The effect of surface coating and artificial aging on the surface roughness and microhardness of glass ionomer-based restorative materials in- vitro
Yüzey örtücü uygulamasının ve yapay yaşlandırmanın cam iyonomer esaslı restoratif materyallerin yüzey pürüzlülüğü ve mikrosertliğine etkilerinin ın vitro değerlendirilmesi
- Tez No: 790451
- Danışmanlar: DOÇ. DR. ELİF SUNGURTEKİN EKÇİ
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Yüzey pürüzlülüğü, yüzey mikrosertliği, termosiklus, cam iyonomer siman, yapay yaşlandırma, in vitro, yüzey örtücü, Cam iyonomer çimentoları, Dental restorasyon, Mikrosertlik, Çukur ve fissür örtücüler, Surface roughness, surface microhardness, thermal aging, glass ionomer cement, artificial aging, in vitro, surface coating, Glass ionomer cements, Dental restoration, Microhardness, Pit and fissure sealants, In vitro
- Yıl: 2023
- Dil: İngilizce
- Üniversite: Yeditepe Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Çocuk Diş Hekimliği Ana Bilim Dalı
- Bilim Dalı: Çocuk Diş Hekimliği Bilim Dalı
- Sayfa Sayısı: Belirtilmemiş.
Özet
Cam İyonomer Simanlar (CIS); minimal preparasyonla diş dokularına kimyasal bağlanmaları ve fluorid salma özellikleri nedeniyle özellikle çocuk diş hekimliğinde yaygın şekilde kullanılmaktadır. Cam iyonomer siman restorasyonların sekonder sertleşmesi tamamlanana kadar olumsuz fiziksel özelliklerini azaltmak için yüzey örtücü ajanlarının kullanılması giderek yaygınlaşmaktadır. Yüzey örtücü ajanlar, cam iyonomer restorasyonlara uygulandığında restorasyonun yüzey pürüzlülüğü ve mikrosertlik gibi fiziksel özelliklerini iyileştirir. Çalışmamızda biyoaktif bir restoratif materyal olan ACTIVATM kids BioACTIVE-RESTORATIVETM (PULPDENT®, Watertown, USA), yüksek viskoziteli cam iyonomer siman materyalleri; EQUIA® Forte Fil (GC Corporation, Tokyo, Japonya) ve ChemFil® Rock (Dentsply Sirona, Kontstantz, Almanya) kullanılmıştır. Yüzey örtücü ajan olarak EQUIA ForteTM Coat (GC Corporation, Tokyo, Japonya) kullanılmıştır. Mikrosertlik ve yüzey pürüzlülük testleri için pleksi cam kalıplar (10±0.1 mm çapında ve 2±0.1 mm derinliğinde) kullanılmıştır. Termal döngü işleminden önce ve sonra örneklerin yüzey pürüzlülüğü ve mikrosertlik ölçümleri yapılmıştır. İstatistiksel analizler için SPSS (Statistical Package for the Social Sciences) 24.0 programı kullanılmıştır. Anlamlılık p<0,01 ve p<0,05 seviyelerinde değerlendirilmiştir. Yüzey örtücü uygulamasının etkisinin değerlendirildiği grup içi karşılaştırmada, test edilen tüm malzemelerin yüzey pürüzlülük değeri istatistiksel olarak anlamlı düşüş göstermiştir (p<0,05). Test edilen diğer tüm materyallerde yüzey pürüzlülük değerleri yapay yaşlandırma sonrası istatistiksel olarak anlamlı düşüş göstermiştir (p<0,05). Yüzey örtücü uygulamasının etkisinin değerlendirildiği grup içi karşılaştırmada, test edilen tüm malzemelerin yüzey sertlik değeri istatistiksel olarak anlamlı düşüş göstermiştir (p<0,05). Test edilen diğer tüm materyallerim mikrosertlik değeri yapay yaşlandırma sonrası istatistiksel olarak anlamlı düşüş göstermiştir (p<0,05).
Özet (Çeviri)
Yıldırım Y. 2023. The Effect of Surface Coating and Artificial Aging on the Surface Roughness and Microhardness of Glass Ionomer-Based Restorative Materials In- Vitro. Yeditepe University Institute of Health Sciences, Ph.D. Thesis, Istanbul. Glass Ionomer Cements (GIC), due to their chemical bonding to dental tissues with minimal preparation and their fluoride-releasing properties, have become popular in pediatric dentistry. Until the secondary hardening of restorations made using GIC is completed, surface coatings are applied to the restoration surface to reduce its negative physical properties. When applied to glass ionomer restorations, surface coatings improve the properties of materials, such as surface roughness and microhardness. A bioactive restorative material ACTIVATM kids BioACTIVE-RESTORATIVETM (PULPDENT®, Watertown, USA), high-viscosity glass ionomer cement materials EQUIA® Forte Fil (GC Corporation, Tokyo, Japan) and ChemFil® Rock (Dentsply Sirona, Konstanz, Germany) were used within the scope of the study. EQUIA ForteTM Coat (GC Corporation, Tokyo, Japan) was used as a surface coating agent. Thirty-four samples were prepared from each material group, and Equia Forte Coat was applied to half of them. Plexiglass molds (10±0.1 mm in diameter and 2±0.1 mm in depth) were used for surface roughness and microhardness tests. Before and after the thermal cycling procedure, surface roughness and microhardness measurements were performed for all samples. Statistical Package for the Social Sciences (SPSS) 24.0 program was used for statistical analysis. Significance was evaluated at p<0.01 and p<0.05 levels. In the intragroup comparison where the effect of the surface coating application was evaluated, the surface roughness values of all tested materials showed a statistically significant decrease (p<0.05). Surface roughness values in all other tested materials showed a statistically significant decrease after artificial aging (p<0.05). In the intragroup comparison where the effect of the surface coating application was evaluated, the surface hardness value of all tested materials showed a statistically significant decrease (p<0.05). The microhardness value of all other tested materials showed a statistically significant decrease after artificial aging (p<0.05).
Benzer Tezler
- Eloksal kaplanmış AA060 alüminyum profillerinin kaplama yüzeyine alaşım elementi ve suni yaşlandırma sıcaklığının etkisi
The effect of alloy element and artificial aging temperature on the coating surface of anodized AA6060 aluminum profiles
CANSU ÇEÇEN
Yüksek Lisans
Türkçe
2026
Metalurji MühendisliğiSakarya ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. NİL TOPLAN
- Farklı yüzey işlemlerinin zirkonya ile rezin siman arasındaki bağlantı kuvveti üzerine etkisi
The effect of different surface treatments on the bond strength between zirconia and resin luting cement
GÖKHAN ÇİÇEKCİ
Diş Hekimliği Uzmanlık
Türkçe
2020
Diş HekimliğiAnkara ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. LALE KARAAĞAÇLIOĞLU
- Farklı yüzey işlemleri uygulanan monolitik zirkonya seramiğin diş dokularına olan bağlantısının incelenmesi
Investigation of the bonding of monolithic zirconia ceramics with different surface treatments to dental tissues
GÖNÜL MERVE EYÜBOĞLU ATEŞ
Diş Hekimliği Uzmanlık
Türkçe
2025
Diş HekimliğiKocaeli ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. AYŞE KOÇAK BÜYÜKDERE
- Ahşap yatlarda kullanılan çeşitli verniklerin farklı ağaç malzemeler üzerindeki performanslarının karşılaştırılması
Comparison of the performance of various varnishes used in wooden yachts on different wood species
MURAT ALTIPARMAK
Yüksek Lisans
Türkçe
2017
Gemi MühendisliğiMuğla Sıtkı Koçman ÜniversitesiAğaç İşleri Endüstri Mühendisliği Ana Bilim Dalı
DOÇ. DR. MEHMET ÇOLAK
- Eklemeli üretim teknolojileri ile üretilen dental restoratif materyallerin yaşlandırma sonrasi renk stabilitesi, yüzey pürüzlülüğü ve L929 fibroblast hücreleri üzerine sitotoksik etkilerinin incelenmesi
Evaluation of color stability, surface roughness, and cytotoxic effects on L929 fibroblast cells of dental restorative materials produced by additive manufacturing technologies after thermocycling
AYGÜL YAPRAK
Diş Hekimliği Uzmanlık
Türkçe
2025
Diş HekimliğiErciyes ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. AYŞEGÜL GÜLERYÜZ