Translüsent monolitik zirkonya kron restorasyonlarında, ısısal ve mekanik yaşlandırmanın kırılma direncine etkisinin incelenmesi
Evaluation of the effect of thermal and mechanical aging on fracture strength of translucent monolithic zirconia crown restorations
- Tez No: 790858
- Danışmanlar: PROF. DR. HANDAN YILMAZ
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Dental restorasyon, Dental stres analizi, Kırılma, Yaşlandırma, Zirkonyum, Zirkonyum oksit, Dental restoration, Dental stress analysis, Fracture, Ageing, Zirconium, Zirconium oxide
- Yıl: 2023
- Dil: Türkçe
- Üniversite: Gazi Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Dental restorasyonlar ağız içinde görülen çiğneme ve yutkunma esnasında aralıklı olarak ısısal değişimlere ve oklüzal kuvvetlere maruz kalmaktadırlar. Bu amaçla tez çalışmasında 4 farklı içeriğe sahip yeni geliştirilen yüksek translüsent monolitik zirkonya materyali Nacera Pearl Multi Shade (NMS), Katana STML (KST), Katana UTML (KUT), Nacera Pearl Q3 Multi Shade (NCQ) ve 1 adet lityum disilikat IPS e.max CAD materyali kullanılarak ısısal ve mekanik yaşlandırma işleminin kırılma direncine etkisinin incelenmiştir. Bu amaçla tüm materyallerden 20 adet olmak üzere mandibular 1. molar monolitik kron restorasyonları üretilmiş, yapay dişlere adeziv olarak simante edilmiştir. Tüm mandibular 1. molar monolitik kron restorasyonları ısısal ve mekanik yaşlandırmanın kırılma direncine etkisinin değerlendirilmesi amacıyla 2 gruba ayrıldı. İlk gruba (n=50) ısısal ve mekanik yaşlandırma işlemi uygulanmadı, diğer gruba (n=50) ısısal ve mekanik yaşlandırma işlemi uygulandı. Tüm materyaller, Universal test cihazında kırılana kadar yüklenip, kırılma değerleri saptanarak Weibull dağılımına bağlı güvenilirlik analizi yapıldı. Isısal ve mekanik yaşlandırma uygulanan restorasyonların kırılma direncinde azalma meydana geldi (p<0,001). Isısal ve mekanik yaşlandırma işlemi uygulanan ve uygulanmayan gruplarda NMS materyalinin kırılma direnci ve karakteristik direnci diğer materyallerden yüksek bulundu. Isısal ve mekanik yaşlandırma işleminin uygulandığı grupta Weibull modülü ise en yüksek EMAX materyalinde bulundu.
Özet (Çeviri)
Dental restorations are exposed to intermittent thermal changes and occlusal forces during chewing and swallowing in the mouth. For this purpose, in the thesis study, the newly developed highly translucent monolithic zirconia material Nacera Pearl Multi Shade (NMS), Katana STML (KST), Katana UTML (KUT), Nacera Pearl Q3 Multi Shade (NCQ) with 4 different contents and 1 lithium disilicate IPS e.max CAD material have been used. The effect of thermal and mechanical aging on fracture strength was investigated. With this design, 20 mandibular first molar monolithic crown restorations were produced from all materials and adhesively cemented to artificial teeth. All mandibular first molar monolithic crown restorations were divided into 2 groups to evaluate the effect of thermal and mechanical aging on fracture strength. Thermal and mechanical aging was not applied to the first group (n=50), while thermal and mechanical aging was applied to the other group (n=50). Reliability analysis based on Weibull distribution was performed by loading all the materials until they fractured in the Universal testing device and determining the fracture strength values. There was a decrease in fracture strength of the restorations that applied thermal and mechanical aging (p<0.001). The fracture strength and characteristic strength of NMS material are higher than the other materials in the groups that applied and did not undergo thermal and mechanical aging. Weibull modulus was found in the highest EMAX material in the group in which the thermal and mechanical aging process was applied.
Benzer Tezler
- Farklı materyaller ile restore edilmiş farklı bağlantı sistemlerine sahip konometrik tek kron restorasyonlarda stres dağılımının 3 boyutlu sonlu elemanlar analizi ile değerlendirilmesi
Evaluation of stress distribution in conometric single crownrestorations with different connection systems restored with different materials using3d finite element analysis
SİNEM VURAL
- Tekrarlanan fırınlama işleminin zirkonya kronların marjinal uyum ve optik özelliklerine etkisinin araştırılması
Investigation of the effect of repeated firing on the marginal fit and optical properties of zirconia crowns
AYŞEGÜL ÜÇDAL ASLAN
- Translüsent monolitik zirkonya seramik sistemlerinde düşük ısı bozunmasının iki eksenli bükülme dayanıklılığı ve faz değişimine etkisinin incelenmesi
Evaluation of the effect of low temperature degradation on biaxial flexural strength and phase change of translucent monolithic zirconia ceramic systems
GÜLSÜM DOĞRU
- Monolitik yüksek translusent itriya parsiyel stabilize zirkonya sistemlerinde farklı yüzey işlemlerinin, yüzey pürüzlülüğü ve iki eksenli bükülme dayanımına etkisinin incelenmesi
Evaluation of the effect of different surface treatments on monolithic high translucent yttria partially stabilized zirconia systems on surface roughness and biaxial flexural
EZGİ GÜRSOY TAN
- Bilgisayar ile tasarlanarak üretilen translüsent monolitik zirkonya ve çift tabakalı zirkonya restorasyonların klinik başarılarının değerlendirilmesi
Clinical evaluation of CAD-CAM made translucent monolithic restorations and double-layered restorations
FİRUZAN TAN