Farklı yüzey işlemlerinin zirkonya ile rezin siman arasındaki bağlantı kuvveti üzerine etkisi
The effect of different surface treatments on the bond strength between zirconia and resin luting cement
- Tez No: 658641
- Danışmanlar: PROF. DR. LALE KARAAĞAÇLIOĞLU
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Dental bonding, Dental materyaller, Dental çimentolar, Kompozit reçineler, Yüzey pürüzlülüğü, Zirkonyum oksit, Dental bonding, Dental materials, Dental cements, Composite resins, Surface roughness, Zirconium oxide
- Yıl: 2020
- Dil: Türkçe
- Üniversite: Ankara Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Estetik, dayanıklı ve biyouyumlu bir seramik olan zirkonya, restorasyon materyali olarak klinik uygulamalarda gün geçtikçe daha çok tercih edilir hale gelmektedir. Ancak rezin simanlar ile simantasyon prosedürü polikristalin yapısı sebebi ile diğer cam içerikli seramik materyallerden çok daha farklıdır. Hidroflorik asit ve silan kullanılarak bağlantı kurulabilecek bir silika içeriği bulunmayışı, araştırmacıları farklı yöntemler denemek zorunda bırakmıştır. Tez çalışmamızda amaç, bu yöntemlerden bazılarını oluşturduğu pürüzlülük ve ıslanabilirlikteki değişim ile birlikte iki farklı kimyasal özellikteki self adeziv rezin simanın kesme bağlantı kuvvetine etkisi yönünden incelemektir. Çalışmamızda, klinik pratikteki restorasyonların yapım prosedürüne uygun olarak zirkonya örnekler, dijital bir şekilde dizayn edilerek monolitik zirkonya disklerden (inCoris TZI C, Dentsply Sirona, USA) bir CAM cihazı (MC X5, Dentsply Sirona, USA) kullanılarak freze edildi, ardından bir sinterleme fırını (inFire HTC Speed, Dentsply Sirona, USA) yardımı ile sinterlendi. Hazırlanan örnekler (n=88) bir kontrol ve üç yüzey işlemi (Kumlama, Rocatec ve Z-Prime) olmak üzere rastgele 4 gruba ayrıldı. Kontrol grubunda (n=22) hiçbir yüzey işlemi uygulanmadı. Kumlama grubunda (n=22) örnek yüzeyleri 50 µm Al2O3 kumu ile pürüzlendirildi. Rocatec grubunda (n=22) yüzeyler, silika ile modifiye edilmiş 30 µm Al2O3 kumu (Rocatec Soft, 3M ESPE, Seefeld, Germany) ile pürüzlendirildikten sonra silan uygulandı. Z-Prime grubunda (n=22) ise 50 µm Al2O3 kumu ile pürüzlendirildikten sonra zirkonya yüzeylerine MDP içerikli bir primer olan Z-Prime Plus (BISCO, Schaumburg IL, U.S.A) uygulandı. Tüm örneklerden pürüzlülük (Ra) ve yüzey temas açısı ölçümü yapıldı. Hazırlanan gruplar kendi içinde rastgele bir şekilde biri MDP monomeri içeren diğeri ise içermeyen iki farklı rezin siman (Panavia SA Cement Plus ve RelyX U200) grubuna ayrıldı (n=11). Simanlar yüzeylere standardizasyonu sağlamak için Ultradent Bonding Jig yardımı ile bağlandı. Simantasyonu tamamlanan örneklere 10000 döngü termal siklus uygulandı. Yapay yaşlandırma işlemi bittikten hemen sonra simanlara kesme kuvveti uygulanarak bağlantı değerleri MPa cinsinden kaydedildi. İstatistiksel analiz sonucunda en düşük ıslanabilirlik kontrol grubunda gözlenirken, ıslanabilirliği en yüksek olanın Z-Prime grubu olduğu görülmüştür (P<0,05). En yüksek pürüzlülük değerine ise kumlama grubunda ulaşılmıştır (P<0,05). Grup içindeki ortalama kesme bağlantı kuvvetlerine bakıldığında istatistiksel olarak anlamlı en yüksek değer Z-Prime grubunda görülmüştür (P<0,05). En düşük değerler ise RelyX U200 ile bağlanan örnekleri termal siklus sırasında ayrılan kontrol grubunda gözlenmiştir. Kumlama ve Rocatec gruplarında iki tip simanın bağlantı kuvvetleri arasında anlamlı fark gözlenmezken, Z-Prime grubunda RelyX U200 uygulanan örneklerin bağlantı değerleri istatistiksel olarak anlamlı bir şekilde yüksek bulunmuştur (P<0,05). Tüm Panavia uygulanan örnekler arasında en yüksek bağlantı değerleri Rocatec ve Z-Prime gruplarında, RelyX U200 uygulanan örneklerde ise Z-Prime grubunda gözlemlenmiştir (p<0,05). Çalışmamızın sonuçlarına göre zirkonya ile rezin siman arasında başarılı bir bağlantı kurmak için mutlaka bir yüzey işlemi uygulanması gerekmektedir. Tercih edilen yüzey işleminin tipi de bağlantı kuvvetinde önemli rol oynamaktadır. Zirkonya yüzeyine pürüzlülüğü arttırarak sadece mikromekanik bağlantı sağlayan kumlama gibi işlemlerin yanında, silika kaplama sonrası silan uygulama veya primer kullanımı gibi kimyasal bağlantıyı güçlendirecek işlemlerin de uygulanması rezin simanlar ile bağlantı başarısını arttırmaktadır. Kimyasal bağlantıyı sağlamak için kullanılan monomer çeşitliliğinin artmasının da bağlantı kuvvetine olumlu etkisi olmaktadır. Islanabilirliğin artışının ise rezin siman ile zirkonya arasındaki bağlantıyı kuvvetlendirdiği söylenebilir ancak sadece ıslanabilirlik özelliğine bakarak yorum yapmak yeterli olmamaktadır. Şekillenen yüzey ile siman arasındaki bağlantının mekanizmasının da değerlendirilmesi gerekmektedir.
Özet (Çeviri)
Zirconia, an esthetic, durable and biocompatible ceramic, is becoming more and more preferred in clinical practice as a restoration material. However, the cementation procedure with resin luting cements is much different from other glass-containing ceramic materials due to the polycrystalline structure of zirconia. The lack of a silica content that could be bonded using hydrofluoric acid and silane forced researchers to try different methods. The aim of our thesis is to examine some of these methods in terms of the effect of two self-adhesive resin luting cements with different chemical properties on the shear bond strength, together with the change in roughness and wettability. In our study, in accordance with the manufacturing procedure of restorations in clinical practice, zirconia samples were digitally designed and milled from monolithic zirconia discs (inCoris TZI C, Dentsply Sirona, USA) using a CAM device (MC X5, Dentsply Sirona, USA), after that sintered with the help of a sintering furnace (inFire HTC Speed, Dentsply Sirona, USA). The prepared samples (n=88) were randomly divided into 4 groups as a control and three surface treatments (Sandblasting, Rocatec and Z-Prime). No surface treatment was applied in the control group (n=22). In the sandblasting group (n=22), the sample surfaces were roughened with 50 µm Al2O3 sand. In Rocatec group (n=22), surfaces were roughened with 30 µm Al2O3 sand which modified with silica (Rocatec Soft, 3M ESPE, Seefeld, Germany) and then silane was applied. In the Z-Prime group (n=22), Z-Prime Plus (BISCO, Schaumburg IL, U.S.A), a primer containing MDP, was applied to zirconia surfaces after roughening with 50 µm Al2O3 sand. Roughness (Ra) and surface contact angle measurements were made from all samples. The prepared groups were randomly divided into two groups (n=11) to be bonded with MDP monomer containing Panavia SA and RelyX U200 without MDP. 10000 thermal cycles were applied to the samples whose cementation was completed. Immediately after the artificial aging process, shear force was applied to the cements and the bond strength values were recorded in MPa. As a result of the statistical analysis, the lowest wettability was observed in the control group, while the highest wettability was observed in the Z-Prime group (P<0.05). The highest roughness value was reached in the sandblasting group (P<0.05). When the average shear bond strengths within the groups are examined, the statistically significant highest value was observed in the Z-Prime group (P<0.05). The lowest values were observed in the control group in which the samples with RelyX U200 were separated during the thermal cycle. While there was no significant difference between the bond strengths of the two types of cement in the sandblasting and Rocatec groups, the bonding values of the RelyX U200 samples in the Z-Prime group were found to be statistically significantly higher than Panavia samples (P<0.05). Among all Panavia bonded samples, the highest bonding strength values were observed in the Rocatec and Z-Prime groups, and in the RelyX U200 bonded samples in the Z-Prime group (p<0.05). According to the results of our study, a surface treatment must be applied to establish a successful adhesion between zirconia and resin luting cement. The type of surface treatment preferred also plays an important role in the bond strength. In addition to processes such as sandblasting that provide only micromechanical bonding by increasing the roughness of the zirconia surface, processes that will strengthen the chemical bonding with resin cements such as silane application after silica coating or the application of primers increases the success of the adhesion. Increasing the variety of monomers used to provide chemical bonding also has a positive effect on the bond strength. It can be said that the increase in wettability strengthens the adhesion between resin cement and zirconia, but it is not enough to make a decision only by looking at the wettability feature. The mechanism of bonding between characteristic of created surface and resin luting cement should also be evaluated.
Benzer Tezler
- Çeşitli yüzey şartlandırma işlemlerinin üç farklı in-ceram kor yapısı ile bir dual-cure rezin siman arasındaki bağlanmaya etkisinin incelenmesi
The effect of different surface treatments on the bond strength of a dual cure resin cement to three various in-ceram ceramic
SEMİH TAŞVEREN
Doktora
Türkçe
2004
Diş HekimliğiCumhuriyet ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ.DR. ALİ KEMAL ÖZDEMİR
- Fiber lazer sistemi ve farklı yüzey pürüzlendirme yöntemleri uygulanarak yüzeyi pürüzlendirilen zirkonya materyali ile dentin arasındaki bağlantı kuvvetinin in-vitro olarak değerlendirilmesi
The evaluating in-vitro bond strength of zirconia surface that was roughed with fiber laser and different surface treatments techniques to dentin
SERVER ÜNAL
- Farklı yüzey şekillendirme işlemlerinin zirkonya rezin siman bağlantı dayanıklılığına etkilerinin incelenmesi
Evaluation od different surface treatments on shear bond strength of zirconia- resin cement
MERVE ÇAKIRBAY
Doktora
Türkçe
2014
Diş HekimliğiGazi ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. TURGUT CİHAN AKÇABOY
- Farklı yüzey işlemlerinin monolitik zirkonyumun sertlik ve yüzey pürüzlülüğü ile rezin siman bağlantı dayanımına etkisinin incelenmesi
Effect of different surface processes on monolithic zirconium hardness surface roughness and microtensile bond strength with resin cement
HAMZA ULU
Doktora
Türkçe
2015
Diş HekimliğiAtatürk ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. FUNDA BAYINDIR
- Zirkonya alt yapıya uygulanan farklı yüzey işlemlerinin zirkonya-siman arasındaki fiziksel bağlanma özelliklerine etkisinin araştırılması
Investigation of effects of surface treatment applied zirconia copings between zirconia-cement physical binding properties
BENGİSU YILDIRIM
Doktora
Türkçe
2014
Diş HekimliğiEge ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. AHMET SARAÇOĞLU