MIG kaynak yöntemiyle birleştirilen Hardox 400, Aısı 304l ve St52 kalite çeliklerin miktoyapı ve mekanik özelliklerinin incelenmesi
Investigation of mictostructural and mechanical properties of hardox 400, Aisi 304l and St52 quality steels combined by MIG welding method
- Tez No: 684934
- Danışmanlar: DR. ÖĞR. ÜYESİ HARUN ÇUĞ
- Tez Türü: Yüksek Lisans
- Konular: Makine Mühendisliği, Mechanical Engineering
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2021
- Dil: Türkçe
- Üniversite: Karabük Üniversitesi
- Enstitü: Lisansüstü Eğitim Enstitüsü
- Ana Bilim Dalı: Makine Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 67
Özet
Bu çalışmada, Hardox çeliği ile paslanmaz çeliğin MIG kaynağı ile kaynak edilmesi sonucunda mekanik davranışları incelenmiştir. Sanayi ortamında Hardox çeliği ile Hardox çeliği kaynak edilmiştir. Kaynak işlemi sırasındaki parametreler ise 7.49m/dk tel hızı 20.8 V ve 165 A ile işlem yapılmıştır. Kouyucu gaz oalrak ArCO2 gazı kullanılmıştır. Kaynak sırasında kullanılan kaynak teli ise paslanmaz Si307 tipi teldir. Bu çalışmada 4 mm kalınlığında hardox çelikleri ile paslanmaz çelikleri kaynak edilmişitir. Kaynak edilen plakalrın büyüklüğü ve hassas olmasından ötürü plakalardan gerekli numuneleri hazırlamak için tel erezyon işlemine tabi tutlarak numuneler hazırlanmıştır. Kaynaklı bölgelerin özellikleri belilrlenmek için çekme, darbe tokluk ve sertlik testi yapılmıştır. Ayrıca mikroyapı analizi yapıalrak kaynaklı bölgenin hali incelenmiştir. Yapılan sertlik deneyleri sonucunda Hardox-Hardox birleştirmesinde en büyük sertlik değerini ortalama 403 HV ile ana metalde, sonrasında ITAB'da 365 HV ve ITAB sınırda 330 HV olarak saptanmıştır. Hardox-Paslanmaz çelik birleştirmesinde ise yine ana metalde 388 HV olarak ölçülmüştür. Paslnamaz çelikte 200 HV ve ITAB'da ortalama 230 HV olarak ölçülmüştür. Hardox-ST çeliğinde ise ana metalde 368 HV, ITAB ortalama 270, ITAB sınırları sırasıyla 190 HV ve 310 HV, kaynak metalinde ise 200 HV olarak ölçülmüştür. Çekme testi sonuçlarına göre en dayanaıklı bağlantı 640 Mpa ile Hardox-Paslanmaz çelik bağlantısı, Hardox- Hardox 400 Mpa ve Hardox- St yaklaşık olarak 350 Mpa olarak ölçülmüştür. Darbe tokluk testinde ise en iyi sonuç Paslanmaz metali ile yapılan kaynakta elde edilmiş olup değeri 68 J iken sonrsaında Haardox metali ile yapılan numunede 44 J, St çeliği yapılan numunede 38 J olarak ölçülmüştür.
Özet (Çeviri)
In this study, the mechanical behavior of Hardox steel and stainless steel by MIG welding was investigated. Hardox steel and Hardox steel are welded in the industrial environment. The parameters during the welding process were 7.49m/min wire speed 20.8 V and 165 A. ArCO2 gas was used as the shielding gas. The welding wire used during welding is stainless Si307 type wire. In this study, 4 mm thick hardox steels and stainless steels were welded. Due to the size and sensitivity of the welded plates, the samples were prepared by subjecting the wire erosion to prepare the necessary samples from the plates. Tensile, impact toughness and hardness tests were carried out to determine the properties of the welded areas. In addition, the state of the welded region was examined by performing microstructural analysis. As a result of the hardness tests, the highest hardness value in Hardox-Hardox joint was determined as 403 HV in the base metal, then 365 HV in ITAB and 330 HV in ITAB border. In the Hardox-Stainless steel joint, it was measured as 388 HV in the base metal. It has been measured as 200 HV in stainless steel and 230 HV in ITAB. In Hardox-ST steel, on the other hand, the base metal was 368 HV, the HTA was 270 on average, the HTA limits were 190 HV and 310 HV, respectively, and 200 HV in the weld metal. According to the tensile test results, the most durable connection was measured as 640 Mpa and Hardox-Stainless steel connection, Hardox- Hardox 400 Mpa and Hardox- St approximately 350 Mpa. In the impact toughness test, the best result was obtained in the weld made with Stainless metal, and its value was 68 J, and then 44 J in the sample made with Haardox metal and 38 J in the sample made of St steel
Benzer Tezler
- Gazaltı (MIG) kaynak yöntemiyle birleştirilen 6061 serisi alüminyum plakalarına yapılan kaynak tamirinin mikroyapı ve mekanik özelliklere etkisi
Effect of weld repair on the microstructural and mechanical properties of 6061 series aluminum plates joined by gas (MIG) welding method
MUSTAFA ARSLAN
Yüksek Lisans
Türkçe
2023
Metalurji MühendisliğiSakarya ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. NİL TOPLAN
- MIG ve sürtünme karıştırma kaynak yöntemleri ile birleştirilen farklı alüminyum alaşımlarının mekanik ve mikroyapı özelliklerinin karşılaştırılması
Comparison of mechanical and microstructures properties of different aluminum alloys joined with MIG and friction stir welding methods
ALİ YÜRÜK
Doktora
Türkçe
2021
Mühendislik BilimleriKarabük Üniversitesiİmalat Mühendisliği Ana Bilim Dalı
PROF. DR. NİZAMETTİN KAHRAMAN
DOÇ. DR. BEKİR ÇEVİK
- MIG/MAG kaynağı ile birleştirilen s700 MC yüksek dayanımlı yapı çeliğinin mikroyapı ve mekanik özelliklerinin incelenmesi
Investigation of the microstructural and mechanical properties of s700 MC high strength construction steel combined with MIG/MAG welding
YASİN GÜR
Yüksek Lisans
Türkçe
2022
Makine MühendisliğiGazi ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. BEHÇET GÜLENÇ
- Yüksek frekans dikişli, MIG ve TIG kaynağı ile birleştirilmiş St 37 malzemenin kaynak profilinin incelenmesi
Investigation on the joint profiles of St 37 steel welded with high frequency resistance, MIG and TIG welding methods
MEHMET OZAN KARADAĞ
Yüksek Lisans
Türkçe
2002
Makine MühendisliğiMustafa Kemal ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
YRD. DOÇ. DR. ALİ KOÇ
- Kontrollü atmosferde MIG-MAG ark kaynağının birleştirmenin özelliklerine etkisi
An effect controlled atmosphere on the MIG-MAG arc weldment properties
KORAY KÖKEMLİ
Yüksek Lisans
Türkçe
2004
Metalurji MühendisliğiZonguldak Karaelmas ÜniversitesiMetal Eğitimi Ana Bilim Dalı
Y.DOÇ.DR. RAMAZAN KAÇAR