Farklı seramik kalınlıklarının rezin simanın polimerizasyonuna etkisinin mikrosertlik ölçümü ile değerlendirilmesi
Evaluation of the effect of different ceramic thickness on the polymerization of resin cement by measurement of microhardness
- Tez No: 834380
- Danışmanlar: DOÇ. DR. AYŞE DÜNDAR
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: CAD/CAM, Dental porselen, Dental restorasyon, Dental çimentolar, Kompozit reçineler, Lityum silikat, Mikrosertlik, Polimerleşme, Zirkonyum, CAD/CAM, Dental porcelain, Dental restoration, Dental cements, Composite resins, Lithium silicate, Microhardness, Polymerization, Zirconium
- Yıl: 2023
- Dil: Türkçe
- Üniversite: Akdeniz Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Restoratif Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Amaç: Bu çalışmanın amacı, farklı seramik blokların ve kalınlıklarının ışıkla polimerize rezin simanın polimerizasyonuna etkisini, polimerizasyondan hemen ve 24 saat sonra yapılan Vickers mikrosertlik ölçümleri ile değerlendirmektir. Gereç ve Yöntem: Üç farklı seramik materyalden (Rezin nano seramik- Lava Ultimate (LU), Lösit ile güçlendirilmiş cam seramik- IPS Empress CAD (IPS), Zirkonyum ile güçlendirilmiş lityum silikat cam seramik- Celtra DUO (CD)) 0,5, 1 ve 2 mm kalınlıklarda örnekler hazırlandı (n=12). Seramik bloklar altında polimerize edilen bir ışıkla polimerize rezin simandan (Calibra Veneer, Denstsply) kontrol grubuyla birlikte 10 grup olucak şekilde toplam 120 adet örnek hazırlandı. Rezin siman örnekleri 6 mm çapında, 1 mm kalınlıkta bir teflon kalıpla hazırlandı ve bir LED ışık cihazı ile 30 sn ışıkla polimerize edildi. Tüm gruplar için hem alt hem üst yüzeylerinden Vickers mikrosertlik cihazı kullanılarak polimerizasyondan hemen ve 24 saat sonra mikrosertlik ölçümleri yapıldı. Çalışmadan elde edilen veriler tek yönlü ANOVA, bağımsız t testi ve Tukey testleri ile analiz edildi (p<0,05). Bulgular: Vickers mikrosertlik analizi sonucunda, rezin simanların üst yüzey mikrosertlik değerlerinin 0,5 mm LU grubu hariç kontrol grubuna göre düşük değerler gösterdiği bulgulanmıştır (p<0,05). Alt yüzey değerleri ise tüm gruplarda kontrol grubuna göre düşüktür. Tüm gruplarda polimerizasyondan hemen ve 24 saat sonra yapılan hem alt hem üst yüzey mikrosertlik ölçümlerinde anlamlı fark bulunmuştur (p<0,05). Rezin simanların alt-üst yüzey mikro sertlik oranları incelendiğinde ise tüm örnekler 0,80 kabul edilebilir eşik değeri geçmiştir. Sonuç: Işıkla polimerize rezin simanların mikrosertlik değerleri farklı seramik bloklarından ve kalınlıklarından etkilenmektedir. Simanların mikrosertliği polimerizasyondan 24 saat sonra artmaktadır.
Özet (Çeviri)
Objective: The aim of this study was to evaluate the effect of different ceramic blocks and thicknesses on polymerization of light-cured resin cement, with the measurements of Vickers microchardness performed immediately and 24 hours after polymerization. Materials and Methods: Samples of 0.5, 1 and 2 mm thicknesses were prepared from three different ceramic materials (Resin nano ceramic- Lava Ultimate (LU), Leucite reinforced glass ceramic- IPS Empress CAD (IPS), Zirconium-reinforced lithium silicate glass ceramic- Celtra DUO (CD)) (n =12). A total of 120 samples were prepared from a light-cure resin cement (Calibra Veneer, Denstsply) that was polymerized under ceramic blocks, with 10 groups including the control group. Resin cement samples were prepared with a 6 mm diameter, 1 mm thick teflon mold and light cured for 30 seconds with an LED light device. Microhardness measurements were made immediately and 24 hours after polymerization using a Vickers microhardness device on both the upper and lower surfaces of all groups. Data were analyzed using one way ANOVA, independent t and Tukey HSD tests (p <0.05). Results: As a result of Vickers microchardness analysis, it was found that the upper surface microhardness values of the resin cement show low values compared to the control group except for the 0.5 mm LU group (p <0.05). The lower surface values are low in all groups compared to the control group. In all groups, a significant difference was found in both the upper and lower surface microhardness measurements performed immediately and 24 hours after polymerization (p <0.05). When the lower upper surface microhardness ratios of the resin cements were examined, all samples have passed 0.80 acceptable threshold value. Conclusion: The microhardness values of light-cured resin cements are affected by different ceramic blocks and their thicknesses. The microhardness of the cements increases 24 hours after polymerization.
Benzer Tezler
- Zirkonya ile güçlendirilmiş lityum silikat cam seramik kalınlığının ışıkla polimerize rezin simanın polimerizasyon dönüşüm derecesine etkisinin değerlendirilmesi
Evaluating the effect of zirconia reinforced lithium silicate glass ceramic thickness on the degree of conversion of LIGHT-cured resin cement
GÜLEN DAL
Diş Hekimliği Uzmanlık
Türkçe
2022
Diş HekimliğiKütahya Sağlık Bilimleri ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DR. ÖĞR. ÜYESİ BANU ÇUKURLUÖZ BAYINDIR
- Farklı kalınlıklardaki CAD/CAM seramiklerin dual-cure ve light-cure rezin siman polimerizasyonlarına etkisi
Effect of CAD/CAM ceramics of different thicknesses on dual-cure and light-cure resin cement polymerizations
BURHAN ARSLAN
Doktora
Türkçe
2023
Diş HekimliğiSelçuk ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. TUBA YILMAZ SAVAŞ
- Farklı renk ve kalınlıklardaki zirkonyum seramiklerin ışık geçirgenliği
Light transmission of zirconium ceramics with different color and thickness
İBRAHİM DURAN
Doktora
Türkçe
2011
Diş HekimliğiOndokuz Mayıs ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. AHMET UMUT GÜLER
- Farklı kalınlıklardaki CAD/CAM seramiklerin rezin siman polimerizasyonuna olan etkisi
The effect of CAD/CAM ceramics of different thickness on resin cement polymerization
MUSTAFA BORGA DÖNMEZ
Diş Hekimliği Uzmanlık
Türkçe
2018
Diş HekimliğiSelçuk ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. MÜNİR TOLGA YÜCEL
- Lityum disilikat esaslı press-seramik sistemlerinin farklı seramik kalınlıkları ve farklı polimerizasyon yöntemleri kullanıldığında dentine bağlantı etkisinin incelenmesi
Influence of ceramic thickness and polymerization technique on bond strength of a resin luting agent with a lithium disilicate-based press-ceramic system
AKGÜNGÖR NEVAL
Doktora
Türkçe
2009
Diş Hekimliğiİstanbul ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. YASEMİN ARAS