Doç. Dr. Semra BİLGİÇ Doç. Dr. Mübeccel ERGUN Prof. Dr. Abbas AKSÜT Bu çalışmada, ostenitik krom-nikel çeliğinin sülfürik asit ortamındaki korozyonuna dört karbonlu, bütan-1-ol, 2-büten-l-ol ve 2-bütin-l-ol gibi karbon-karbon bağ türleri farklı alkollerin etkisi incelenmiştir. Bu mııııçlu 2,5 mV^'lik potansiyel tarama hızı lxl<)“\ 2xl0”\ 5x10 \ IxlO2 ve 2xl02 M'hk alkol derişimleri ve dört ayrı sıcaklıkta (25, 40, 55 ve 70°C) çalışılarak korozyon potansiyelleri, anodik ve kalodik Tufel eğimleri, korozyon hızları ve yüzeyin kaplanma kesirleri belirlenmiştir. Çalışılan bütün sıcaklıklarda alkol derişimlerinin artmasıyla korozyon hızları azalmakta, % inhibisyon etkinliği ve yüzey kaplanma kesirleri artmaktadır. Bütün koşullar için inhibisyon etkinliği aşağıdaki sırada değişmektedir. Bütan- 1 -ol < 2-büten-l-ol < 2-bütin-l-ol. Bu sıra, çalışılan alkollerin çelik yüzeyindeki adsorpsiyonu için de bulunmuş ve adsorpsiyonun Temkin izotermine uyduğu gösterilmiştir. Sonuç olarak ostenitik krom-nikel çeliğinin sülfürik asitteki korozyonuna 2-büten-l-ol ve 2-bütin-l-ol'ün inhibitor olarak etkidiği bulunmuştur.
Özet (Çeviri)
ABSTRACT Masters Thesis AN INVESTIGATION ON THE CORROSION INHIBITIVE EFFICIENCES OF SOME FOUR-CARBON ALCOHOLS ON THE AUSTENITIC CROM-NICKEL STEEL IN RELATION TO THE TYPE OF CARBON-CARBON BOND Mükerrem ŞAHİN Ankara University Graduate School of Natural and Applied Sciences Department of Chemistry Supervisor: Assoc. Prof. Dr. Semra BİLGİÇ 1997, Page: 68 Jury: Assoc. Prof. Dr. Semra BİLGİÇ Assoc. Prof. Dr. Miibeccel ERGUN Prof. Dr. Abbas AKSÜT In this study, the effect of alcohols of four carbon atoms, butan-1-ol, 2-buten-l-oI and 2-butyn-l-ol (which differ in the type of carbon-carbon bonding), on the austenitic crom-nickel steel in sulphuric acid was investigated. For this purpose, using potential sweep rate 2,5 mVs“' with the alcohol concentrations of lxlO*3, 2xl0”\ 5x10 \ MO“2 mid 2xl()”2 M tit four different temperatures, 25, 40, 55 and 70"l'. Corrosion potentials, anodic and cathodic Tafel slopes, corrosion hiitciiIn, Inhibition i'fficİeiH'ics mid degrees of surface coverage were determined. It was found that studied temperatures, as the concentrations of alcohols increase, the corrosion rates decrease, the inhibition efficiencies (%) and the degrees of surface coverage increase. For all conditions, the inhibition efficiency value changes in the following order. Butan-1-ol < 2-buten-l-ol < 2-butyn-l-ol. This order way also found for the degree of adsorption of studied alcohols on the steel surface and the adsorption was shown to be in accordance with Temkin isotherm. In conclusion it was found that 2-buten-l-ol and 2-butyn-l-ol have inhibitor effect on the corrosion of austenitic crom-nickel steel in sulphuric acid.
Benzer Tezler
- Paslanmaz çeliklere uygulanan düşük sıcaklık nitrürleme işleminin mekanik ve korozyon özelliklerine etkisi
The effect of low temperature nitriding on mechanical and corrosion properties of stainless steels
ÖZGÜR ÇELİK
Doktora
Türkçe
2010
Metalurji Mühendisliğiİstanbul Teknik Üniversitesiİleri Teknolojiler Ana Bilim Dalı
PROF. DR. EYÜP SABRİ KAYALI
- Ortopedik implant malzemesi olarak kullanılan östenitik paslanmaz çeliğin sol-jel tekniği ile yüzey özelliklerinin geliştirilmesi
Improving surface properties of austenitic stainless steels using for orthopedic implant by sol-gel method
YAKUP GÖNÜLLÜ
Yüksek Lisans
Türkçe
2009
Metalurji Mühendisliğiİstanbul Teknik Üniversitesiİleri Teknolojiler Ana Bilim Dalı
PROF. DR. HÜSEYİN ÇİMENOĞLU
- Understanding the unusual passive behaviour of high strength hybrid steel in corrosive environments
Yüksek mukavemetli hibrit çeliğin korozif ortamlarda olağandışı pasif davranışının anlaşılması
BESTE PAYAM
Yüksek Lisans
İngilizce
2022
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ CEM ÖRNEK
- Paslanmaz çeliklerin kaynağında içyapının belirlenemsi
Estimation the microstructure of stainless steel welds
MERT UĞUR
Yüksek Lisans
Türkçe
2005
Makine Mühendisliğiİstanbul Teknik ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
DOÇ.DR. MURAT VURAL
- Zamanla paslanmaz çeliklerin standartlardaki değişimi
Changes of stainless steel standards with the time
HİLAL CAN
Yüksek Lisans
Türkçe
1999
Makine MühendisliğiPamukkale ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
PROF.DR. MEHMET YÜKSEL
PROF.DR. ROLF KÖNİG