Kemomekanik çürük temizleme yönteminin farklı restoratif materyallerin adezyonuna etkisinin incelenmesi
The evaluation of effect of chemomechanical caries removal method onadhesion of different restorative materials
- Tez No: 729603
- Danışmanlar: DOÇ. DR. DERYA CEYHAN
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Cam iyonomer çimentoları, Dental bonding, Dental materyaller, Dental restorasyon, Dental çimentolar, Diş çürükleri, Süt dişleri, Tedavi, Glass ionomer cements, Dental bonding, Dental materials, Dental restoration, Dental cements, Dental caries, Tooth deciduous, Treatment
- Yıl: 2022
- Dil: Türkçe
- Üniversite: Süleyman Demirel Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Çocuk Diş Hekimliği Ana Bilim Dalı
- Bilim Dalı: Pedodonti Bilim Dalı
- Sayfa Sayısı: Belirtilmemiş.
Özet
Çalışmamızda, kemomekanik yöntem ve atravmatik restoratif tedavi tekniğinin, süt azı dişlerinin yüksek viskoziteli cam iyonomer siman ve kompomer restorasyonları üzerinde çalışma süresi, mikro-gerilim bağlanma dayanımı ve mikrosızıntı açısından etkilerinin değerlendirilmesi amaçlanmıştır. Toplanan 80 adet süt azı dişi, uygulanan çürük uzaklaştırma yöntemine göre Grup 1: BRIX 3000 ve Grup 2: ART olarak iki ana gruba; kullanılan restorasyon materyaline göre Grup A: Equia Forte HT ve Grup B: Dyract XP olarak iki alt gruba ayrıldı. Dişlerin çürük uzaklaştırma ve restorasyon aşamaları için harcanan süre kronometre ile kaydedildi. Her bir çalışma grubundaki 20 adet dişten, okluzal dentin çürüklü 5 adedine mikro-gerilim bağlanma dayanımı testi, okluzoproksimal dentin çürüklü 15 adedine mikrosızıntı testi uygulandı. Örnekler, deney öncesinde 500 kez termal siklus işlemine tabi tutuldu. Mikro-gerilim testi uygulanacak her dişten 1x1 mm2 boyutunda 3'er adet kesit elde edildi ve universal test cihazı ile 1 mm/dk çapraz kafa hızında kuvvet uygulandı. Kesitlerde görülen kopma tipleri stereomikroskop ile incelendi. Mikrosızıntı testi uygulanacak dişler, %0,5'lik bazik fuksin boyasında 24 saat bekletildi. Örnekler, mezio-distal olarak ikiye ayrılarak stereomikroskop ile incelendi. Elde edilen veriler istatistiksel olarak analiz edildi. Çalışma gruplarının çürük temizleme, restorasyon ve toplam işlem süreleri arasında istatistiksel olarak anlamlı farklılık olduğu tespit edildi (p<0,05). BRIX 3000 jel uygulanan gruplarda çürük uzaklaştırma süresinin, Equia Forte HT kullanılan gruplarda restorasyon süresinin daha fazla olduğu görüldü. Mikro-gerilim bağlanma dayanımı değerinin, BRIX kullanılan tüm çalışma gruplarında, ART kullanılan çalışma gruplarına göre daha fazla olduğu saptandı (p<0,05). Equia Forte HT kullanılan çalışma gruplarının mikro-gerilim bağlanma dayanımı değerlerinin, Dyract XP kullanılan çalışma gruplarına göre daha yüksek olduğu ancak anlamlı bir farklılığın görülmediği tespit edildi (p>0,05). BRIX+Equia Forte HT çalışma grubunda en sık koheziv tip kopma, diğer çalışma gruplarında ise en sık adeziv tip kopma görüldü. Çalışma grupları ile kopma tipleri arasında hesaplanan ki-kare test istatistiği 1,120 olup, istatistiksel olarak önemli bulunmadı. Kopma tiplerinin mikro-gerilim bağlanma dayanımı değerleri arasında istatistiksel olarak anlamlı farklılık olduğu tespit edildi (p<0,05). Kopma türüne göre mikro-gerilim bağlanma dayanımı değerlerinin sıralamasının“koheziv>miks>adeziv”olduğu ve yalnızca adeziv ile koheziv tip kopma arasındaki farkın anlamlı olduğu bulundu (p<0,05). Mikrosızıntı skoru ile çalışma grupları arasında hesaplanan ki-kare test istatistiği 21,194 olup, istatistiksel olarak önemli bulundu (p<0,05). En düşük mikrosızıntının BRIX+Equia grubunda, en yüksek mikrosızıntının ART+Dyract XP grubunda ölçüldüğü saptandı. Gingival mikrosızıntı skorunun, BRIX+Equia Forte HT haricindeki çalışma gruplarında, okluzal mikrosızıntı skoruna kıyasla, daha yüksek olduğu tespit edildi. BRIX 3000 jel kullanılan kemomekanik çürük uzaklaştırma yönteminin, yüksek viskoziteli cam iyonomer siman ve kompomer materyalleri ile süt azı dişlerinde yapılan restorasyonların mikro-gerilim bağlanma dayanımı değerini ve sızdırmazlık özelliğini arttırdığı görüldü. BRIX+Equia Forte HT kombinasyonunun, tüm testlerde en başarılı sonuçları verdiği saptandı.
Özet (Çeviri)
Aim of this study was to evaluate the effects of chemomechanical caries removal technique and atraumatic restorative treatment technique (ART) on high viscosity glass ionomer cement and compomer restorations of primary molars in terms of working time, micro-tensile bond strength and microleakage. Eighty primary molars were divided into two main groups as Group 1: BRIX 3000 and Group 2: ART according to the caries removal method and into two subgroups as Group A: Equia Forte HT and Group B: Dyract XP according to the restoration material used. The time spent for caries removal and restoration processes was recorded with a chronometer. Micro-tensile bond strength test was applied to 5 of 20 teeth with occlusal dentin caries and microleakage test was applied to 15 of 20 teeth with occlusoproximal dentin caries. The samples were thermocycled 500 times before the tests. Three sticks of 1x1 mm2 in size were obtained from each tooth to be tested for micro-tensile bond strength, and force was applied with a micro-tensile tester at a crosshead speed of 1 mm/min. The modes of fractures were examined with a stereomicroscope. The teeth to be tested for microleakage were immersed in 0.5% basic fuchsin dye for 24 hours. The samples were divided into two as mesio-distally and examined with a stereomicroscope. The obtained data were analyzed statistically. There was a statistically significant difference between the study groups in terms of caries removal time, restoration time and total procedure time (p<0.05). Caries removal time was longer in the BRIX 3000 gel groups and restoration time was longer in the Equia Forte HT groups. Micro-tensile bond strength values of the groups using BRIX 3000 were higher than the groups using ART (p<0.05). Micro-tensile bond strength values of the groups using Equia Forte HT were higher than the groups using Dyract XP, but no significant difference was observed (p>0.05). Fracture mode assessment showed a predominance of cohesive failures in BRIX+Equia Forte HT group and adhesive failures in the other study groups. The chi-square test statistic calculated between the study groups and fracture mode was 1,120, it was not found to be statistically significant. There was a statistically significant difference between the micro-tensile bond strength values of the fracture mode (p<0.05). It was found that the order of micro-tensile bond strength values according to the fracture mode was“cohesive>mix>adhesive”and the difference between only adhesive and cohesive failure modes was significant (p<0.05). The chi-square test statistic calculated between the microleakage score and the study groups was 21,194, and it was found to be statistically significant (p<0.05). The lowest microleakage was measured in the BRIX+Equia group, the highest microleakage was measured in the ART+Dyract XP group. The gingival microleakage score was higher in the study groups except BRIX+Equia Forte HT compared to the occlusal microleakage score. The chemomechanical caries removal method using BRIX 3000 gel increased the micro-tensile bond strength and sealing property of the restorations with highviscosity glass ionomer cement and compomer materials in primary molars. The BRIX+Equia Forte HT combination gave the most successful results in all tests.
Benzer Tezler
- N-monochloro-DL-2- aminobutyrateın çürük kaldırma etkinliğinin deneysel araştırılması
Başlık çevirisi yok
YAŞAR MERİÇ TUNCA
- “Caridex”sistemi ile çürük temizleme yönteminin mekanik yöntemle karşılaştırılması
Comparison of caridex removal system whith mechanichal caries removal system
FERİDUN HÜRMÜZLÜ
- Retrograd dolgu maddelerinin bakteriyel sızdırmazlığının karşılaştırmalı olarak incelenmesi
Başlık çevirisi yok
AYŞE ERTAN BAYRAKTAROĞLU
Doktora
Türkçe
1998
Diş HekimliğiEge ÜniversitesiDiş Hastalıkları ve Tedavisi Ana Bilim Dalı
PROF. DR. NECDET ERDİLEK
- Deneysel olarak %5.25'lik Sodyumhipoklorit'in dokularda etkisinin histopatolojik incelenmesi
Başlık çevirisi yok
CÜNEYT BOSNA
Doktora
Türkçe
1998
Diş HekimliğiGataDiş Hastalıkları ve Tedavisi Ana Bilim Dalı
PROF. DR. SERVET HARPUTLUOĞLU