Farklı kompozit rezin korların epoksi rezin ve metakrilat matriks yapısındaki cam fiber postlara bağlanmasında silanın etkisinin incelenmesi
The evaluation of the bond strength between resin cores and glass fiber posts with different matrices, and the effect of silanization
- Tez No: 625679
- Danışmanlar: PROF. DR. NURAN DİNÇKAL YANIKOĞLU
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Bağlanma dayanımı, Fiber post, İtme testi, Kompozit rezin kor, Silan bağlayıcı ajan, Bond strength, Composite resin core, Fiber post, Push-out test, Silan coupling agent
- Yıl: 2015
- Dil: Türkçe
- Üniversite: Atatürk Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
ÖZET Farklı Kompozit Rezin Korların Epoksi Rezin ve Metakrilat Matriks Yapısındaki Cam Fiber Postlara Bağlanmasında Silanın Etkisinin İncelenmesi Amaç: Bu in vitro çalışmanın amacı farklı matriks yapılarına sahip cam fiber postların silan bağlayıcı ajan uygulanmadan ya da uygulandıktan sonra kompozit rezin korlar ile bağlanma dayanımının itme testi ile değerlendirilmesidir. Materyal Metot: : Çalışmamızda 40 adet metakrilat matrikse sahip Rebilda Post, 40 adet epoksi rezin matrikse sahip Er Dentin Post olmak üzere 80 adet cam fiber post kullanıldı. Postların yarısına silan (Monobond N) uygulanmadan, yarısına uygulandıktan sonra, kuronalde paralel olan kısımlarında, 4 farklı kompozit rezin ile (3 çeşit kor yapımı için üretilmiş kompozit rezin kor materyali; Grandio Core, Rebilda Core, Build-It FR ve 1 çeşit geleneksel hibrit kompozit olan Filtek Z250) korlar hazırlandı. Tek bir post-kordan 2 mm kalınlığında 3'er kesit alınarak (n=15) universal test cihazı ile itme testi uygulandı. İtme testi sonrası post ve korların yüzey morfolojisi geçirimli elektron mikroskobu (SEM) ile değerlendirildi. İstatistiksel analiz 3 faktörlü varyans analizi ile yapıldı. Bulgular: Metakrilat matriksli Rebilda Postun epoksi rezin matrikse sahip Er Dentin Posttan daha fazla bağlanma dayanımı gösterdiği (p<0.001) ve silanın bu bağlanmayı artırdığı (p<0.05) gözlendi. Tüm kor yapım materyalleri Filtek Z250'den daha fazla bağlanma dayanımı sergilerken, en fazla ortalama bağlanma dayanımı değerinin silanlı Rebilda Post-Rebilda Core arasında (19,309 MPa) olduğu tespit edildi. SEM görüntülerinde RebildaPostun daha fazla açığa çıkmış fibere sahip olduğu ve Filtek Z250 yüzeyinde boşluklar olduğu saptandı. Sonuç: Post-kor restorasyonlarda seçilen fiber postun matriks yapısının bağlanmayı etkilediği, fiber posta silan uygulanmasının ve kor yapımı için özel olarak üretilen kompozit rezin kor materyallerinin kullanımının bağlanmayı artırdığı sonucuna varıldı.
Özet (Çeviri)
ABSTRACT The Evaluation of the Bond Strength between Resin Cores and Glass Fiber Posts with Different Matrices, and the Effect of Silanization Aim: The evaluation of the bond strength between resin cores and glass fiber posts with different matrices, and the effect of silanization Material and Method: 40 Rebilda Posts with methacrylate matrices and 40 Er Dentin Posts with epoxy resin matrices were used in this study. In half of the posts, silanization was performed with Monobond N. Three core materials specifically developed for core build-up (Grandio Core, Rebilda Core, Build-It FR) and one hybrid composite (Filtek Z250) were applied to parallel portions of the posts. Three disks of 2 mm thickness were sliced off from each post-core sample for a push-out test. Surface morphology of the posts and cores was characterized after push-out test using a scanning electron microscope (SEM). Data were analyzed by univariate analysis of variance. Results: The bond strength of Rebilda Posts was more than that of the Er Dentin Post (p<0.05), and silanization (p<0.05) increased the push-out bond strength. As the bond strength of all core build-up materials were more than that of Filtek Z250, the bond strength value between Rebilda Posts with silane applied and the Rebilda Core (19,309 MPa) was the highest in all groups. Under SEM, more numbers of exposed fibers were observed on Rebilda Post surface and voids observed along the fractured Filtek Z250 interface. Conclusion: The kind of matrix in fiber posts can affect the bond strength of post-core restorations. The use of core materials specifically developed for core build-up and the silanization of posts can increase the push-out bond strength.
Benzer Tezler
- Farklı endodontik post-kor sistemler ile restore edilmiş dişlerde kök kırılma dayanımlarının İn Vitro olarak değerlendirilmesi
Evaluation of root fracture strength in teeth restored with different endodontic post-core systems:In Vitro study.
ÖMER FARUK YENİLMEZ
Doktora
Türkçe
2025
Diş Hekimliğiİstanbul ÜniversitesiEndodonti Ana Bilim Dalı
DR. ÖĞR. ÜYESİ TURGUT YAĞMUR YALÇIN
- Farklı kompozit rezin simanlar ve adeziv sistemlerle yapıştırılmış IPS empress seramik inleylerin mikrosızıntı yönünden değerlendirilmesi
Microleakage of IPS empress ceramic inlays luted with different composite resin luting cements and adhesive systems
ÖZGE ÖZTÜRK
Doktora
Türkçe
2006
Diş HekimliğiAnkara ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF.DR. BÜLENT ULUDAĞ
- Farklı bioaktif kompozit rezin ile restore edilen sınıf II kavitelerde klorheksidin glukonat kullanımının marjinal boşluk oluşumu ve mikrosızıntı üzerine etkisinin incelenmesi
The effect of chlorhexidine gluconate on marginal gap formation and microleakage in class-II cavities restored using different bioactive composite resins
HAKAN KARAOĞLAN
Doktora
Türkçe
2024
Diş HekimliğiSağlık Bilimleri ÜniversitesiÇocuk Diş Hekimliği Ana Bilim Dalı
PROF. DR. GÜNSELİ GÜVEN POLAT
- Dört farklı tip kompozit rezin materyalden polimerizasyon sonrası salınan artık monomer miktarının karşılaştırılarak değerlendirilmesi
The evaluation of residual monomer release after polymerization of four different composite resin
EZGİ SONKAYA
Diş Hekimliği Uzmanlık
İngilizce
2019
Diş HekimliğiDicle ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
DR. ÖĞR. ÜYESİ ŞEYHMUS BAKIR
- Farklı ferrule seviyelerinde amalgam ve kompozit rezin core uygulanmış endodontik tedavili dişlerin sıkışma-kesme kuvvetine karşı direncinin incelenmesi
The Determination of the resistance of amalgam and composite core applied endodontic treatment in different ferrule effects against compressive-shear forces
MUSTAFA KALKAN
Doktora
Türkçe
1998
Diş HekimliğiSelçuk ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. BÜLENT KESİM