Fiberle güçlendirilmiş kompozit rezinler kullanılarak hazırlanan diş alt yapılarının CAD/CAM restorasyonların kırılma dayanımı değerleri üzerine etkisinin incelenmesi
Investigation of the effect of dental substructures prepared using fiber-reinforced composite resins on the fracture strength values of CAD/CAM restorations
- Tez No: 818893
- Danışmanlar: DOÇ. DR. NESLİHAN TEKÇE
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2023
- Dil: Türkçe
- Üniversite: Kocaeli Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Restoratif Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Restoratif Diş Tedavisi Bilim Dalı
- Sayfa Sayısı: 67
Özet
Amaç: Çalışmamızın amacı kanal tedavili üst premolar dişlere uygulanan fiberle güçlendirilmiş kompozit rezinlerin CAD/CAM restorasyonların kırılma dayanımlarına olan etkisinin değerlendirmektir. Metod: Çalışmamızda periodontal, protetik veya ortodontik amaçla çekilmiş 100 insan üst küçük azı dişi kullanıldı. Dişler yer düzlemine paralel olacak biçimde kendiliğinden sertleşen akrilik rezine gömüldü. Numuneler A1-2-3-4-5 ve B1-2-3-4-5 olmak üzere toplam 10 gruba ayrıldı (n=10). A1 ve B1 pozitif kontrol grubu olarak kabul edildi ve herhangi bir restoratif protokol uygulanmadı. Kontrol grupları yalnızca mine sement seviyesinin 3-mm (Grup-A1) ve 4-mm (Grup-B1) üzerinden kesilecek şekilde ayarlandı. Diğer tüm numuneler, mine sement seviyesinin 1-mm üzerinden kesildi. Arkasından, okluzali uzaklaştırılmış olan her bir dişin (A1 ve B1 grupları hariç) iki aproksimal kenarına da mine sement seviyesinin 2-mm altında ve 3-mm basmak genişliğinde olacak şekilde kaviteler hazırlandı. Hazırlanan her bir kavite mine sement seviyesinin 1-mm üzerine kadar, aproksimal duvar oluşturmak amacıyla akıcı bir kompozitle (GC Universal Flo) yükseltildi (ortalama 0,5-mm kalınlığında). A2 ve B2 grubunda kavitelerin tamamı Universal Flo ile dolduruldu. Fiberle güçlendirilmiş kompozit rezinlerin yer aldığı kalan gruplarda kavitelere 2-mm yüksekliğinde fiberler uygulandı ve üzerleri akıcı bir kompozitle kapatıldı. CAD/CAM blok Cerasmart restorasyon materyali olarak kullanıldı. A grubu numunelere 2-mm, B grubu numunelere 3-mm kalınlıkta olacak şekilde düz kesitler hazırlandı. Düz CAD/CAM kesitleri diş yüzeylerine dual cure siman ile simante edildi. Kırılma dayanım testi için 5-mm çapında küresel metal bir uç kullanılarak numunelere dik olacak şekilde kuvvet uygulandı. Her bir örneğin kırılma dayanım değerleri kaydedildi. Verilerin normal dağılıma uygunlukları Shapiro-Wilk testi ile incelendi. Normal dağılım gösteren değişkenler ortalama±standart sapma, normal dağılım göstermeyen değişkenler medyan (25.-75. yüzdelik) olarak verildi. Gruplar arasındaki farklılık normal dağılım varsayımı sağlandığında bağımsız örneklem t testi ve tek-yönlü varyans analizi ile, normal dağılım varsayımı sağlanmadığında Mann-Whitney U testi ve Kruskal-Wallis testi ile belirlendi. Hipotez testlerinde p
Özet (Çeviri)
Objective: The aim of our study was to evaluate the effect of fiber-reinforced composite resins applied to root canal-treated upper premolar teeth on the fracture strength of CAD/CAM restorations. Method: In our study, 100 human maxillary premolars extracted for periodontal, prosthetic, or orthodontic purposes were used. The teeth were embedded in self-curing acrylic resin parallel to the ground plane. The samples were divided into 10 groups as A1-2-3-4-5 and B1-2-3-4-5 (n=10). A1 and B1 were considered as positive control groups and no restorative protocol was applied. Control groups were set to cut only 3-mm (Group-A1) and 4-mm (Group-B1) above the enamel cement level. All other samples were cut 1-mm above the enamel cement level. Subsequently, cavities were prepared 2-mm below the enamel-cementum level and 3-mm pressing width on the two approximal edges of each tooth (except A1 and B1) of which occlusal had been removed. Each prepared cavity was elevated to 1-mm above the enamel cement level with a flowable composite (GC Universal Flo) (average 0.5-mm thick) to create an approximal wall. All cavities in groups A2 and B2 were filled with Universal Flo. In the remaining groups with fiber-reinforced composite resins, 2-mm high fibers were applied to the cavities and covered with a flowable composite. CAD/CAM block was used as Cerasmart restoration material. Straight sections were prepared with a thickness of 2-mm for group A samples and 3-mm thick for group B samples. Straight CAD/CAM sections were cemented to the tooth surfaces with dual cure cement. For the fracture strength test, a 5-mm diameter spherical metal tip was used and the force was applied perpendicular to the samples. The breaking strength values of each sample were recorded. The conformity of the data to the normal distribution was examined using the Shapiro-Wilk test. Normally distributed variables were given as mean±standard deviation, and non-normally distributed variables were given as median (25th-75th percentile). The difference between the groups was determined by independent sample t-test and one-way analysis of variance when the assumption of normal distribution was provided, and with the Mann-Whitney U test and Kruskal-Wallis test when the assumption of normal distribution was not met. P
Benzer Tezler
- Farklı fiberle güçlendirilmiş kompozit rezinlerin bulk fill kompozit rezinin eğme direncine etkisinin değerlendirilmesi
Evaluation of the effect of different fiber reinforced composite resins on the flexural strength of bulk fill composite resin
RUŞEN DEMİR
Diş Hekimliği Uzmanlık
Türkçe
2024
Diş HekimliğiDicle ÜniversitesiÇocuk Diş Hekimliği Ana Bilim Dalı
PROF. DR. BUKET AYNA
- Farklı fiberle güçlendirilmiş kompozit rezinler ile tedavi edilen kök kanal tedavili maksiller kesici dişlerde oluşan stres dağılımının sonlu elemanlar analizi ile değerlendirilmesi
Evaluation of stress distribution in root canal treated maxillary incisors treated with different fiber-reinforced composite resins by finite element analysis
ÖZGE SÖNMEZ UZEL
Diş Hekimliği Uzmanlık
Türkçe
2023
Diş HekimliğiDicle ÜniversitesiÇocuk Diş Hekimliği Ana Bilim Dalı
PROF. DR. BUKET AYNA
- Aşırı harabiyet gösteren endodontik tedavili dişlerin farklı materyaller ile restorasyonu
The restoration of badly broken pupless teeth with restorative materials
BAĞDAGÜL HELVACIOĞLU KIVANÇ
Doktora
Türkçe
2004
Diş HekimliğiGazi ÜniversitesiDiş Hastalıkları ve Tedavisi Ana Bilim Dalı
PROF.DR. GÜLİZ GÖRGÜL
- Farklı yöntemlerle polimerize edilen fiberle güçlendirilmiş akrilik rezinlerin artık monomer miktarının ve bazı fiziksel özelliklerinin değerlendirilmesi
Evaluation of the residual monomer amount and some physical properties of fiber reinforced acrylic resins polymerized by different methods
AYŞEGÜL KÖROĞLU
Doktora
Türkçe
2007
Diş HekimliğiAnkara ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF.DR. AHMET DURU PAMİR
- Sabit protetik restorasyonlarda kullanılan farklı içerikli CAD/CAM yüksek performans polimerleri ile indirekt kompozit veneer materyali arasındaki makaslama bağlanma dayanımının incelenmesi
Evaluation of shear bond strength between CAD/CAM HİGH performance polymers with different contents used in fixed prosthetic restorations and indirect composite veneer material
NAZİK İREM ÖNÜGÖREN
Diş Hekimliği Uzmanlık
Türkçe
2022
Diş Hekimliğiİnönü ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DR. ÖĞR. ÜYESİ FATİH DEMİRCİ
DR. ÖĞR. ÜYESİ NUMAN TATAR