Geri Dön

Farklı özelliklere sahip polimer malzeme kullanılarak değişik extrüzyon parametreleriyle boru imalatı ve karakterizasyonu

Manufacture and characterization of pipes with different extrusion parameters using polymer materials with different properties

PDF İndir

  1. Tez No: 859306
  2. Yazar: HARUN SEVİNÇ
  3. Danışmanlar: PROF. DR. BEKİR YALÇIN
  4. Tez Türü: Yüksek Lisans
  5. Konular: Mühendislik Bilimleri, Engineering Sciences
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2024
  8. Dil: Türkçe
  9. Üniversite: Afyon Kocatepe Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Makine Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 118

Özet

Bu yüksek lisans tezinde, mesken ısıtma sisteminde kullanılan plastik boruların değişik extrüzyon imalat parametreleri göz önüne alınarak, verimlilik ve dayanıklılık özellikleri deneysel araştırılmıştır. Polimer esaslı boruların, kullanım alanı olarak mesken içerisine, strafor yardımıyla döşemesi yapılmakta ve şap malzemesi ile kapatılarak üzerine mesken mimari etkisine göre parke, fayans, mermer vb. eklentiler uygulanmaktadır. Bu borularda oluşacak lokal veya genel arızaların tamiratı, yapılan mimari eklentilerin bozulmasına ve maddi-manevi kayıplara sebep olacaktır. Ayrıca, uzun ömürlülük göstermeyip kısa süre içerisinde hasara uğrayan boruların tamiratı, insanların yaşam kalitesi ve refah düzeylerini olumsuz etkilediği bilinen bir gerçektir. Hatta, boru ve imalat arızla nedeniyle çok katlı binalarda oluşan su kaçağının binanın mali değerinin ve dayanıklılığının düşmesine sebep olmakla birlikte binanın ısıtma sisteminde enerji kaybına da yol açmaktadır. Bu bağlamda, XP 9000 polietilen (PE), XP 9020 PE, geri dönüştürülmüş PE, XP9020 ile geri dönüştürülmüş PE karışımından oluşan dört farklı granül polimer malzeme ile dört farklı ekstrüzyon sıcaklığı (oC) ile (180oC, 200 oC, 220 oC, 245 oC) ve dört farklı ekstrüzyon hızı (d/d) ile (35 d/d, 38 d/d, 42 d/d ve 46 d/d) ve dört ekstrüzyon çekme hızı (m/d) ile (14 m/d, 15 m/d, 16 m/d ve 17 m/d) seçilerek, L16 Taguchi deney tasarımı yapılmış ve 16 adet boru numunesi imal edilmiştir. Bu numunelerden sadece 9 numunede somut boru elde edilebilmiştir. Diğer deney koşulları ile somut boru elde edilememiştir. Elde edilebilen 9 adet boru numunesi üzerinde mikroskobik çap ölçümü, yüzey düzgünsüzlülüğü ve esneklik tayin edilmeye çalışılmış olup, sadece bir boru numunesinin kullanılabilir olduğu belirlenmiştir. Akabinde bu numuneye, standart basınç, sıcaklık, buhar testlene tabi tutulmuştur. Sonuçta, XP 9000 PE hammadde kullanılarak 180oC ekstrüzyon sıcaklığı, 38 d/d helezon hızı ve 16 m/d çekme hızı ile imal edilen borunun test sonuçları kullanılabilirlik açısından anlamlı olabileceği kanaati oluşmuştur. Elde edilen numuneyi piyasa da markalaşmış 4 adet boru numunesiyle sıcaklık, basınç, yüzey pürüzlülüğü ve basma deneyleri bakımından kıyaslanmıştır. Sonuç olarak X boru numunesi A, B, C, ve D ticari boru numuneleriyle tezin araştırma konusu kapsamında benzer olabileceği kanaatine varılmıştır.

Özet (Çeviri)

In this master's thesis, the efficiency and durability characteristics of plastic pipes used in residential heating systems were experimentally investigated by considering various extrusion manufacturing parameters. Polymer-based pipes, intended for residential use, are laid with the assistance of styrofoam within the residence and covered with screed material. Subsequently, architectural enhancements such as parquet, tiles, marble, etc., are applied based on the architectural style of the residence. The repair of local or general faults in these pipes may lead to the deterioration of the applied architectural enhancements and result in material and immaterial losses. Moreover, the repair of pipes that do not demonstrate longevity and are prone to damage in a short period negatively impacts the quality of life and well-being of individuals. In fact, water leakage in multi-story buildings due to pipe and manufacturing defects not only reduces the building's monetary value and durability but also results in energy loss in the heating system of the building. In this context, a L16 Taguchi experimental design was implemented with four different granular polymer materials, namely XP 9000 polyethylene (PE), XP 9020 PE, recycled PE, and a mixture of XP9020 with recycled PE. Four different extrusion temperatures (180°C, 200°C, 220°C, 245°C), four extrusion speeds (35 d/d, 38 d/d, 42 d/d, and 46 d/d), and four extrusion draw rates (14 m/d, 15 m/d, 16 m/d, and 17 m/d) were selected for the manufacturing process, resulting in the production of 16 pipe samples. However, only 9 samples yielded concrete pipes, while others did not meet the specified conditions. Microscopic diameter measurement, surface roughness, and flexibility were attempted to be determined on the obtained 9 pipe samples, and only one pipe sample was found to be usable. Subsequently, this sample was subjected to standard pressure, temperature, and steam tests. Ultimately, the test results of the pipe manufactured using XP 9000 PE raw material, with an extrusion temperature of 180°C, a helix speed of 38 d/d, and a draw rate of 16 m/d, were deemed meaningful in terms of usability. The obtained sample was then compared with four commercially branded pipe samples in the market in terms of temperature, pressure, surface roughness, and compression tests. As a result, it was concluded that the X pipe sample could be similar to A, B, C, and D commercial pipe samples within the scope of the thesis research.

Benzer Tezler

  1. Tez No

    605419

    Reaktif ekstrüzyon ile mobilya atığı ahşap unu/polipropilen kompozitlerin silan bazlı uyumlaştırıcılar kullanılarak üretilmesi ve özelliklerinin incelenmesi

    Production and properties of waste wood fibers / polypropylene composites by reactive extrusion using silane-based compatibilizers

    ELİF AYDEMİR

    Yüksek Lisans

    Türkçe

    Türkçe

    2019

    Ağaç İşleriBursa Teknik Üniversitesi

    Biyokompozit Mühendisliği Ana Bilim Dalı

    DOÇ. DR. MAHMUT ALİ ERMEYDAN

  2. Tez No

    172194

    Preparation of a lab scale extruder machine and investigation of the periodic surface distortions in extrusion of polyolefins and usage of novel processing aids to overcome these instabilities

    Labaratuvar boyutunda bir ekstruder makinesinin hazırlanması ve poliolefinlerin ekstruzyonunda peryodik biçim bozukluklarının yeni proses iyileştiriciler ile giderilmesi

    AHMET MERİÇ

    Yüksek Lisans

    İngilizce

    İngilizce

    2006

    Polimer Bilim ve Teknolojisiİstanbul Teknik Üniversitesi

    Polimer Bilim ve Teknolojisi Ana Bilim Dalı

    PROF.DR. NURSELİ UYANIK

  3. Tez No

    327320

    Characterization of baroplastics

    Baroplastiklerin karakterizasyonu

    ARİ ŞANT BİLAL

    Yüksek Lisans

    İngilizce

    İngilizce

    2011

    Polimer Bilim ve Teknolojisiİstanbul Teknik Üniversitesi

    Polimer Bilim ve Teknolojisi Ana Bilim Dalı

    PROF. DR. METİN HAYRİ ACAR

  4. Tez No

    594391

    Çekirdekleştirici ajanların, geri dönüştürülmüş polipropilenin yapısal ve fiziksel özellikleri üzerine etkilerinin incelenmesi

    The investigation of the effect of the nucleating additives on the thermal and mechanical properties of recycled polypropylene

    METE EVREN BERKTAŞ

    Yüksek Lisans

    Türkçe

    Türkçe

    2019

    Polimer Bilim ve TeknolojisiYalova Üniversitesi

    Polimer Mühendisliği Ana Bilim Dalı

    PROF. MUSTAFA ÖKSÜZ

  5. Tez No

    168912

    Farklı oranlardaki EPDM/PP dinamik vulkanize karışımlarının mekanik, termal ve morfolojik özelliklerinin incelenmesi

    Influence of different contents EPDM/PP blends mechanical, thermal and morphologycal properties

    MURAT TOPSAKALOĞLU

    Yüksek Lisans

    Türkçe

    Türkçe

    2004

    Metalurji MühendisliğiMarmara Üniversitesi

    Metal Eğitimi Ana Bilim Dalı

    Y.DOÇ.DR. HALİL DEMİRER

    Y.DOÇ.DR. MÜNİR TAŞDEMİR

Geri Dön