Polietilen imin modifiye edilmiş TiO2'in sentezi ve krom iyonlarının adsorpsiyonu ve/veya organik kirliliklerin fotokatalitik parçalanması için kullanılabilirliğinin araştırılması

Synthesis of polyethylene imine modified TiO2 and investigationof its usability for adsorption of chromium ions and/orphotocatalytic decomposition of organic pollutants

  1. Tez No: 744943
  2. Yazar: EMRAH AKGEYİK
  3. Danışmanlar: PROF. DR. SEMA ERDEMOĞLU, PROF. DR. AHMET GÜLTEK
  4. Tez Türü: Doktora
  5. Konular: Kimya, Chemistry
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2022
  8. Dil: Türkçe
  9. Üniversite: İnönü Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Kimya Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 210

Özet

Tez kapsamında; Anataz TiO2'in sentez aşamasında ortama polietilen imin ve gluteraldehit eklenerek TiO2-PEI-GA materyali reflux yöntemle sentezlendi ve atık sularda bulunan anyonik Cr6+'nın yani CrO42- iyonlarının adsorpsiyonu ve dirençli organik kirliliklerin fotokatalitik yıkımı için ''bifonksiyonel'' materyalin sentezi gerçekleştirildi. Ayrıca, sentezlenen bifonksiyonel materyal, farklı matriks ortamlarında bulunan düşük derişimdeki Cr6+ iyonlarını katı faz ekstraksiyonu (SPE) ile ayrılması ve ön-deriştirilmesi için kolon dolgu maddesi olarak kullanıldı. TiO2-PEI-GA materyalinin, XRD, FT-IR, SEM-EDX, BET, TGA, Dinamik ışık saçılması (DLS) ve Zeta potansiyel analizleri yapılarak karakterizasyonu yapıldı. CrO42-→Cr6+ iyonlarının optimum adsorpsiyon koşullarını belirlemek için batch yöntem kullanıldı ve çözelti pH, adsorbent miktarı, adsorpsiyon süresi, ortam sıcaklığı, başlangıç derişimi, çözelti hacmi, organik ve inorganik kirliliklerin etkisi ve ayrıca seçicilik faktörü araştırıldı. Cr6+ 'nın pH 3 çözelti ortamında 45 dk'da maksimum adsorpsiyon kapasitesi 156,0 mgg-1 olarak belirlendi. Fotokatalitik çalışmalar tannik asit, reaktif black 5, rodamin b ve metilen mavisi çözeltileri ile yapıldı. TiO2-PEI-GA'nin görünür ışık altında 4 saat ışınlama sonucu tannik asit ve boyar maddeleri neredeyse tamamen parçaladığı görüldü. Son olarak sentezlenen materyalin antimikrobiyal etkisi incelendi ve antifungal etki gösterdiği belirlendi.

Özet (Çeviri)

In this thesis; TiO2-PEI-GA material was synthesized by reflux method by adding polyethylene imine and glutaraldehyde to the medium at the TiO2 synthesis process.“Bifunctional”material synthesis was aimed for the adsorption of anionic Cr6+, namely CrO42- ions in wastewater and photocatalytic degradation of tannic acid. In addition, the synthesized bifunctional material was used as an adsorbent in order to separate and concentrate low concentration Cr6+ ions in different matrix environments by solid phase extraction (SPE). The synthesized material was characterized by XRD, FT-IR, SEM-EDX, BET, TGA, DLS, Zeta potential measurements. The batch method was used to determine the optimum experimental conditions. In this context solution pH, adsorbent amount, adsorption time, ambient temperature, initial concentration, solution volume, the effect of organic and inorganic impurities as well as selectivity factor were studied. The maximum adsorption capacity of Cr6+ at pH 3 in solution medium in 45 minutes was determined to be 156.0 mgg-1. For photocatalytic studies, tannic acid, reagent black 5, rhodamine B and methylene blue solutions were used. It was observed that TiO2-PEI-GA almost completely broken down tannic acid and dyestuffs subjected to 4 hours of irradiation under visible light. As a result, the antimicrobial effect of the material with antifungal propertion were eluciated.

Benzer Tezler

  1. Synthesis and characterization of mesoporous metal sulfide and metal selenide thin films using liquid crystalline mesophases

    Sıvı kristal mezofazları kullanarak mezogözenekli metal sülfür ve metal selenür ince film sentezi ve karakterizasyonu

    YURDANUR TÜRKER

    Doktora

    İngilizce

    İngilizce

    2012

    Kimyaİhsan Doğramacı Bilkent Üniversitesi

    Kimya Bölümü

    PROF. DR. ÖMER DAĞ

  2. Preparation of poly(Amidoamine) grafted polyethylene imine (PEI) for drug solubility enhancement applications

    İlaç çözünürlüğünü geliştirici uygulamalar için poli (Amidoamine) ile kaplanmış poletilen imin'in hazırlanması

    KEREM UZUN

    Yüksek Lisans

    İngilizce

    İngilizce

    2014

    KimyaFatih Üniversitesi

    Kimya Ana Bilim Dalı

    DOÇ. MEHMET ŞENEL

  3. PH and temperature responsive multiple drug release from layer-by-layer modified microparticles

    Katman-katman yüzeyi değiştirilmiş mikroparçacıklardan pH ve sıcaklık duyarlı çoklu ilaç salımı

    ESMA UĞUR

    Yüksek Lisans

    İngilizce

    İngilizce

    2022

    KimyaOrta Doğu Teknik Üniversitesi

    Kimya Ana Bilim Dalı

    PROF. DR. İREM EREL GÖKTEPE

  4. Kansere karşı çok yönlü tedavi aracı olarak manyetik nanopartiküllerin geliştirilmesi

    Development of magnetic nanoparticles as a potential multi-therapy agent against cancer

    KÜBRA SOLAK

    Doktora

    Türkçe

    Türkçe

    2023

    BiyomühendislikAtatürk Üniversitesi

    Nanobilim ve Nanoteknoloji Ana Bilim Dalı

    PROF. DR. AHMET MAVİ

  5. Production of high performance and innovative materials based on polybenzoxazine

    Polibenzoksazin esaslı yüksek performanslı ve yenilikçi malzemelerin üretilmesi

    SEVİNÇ GÜLYÜZ

    Doktora

    İngilizce

    İngilizce

    2024

    Kimyaİstanbul Teknik Üniversitesi

    Kimya Ana Bilim Dalı

    PROF. DR. BARIŞ KIŞKAN