Farklı sinterleme protokollerinin çok katmanlı monolitik zirkonya restorasyonların ışık geçirgenliğine ve bükülme dayanımına etkisinin incelenmesi
Investigation of the effect of different sintering protocols on LİGHT transmittance and flexural strength of multilayer monolithic zirconia restoration
- Tez No: 808633
- Danışmanlar: PROF. DR. DUYGU SARAÇ
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Bükülme Dayanımı, Hızlı sinterleme, Işık geçirgenliği, Monolitik zirkonya, Dental materyaller, Dental restorasyon, Dental stres analizi, Opaklık, Protetik diş tedavisi, Sinterleme, Zirkonyum, Flexural Strength, Speed sintering, Light transmittance, Monolithic zirconia, Dental materials, Dental restoration, Dental stress analysis, Opacity, Prosthetic dental treatment, Sintering, Zirconium
- Yıl: 2022
- Dil: Türkçe
- Üniversite: Ondokuz Mayıs Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Amaç: Bu tez çalışmasının amacı farklı sinterleme protokolü uygulanmasının, yapısında farklı mollerde yitrium ile stabilize edilmiş zirkonya tiplerini bir arada bulunduran çok katmanlı monolitik zirkonya restorasyonların ışık geçirgenliğine ve bükülme dayanımına etkisinin incelenmesidir. Materyal ve Metod: Çalışmamızda kullanılan örnekler presinterize A2 renkli çok katmanlı monolitik zirkonya bloktan (IPS e.max ZirCAD Prime, Ivoclar Vivadent, Schaan, Lihtenştayn) CAD/CAM teknolojisi kullanılarak üretilmiştir. Örnekler üç gruba ayrılarak (n=15) üretici talimatlarına uygun olacak şekilde standart, hızlı ve yüksek hızlı olmak üzere üç farklı protokolde sinterlenmiştir (Programat S2, Ivoclar Vivadent, Schaan, Lihtenştayn). Yüzey bitim işlemi olarak glaze uygulanan örneklerin ilk renk ölçümleri spektrofotometre (SpektroShade, MHT Optic Research, Niederhasli, İsviçre) ile yapılarak TP00 değeri saptanmıştır. Termal devirlendirme işlemi sonrası ikinci renk ölçümleri yapılan örneklere bükülme dayanımını incelemek için 4 nokta bükme testi uygulanmıştır. Çalışmanın istatiksel analizi için Tek Yönlü Varyans Analizi, Kruskal Wallis Testi ve Wilcoxon Testi kullanılmıştır ( p<0,05). Bulgular: Farklı sinterleme protokollerine göre TP00 değerlerinde anlamlı farklılık bulunmuştur (p<0,001). Termal devirlendirme öncesi ve sonrası TP00 değerleri karşılaştırıldığında yüksek hızlı (p=0,001) ve standart (p=0,036) sinterleme grupları arasında fark bulunurken, hızlı sinterleme grubunda fark bulunamamıştır (p=0,078). Yüksek hızlı sinterleme protokolü uygulanması bükülme dayanımının düşmesiyle sonuçlanmıştır (p=0,013). Sonuç: Hızlı sinterleme protokolü uygulanan grup en iyi bükülme dayanımı gösterirken, yüksek sinterleme sıcaklıklarının ve artan bekleme sürelerinin zirkonyanın yaşlanmaya bağlı ışık geçirgenliği stabilitesini olumsuz etkilediği tespit edilmiştir.
Özet (Çeviri)
Aim: The aim of this thesis study is to examine the effect of applying different sintering protocols on the light transmittance and flexural strength of multilayer monolithic zirconia restorations that contain different moles of yttrium-stabilized zirconia types. Materials and Methods: The samples used in our study were produced from pressinterized A2 colored multilayer monolithic zirconia block (IPS e.max ZirCAD Prime, Ivoclar Vivadent, Schaan, Liechtenstein) using CAD/CAM technology.The samples were divided into three groups (n=15) and sintered in three different protocols as standard, fast and high speed (Programat S2, Ivoclar Vivadent, Schaan, Liechtenstein) in accordance with the manufacturer's instructions. The first color measurements of the glazed samples were made with a spectrophotometer (SpektroShade, MHT Optic Research, Niederhasli, Switzerland) and the TP00 value was determined. After the thermal cycle process, the second color measurements were made, and the 4-point bending test was applied. One-Way Analysis of Variance, Kruskal Wallis Test and Wilcoxon Test were used for the statistical analysis of the study. Results: A significant difference was found in TP00 values according to different sintering protocols (p<0,001). When the TP00 values before and after the thermal cycle were compared, there was a difference between the high speed (p=0.001) and standard (p=0.036) sintering groups, but no difference was found in the fast sintering group (p=0.078). Application of high speed sintering protocol resulted in a decrease in flexural strength (p=0.013). Conclusions: While the group with the fast sintering protocol showed the best flexural strength, it was determined that high sintering temperatures and increased waiting times adversely affected the light transmission stability of zirconia due to aging.
Benzer Tezler
- Yaşlandırma ve sinterizasyon işlemlerinin tabakalı zirkonyum materyalleri üzerindeki bükülme dayanımı ve ışık geçirgenliğine etkisi
Effect of aging and sintering processes on flexural strength and light transmittance on multi-layered zirconium materials
AYÇA İPEK KAHAR
Diş Hekimliği Uzmanlık
Türkçe
2022
Diş HekimliğiNecmettin Erbakan ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
YRD. DOÇ. DR. CEYDA AKIN
- Farklı sinterizasyon hızlarının dental zirkonyaların optik özellikleri üzerine etkisi
Effect of different sintering protocols on the optical properties of dental zirconia
İBRAHİM TAŞ
Diş Hekimliği Uzmanlık
Türkçe
2025
Diş HekimliğiUşak ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. BENGİSU YILDIRIM
- Farklı sinterleme protokolleri ve yaşlandırma işleminin çok katmanlı zirkonya seramiklerin biaksiyel eğilme dayanımı üzerine etkisi
Effect of different sintering protocols and aging process on the biaxial flexural strength of multilayered zirconia ceramics
EZGİ KARACA CEYLAN
Diş Hekimliği Uzmanlık
Türkçe
2026
Diş HekimliğiSelçuk ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. MÜNİR TOLGA YÜCEL
- Monolitik zirkonya materyallerinin farklı sinterleme parametrelerinde optik ve mekanik özelliklerinin değerlendirilmesi
Effect of sintering conditions on the optical and mechanical properties of monolithic zirconia
BENSU ÇALIŞKAN ÇELİK
Doktora
Türkçe
2026
Diş Hekimliğiİstanbul ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. GÖKHAN AKGÜNGÖR
- İki farklı multilayer zirkonyum oksit restorasyon materyalinin fiziksel ve mekanik özelliklerinin karşılaştırılması
A comparative study on the physical and mechanical properties of two different multilayer zirconia based dental restorative materials
FURKAN ÇETİNTÜRK
Diş Hekimliği Uzmanlık
Türkçe
2025
Diş HekimliğiSüleyman Demirel ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. HAKKI CENKER KÜÇÜKEŞMEN