CAD/CAM ile üretilmiş polietereterketon post sistemlerinin dentine bağlanma dayanımlarının itme testi ile değerlendirilmesi
Evaluation of bond strength to dentin CAD/CAM milled customized peek posts by push out test
- Tez No: 727439
- Danışmanlar: DR. ÖĞR. ÜYESİ SAMET TEKİN
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Post, Rezin Siman, Polieter Eter Keton, PEEK, Bağlanma dayanımı, İtme Testi, Post, Resin Cement, Polyether Ether Ketone, PEEK Bonding strength, Pust out
- Yıl: 2022
- Dil: Türkçe
- Üniversite: Fırat Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 74
Özet
Çalışmamızın amacı farklı içerikteki PEEK materyalleri kullanarak hazırlanan dental postların dentine bağlanma dayanımlarının itme testi ile değerlendirilmesi ve ayrılma tiplerinin karşılaştırılmasıdır. Çeşitli sebeplerle çekilmiş 60 tane mandibular premolar diş rastgele 3 gruba ayrıldı (n=20). Her bir gruptaki dişin koronali, mine-sement sınırının 2 mm apikalinden kesildi. Kanal içi post preparasyonu yapılmış dişlere CAD/CAM yöntemi ile her biri farklı içerikteki PEEK materyalinden 20'şer adet kişisel post elde edildi. Elde edilen postların yarısına Monobond, diğer yarısına Visiolink bağlanma ajanları uygulandı. Panavia F 2.0 dual kür rezin siman ile simante edildi. Her bir dişten koronal, orta, apikal olmak üzere 1-mm kesitler alındı. 180 adet dentin diski elde edildi ve 0.5 mm/dk hızla geleneksel test cihazında bağlanma dayanımı başarısız olana dek itme kuvveti uygulandı. Bağlanma dayanımın başarısız olduğu değerler MPa cinsinden kaydedildi. Çalışmada, istatistiksel analiz için ANOVA testi ve Kruskal Wallis H testi kullanılmıştır. Sonuçlar yorumlanırken anlamlılık düzeyi olarak 0,05 kullanılmış olup; p0,05 olması durumunda ise anlamlı bir farklılığın olmadığı belirtilmiştir. Bağlanma dayanımı (MPa) üzerine etki eden faktörler incelendiğinde; materyallerin bağlanma dayanımı (MPa) üzerine istatistiksel olarak anlamlı etkisi bulunmaktadır (p0,05). Materyal ve bond etkileşiminin bağlanma dayanımı (MPa) üzerine istatistiksel olarak anlamlı etkisi bulunmamaktadır (p>0,05). Kesit ve bond etkileşiminin bağlanma dayanımı (MPa) üzerine istatistiksel olarak anlamlı etkisi bulunmamaktadır (p>0,05). Materyal, kesit ve bond etkileşiminin bağlanma dayanımı (MPa) üzerine istatistiksel olarak anlamlı etkisi bulunmamaktadır (p>0,05). Postlar ve adeziv rezin simanlar arasındaki bağlanma dayanımı başarısızlık tipleri steromikroskop ile 40x büyütmede incelendi. Gruplar içerisinde en fazla oranda adeziv başarısızlık olduğu rapor edildi. Yapılan çalışma sonucunda saf PEEK ve modifiye PEEK materyallerinden üretilen postlar klinik kullanımda başarı göstereceği konusunda umut vermiştir.
Özet (Çeviri)
The purpose of this study is to evaluate the bond strength to dentin of dental posts prepared using PEEK materials with different contents by push test and to compare the separation types. 60 mandibular premolar teeth which extracted for various reasons were randomly divided into 3 groups (n=20). The coronal part of teeth was cut off 2 mm above of the cemento-enamel junction. 20 individual posts were obtained from PEEK material with different contents by CAD/CAM method for teeth which canals prepared for their intracanal posts. Monobond bonding agents were applied to half of the obtained posts and Visiolink bonding agents were applied to the other half. It was cemented with Panavia F 2.0 dual cure resin cement.2 mm sections were taken from each tooth, coronal, middle and apical. 180 dentin discs were obtained and force was applied at 0.5 mm/min until the bond strength failed in the universal testing machine. The values at which the bond strength failed were recorded in MPa. When the factors affecting the bond strength (MPa) are examined; there is a statistically significant effect on the bond strength (MPa) of the materials (p0.05). The interaction of material and bond has no statistically significant effect on bond strength (MPa) ( p>0.05). The interaction of cross-section and bond has no statistically significant effect on bond strength (MPa) (p>0.05). Interaction of material, cross-section and bond has no statistically significant effect on bond strength (MPa) (p> 0.05). Bond strength failure types between posts and adhesive resin cements were examined with a stereomicroscope at 40X magnification. The highest rate of adhesive failure was reported among the groups. As a result of the study, it was hoped that pure PEEK and modified PEEK post materials would be successful in clinical use.
Benzer Tezler
- CAD/CAM yardımıyla kişiye özel hazırlanmış polietereterketon post-korların kırılma dayanımlarının değerlendirilmesi
Evaluation of the fracture strength of CAD/CAM milled custom polyetheretherketone dental post-cores
AYETULLAH DİREK
Diş Hekimliği Uzmanlık
Türkçe
2022
Diş HekimliğiFırat ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DR. ÖĞR. ÜYESİ SAMET TEKİN
- Estetik zirkonyum, polietereterketon ve polieterketonketon implant dayanakları üzerine yapılan lityum disilikatla güçlendirilmiş CAD/CAM monolitik cam seramik kronların yaşlandırma işlemi sonrası kırılma dayanımlarının ve kırılma tiplerinin in vitro değerlendirilmesi
Evaluation of fracture resistance and fracture types of titanium sub-structured zirconium, polyetheretherketone, polyetherketoneketone implant abutments restored with lithium disilicate reinforced monolithic CAD/CAM glass ceramic crowns after cyclic fatique loading
ALMİRA ADA DİKEN TÜRKSAYAR
Diş Hekimliği Uzmanlık
Türkçe
2019
Diş HekimliğiKırıkkale ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. SAADET SAĞLAM ATSÜ
- CAD/CAM sistemleri kullanılarak üretilen üç üyeli implant destekli sabit bölümlü protez altyapılarının marjinal ve internal uyumlarının karşılaştırılması
Comparison of marginal and internal adaptation in the frameworks of three-unit implant supported fixed partial denture produced by using CAD/CAM systems
ÖZLEM KAYIKÇI
Diş Hekimliği Uzmanlık
Türkçe
2020
Diş HekimliğiRecep Tayyip Erdoğan ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. SABİT MELİH ATEŞ
- Farklı termoplastik polimerlerin mekanik özelliklerinin karşılaştırmalı olarak değerlendirilmesi
Comparative evaluation of mechanical properties of different thermoplastic polymers
FATMA GÜNEŞ
Diş Hekimliği Uzmanlık
Türkçe
2023
Diş HekimliğiGazi ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. TURAN KORKMAZ
- Load bearing of different fixed prosthesis materials with various cantilever lenghts
Değişik sabit protez materyallerinin farklı kantilever boylarındaki yük dayanımı
İLAYDA AŞKAN
Doktora
İngilizce
2023
Diş HekimliğiYeditepe ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. ENDER KAZAZOĞLU