In-vitro evaluation of microleakage under orthodontic brackets bonded with various adhesive systems
Farklı adeziv sistemler ile yapıştırılan ortodontik braketlerin altında oluşan mikrosızıntının in-vitro olarak değerlendirilmesi
- Tez No: 655508
- Danışmanlar: PROF. DR. DİDEM NALBANTGİL
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: mikrosızıntı, ortodonti, braket, kendinden asitli, tek adımlı adeziv, kumlama, Dental bonding, Dental sızma, Dental çimentolar, Ortodontik aygıtlar, Ortodontik braketler, microleakage, orthodontics, brackets, self-etching, one step adhesive, air abrasion, Dental bonding, Dental leakage, Dental cements, Orthodontic appliances, Orthodontic brackets
- Yıl: 2020
- Dil: İngilizce
- Üniversite: Yeditepe Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Ortodonti Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışmanın amacı yapıştırılmasında; üç adeziv sistem, farklı yüzey hazırlıkları ve iki ışık kaynağı kullanılan ortodontik braketlerin altındaki mikrosızıntının değerlendirilmesidir. 144 çekilmiş sığır kesici dişi gelişigüzel şekilde on iki gruba ayrılmıştır. Bu grupların altısına kumlama uygulanmıştır. Braketleri mine yüzeylerine yapıştırmak için üç adeziv sistem kullanılmıştır: %37'lik fosforik asitle pürüzlendirme+Transbond XT Primer +Transbond XT Adhesive, Transbond Plus Self Etching Primer+Transbond XT Adhesive ve %37'lik fosforik asitle pürüzlendirme+GC Ortho Connect. Adeziv polimerizasyonu için Elipar S10 Curing Light ve Valo Ortho Cordless Curing Light kullanılmıştır. Braketleme işleminden sonra örnekler %0.5'lik bazik fuksin solüsyonu ile boyanmış, bukkolingual yönde ikiye ayrılmış ve mikroskop altında 20x büyütme ile mine-adeziv ve braket-adeziv ara yüzleri gingival ve insizal kenarlardan incelenmiştir. Bütün gruplarda mikrosızıntı gözlenmiştir. Gingival ve insizal kenarların mikrosızıntı değerleri arasında anlamlı bir farklılık bulunmamıştır (p>0.05). Mine yüzeylerine kumlama uygulandığında adeziv tipinin mikrosızıntı üzerinde anlamlı bir etkisi olmamıştır. Kumlama uygulanmayan mine yüzeylerinde GC Ortho Connect hem mine-adeziv ara yüzünde (p=0.004) hem de mine-braket ara yüzünde (p=0.0001) daha fazla mikrosızıntıya neden olmuştur. Mine yüzeyine kumlama uygulanması, braketlerin Transbond XT Primer (p<0.05) ve Transbond Plus Self Etching Primer (p=0.0001) ile yapıştırıldığı durumlarda daha çok mikrosızıntıya neden olmuştur. Valo Ortho Curing Light, kumlama uygulanmayan ve Transbond XT Primer ile yapıştırılan grupta daha fazla mikrosızıntıya neden olmuştur (p=0.0001). Işık kaynağından bağımsız olarak, kumlama uygulandığında kullanılan adeziv tipi mikrosızıntı üzerinde önemli bir etkiye sahip değildir. Mine yüzeyinde kumlama ile ön hazırlık yapılmadığında, tek adımlı adeziv sistemler diğer sistemlerden anlamlı derecede fazla mikrosızıntıya neden olmuştur.
Özet (Çeviri)
The aim is to evaluate the microleakage under orthodontic brackets bonded with three adhesive systems, different surface preparations, and two light curing units. 144 extracted bovine incisors were divided randomly into twelve groups. Six of these groups were preconditioned with air abrasion. Three adhesives were used to bond the brackets to enamel: 37% phosphoric acid+Transbond XT Primer+Transbond XT Adhesive, Transbond Plus Self-Etching Primer+Transbond XT Adhesive and 37% phosphoric acid+GC Ortho Connect. Elipar S10 Curing Light and Valo Ortho Curing Light were used to polymerize the adhesives. The specimens were stained with 0.5% basic fuchsine solution, sectioned buccolingually and evaluated under microscope (20x magnification) at enamel-adhesive and bracket-adhesive interfaces from gingival and incisal margins. Microleakage was observed in all groups. There was no significant difference between microleakage scores of gingival and incisal margins (p>0.05). When air abrasion was applied, the type of adhesive did not have a significant effect on microleakage. When enamel was not preconditioned with air abrasion, GC Ortho Connect showed more microleakage in enamel-adhesive (p=0.004) and bracket-adhesive interfaces (p=0.0001). Air abrasion caused more microleakage when brackets were bonded with Transbond XT Primer (p<0.05) and Transbond Plus Self-Etching Primer (p=0.0001). Valo Ortho Curing Light caused more microleakage when Transbond XT Primer was used without air abrasion preconditioning (p=0.0001). Regardless of the curing unit, adhesive type does not have a significant effect on microleakage, when air abrasion preconditioning. When the enamel is not preconditioned with air abrasion, one step adhesive system causes more microleakage than the conventional and self-etching adhesive systems.
Benzer Tezler
- In vitro evaluation of microleakage under lingual brackets bonded with different adhesion materials and different light sources
Farklı adezyon malzemeleri ve farklı ışık kaynakları kullanılarak yapıştırılan lingual braketlerin altındaki mikrosızıntının in vitro değerlendirilmesi
SİNEM UZUNER
Doktora
İngilizce
2022
Diş HekimliğiYeditepe ÜniversitesiOrtodonti Ana Bilim Dalı
PROF. DR. DİDEM NALBANTGİL
- Ortodontik braketlerin yapıştırılmasında kullanılan farklı adeziv sistemlerin mine dokusu üzerindeki etkilerinin in vitro olarak incelenmesi
An in vitro study:The effects on enamel tissue of different adhesive systems used in orthodontic bracket bonding
ASLI GÜZEY
Doktora
Türkçe
2009
Diş HekimliğiBaşkent ÜniversitesiOrtodonti Ana Bilim Dalı
DOÇ. DR. AYÇA ARMAN ÖZÇIRPICI
DOÇ. DR. NESLİHAN ARHUN
- Farklı tekniklerle uygulanan kompozit inleylerin mikrosızıntı yönünden in vitro olarak incelenmesi
In vitro evaluation of microleakage around composite inlays fabricated by different techniques
YILDIRIM HAKAN BAĞIŞ
- Gümüş daimin florür ile modifiye atravmatik restoratif tedavi uygulamasının etkinliğinin İn Vitro koşullarda değerlendirilmesi
Evaluation of the effectiveness of modified atraumatic restorative treatment with silver daimine fluoride under In Vitro conditions
MERVE MANDAL
Doktora
Türkçe
2025
Diş HekimliğiAltınbaş ÜniversitesiÇocuk Diş Hekimliği Ana Bilim Dalı
PROF. DR. FİGEN SEYMEN
DOÇ. DR. MUSA KAZIM ÜÇÜNCÜ
- Gümüş diamin florür ve lazer uygulamasının cam iyonomer restorasyonlara etkisinin in vitro değerlendirilmesi
In vitro evaluation of the effects of silver diamine fluoride and laser application on glass ionomer restorations
DİLANUR DEMİROĞLU AKAY
Doktora
Türkçe
2026
Diş HekimliğiMarmara ÜniversitesiPedodonti Ana Bilim Dalı
DOÇ. DR. MÜESSER AHU YILMAZ