Konvansiyonel, eksiltmeli ve tabakalı üretim yöntemleri ile farklı yüksekliklerde üretilen oklüzal splint materyallerinin aşınmasının değerlendirilmesi
Evaluation of wear of occlusal splint materials produced at different heights using conventional, subtractive and additive manufacturing methods
- Tez No: 869349
- Danışmanlar: DOÇ. DR. ÖZGÜN YUSUF ÖZYILMAZ
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2024
- Dil: Türkçe
- Üniversite: Bezm-i Alem Vakıf Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 104
Özet
Bu çalışmanın amacı; konvansiyonel, eksiltmeli ve tabakalı üretim yöntemleriyle farklı yüksekliklerde üretilen oklüzal splint materyallerinin farklı zaman dilimlerinde termal ve mekanik yaşlandırma sonrası aşınma değerlerinin incelenmesidir. Konvansiyonel yöntemle ısı ile polimerize olan akrilik rezin, eklemeli yöntemle 3B baskı ile reçine ve eksiltmeli yöntemle PEEK ve PMMA bloktan elde edilen oklüzal splint materyalleri 2 mm, 4 mm ve 6 mm olarak 3 farklı yükseklikte, her yükseklik grubu için 10 örnek, toplamda 120 örnek 20 mm çapında üretilmiştir. Örneklerin aşınma değerlerin üretim sonrası 1 ay, 3 ay ve 6 ay klinik zaman dilimlerine denk gelen sürelerde termal ve mekanik yaşlandırma uygulanması sonucu karşılaştırılmıştır. 1 aylık zaman dilimine denk gelen sürede örneklere önce 5-55 oC termal yaşlandırma işlemi uygulanmıştır. Termal yaşlandırma uygulanan örnekler 1 aylık zaman dilimine denk 20.000 döngüde çiğneme simülatöründe mekanik yaşlandırma uygulanmıştır. Örnekler 1 aylık zaman dilimi termal ve mekanik yaşlandırma sonrası oluşan aşınma laboratuvar tarayıcısı ile dijital ortama aktarılmıştır. Elde edilen veriler Geomagic DesignX tersine mühendislik programına aktarılıp, işlem uygulanmamış örnek verileriyle çakıştırma yöntemi uygulanarak hacim kaybı mm3 cinsinden elde edilmiştir. 3 aylık ve 6 aylık zaman dilimleri için uygulanacak termal ve mekanik yaşlandırma sonucu aşınma ile oluşan hacim kaybının ölçümü aynı şekilde gerçekleştirilmiştir. Elde edilen verilerin normallik testlerine Shapiro-Wilk testi ile bakılmıştır. Verilerin normal dağılmamasından dolayı gruplar arasındaki karşılaştırmalara Kruskall-Wallis H testi ile grup içi karşılaştırmalara ise Mann-Whitney U testi testi ile bakılmıştır. Örneklerin aşınma öncesi ve aşınma sonrası karşılaştırması Wilcoxon testi ile bakılmıştır. Anlamlılık seviyesi olarak 0,05 kullanılmış olup, p0,05 olması durumunda ise anlamlı farklılığın olmadığı belirtilmiştir. Çalışmamızda yapılan istatistiksel analiz sonuçlarına göre farklı üretim yöntemiyle üretilen her örnek grubunda 6 aylık zaman dilimlindeki aşınma oranı istatistiksel olarak anlamlı derecede en yüksek (p0,05). 3 ve 6 aylık zaman diliminde örneklerin kendi yükseklik grupları içinde konvansiyonel yöntemle ısı ile polimerize olan ProBase materyali dışında istatistiksel olarak anlamlı fark görülmemiştir (p>0,05). Aynı yükseklik grubunda materyallerin farklı zaman dilimlerinde karşılaştırmasında eksiltmeli yöntemle üretilen PEEK materyali istatistiksel olarak anlamlı derecede en düşük aşınma değerlerini(p0,05).
Özet (Çeviri)
SUMMARY The purpose of this study; It is the examination of the wear values of occlusal splint materials produced at different thickness by conventional, subtractive and additive manufacturing methods after thermal and mechanical aging in different time periods. Occlusal splint materials obtained from acrylic resin polymerized by heat with the conventional method, resin with 3D printing with the additive method, and PEEK and PMMA blocks with the subtractive method were used in 3 different thickness as 2 mm, 4 mm and 6 mm, 10 samples for each thickness group, 120 samples in total. It is produced in 20 mm diameter. The comparison of the wear values of the samples was compared as a result of applying thermal and mechanical aging for periods corresponding to the clinical time periods of 1 month, 3 months and 6 months after production. The samples were first subjected to a 5-55 oC thermal aging process for a period of 1 month. The thermally aged samples were mechanically aged in a chewing simulator for 20,000 cycles, equivalent to a period of 1 month. The wear of the samples after thermal and mechanical aging for a period of 1 month was transferred to the digital environment with a laboratory scanner. The obtained data was transferred to the Geomagic DesignX reverse engineering program and the volume loss was obtained in mm3 by applying the overlay method with the untreated sample data. The measurement of volume loss due to wear as a result of thermal and mechanical aging for 3 month and 6 month periods was carried out in the same way. Normality tests of the obtained data were checked with the Shapiro-Wilk test. Since the data were not normally distributed, comparisons between groups were made with the Kruskall-Wallis H test and within-group comparisons were made with the Mann-Whitney U test. Comparison of the samples before and after wear was made using the Wilcoxon test. 0.05 was used as the significance level, and if p0.05 it was stated that there was no significant difference. According to the results of the statistical analysis conducted in our study, in each sample group produced with different production methods, the wear rate in the 6 month period is statistically significantly highest (p0.05). During the 3 and 6 month period, no statistically significant difference was observed within the thickness groups of the samples, except for the ProBase material, which was polymerized with heat using the conventional method (p>0.05). In the comparison of materials in the same thickness group in different time periods, the PEEK material produced by the subtractive method showed the statistically significantly lowest wear values (p0.05).
Benzer Tezler
- Dijital ve konvansiyonel yöntemlerle elde edilen oklüzal splintlerin dayanımlarının in vitro olarak değerlendirilmesi
In vitro evaluation of the strength of occlusal splints obtained by digital and conventional method
SUZAN EDA EYYUPOĞLU
Doktora
Türkçe
2023
Diş Hekimliğiİstanbul Medipol ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. HALENUR BİLİR
- Farklı protez temizleme solüsyonlarının farklı tekniklerle üretilen akrilik kaide materyalleri ile yapay dişlerin bağlantısına etkisi
The effect of different cleaning solutions on the bonding strength of artificial teeth with acrylic base produced with different techniques
ELİF ÇELİK
Diş Hekimliği Uzmanlık
Türkçe
2023
Diş HekimliğiOrdu ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. DOĞU ÖMÜR DEDE
- Evaluation of the mechanical effects of thermal aging on Resin-Based indirect restoration materials produced by additive and subtractive manufacturing
Eklemeli ve eksiltmeli imalat ile üretilen reçine esaslı indirekt restorasyon materyallerinde termal döngü yaşlandırmanın mekanik etkilerinin değerlendirilmesi
HAMZA KÜRŞAT YILMAZ
Doktora
İngilizce
2024
Diş HekimliğiYeditepe ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. NURAY ÇAPA YILDIRIM
- Dijital ve konvansiyonel yöntemlerle elde edilen oklüzal splint materyallerinin aşınmasının in vitro olarak değerlendirilmesi
In vitro evaluation of wear of occlusal splint materials obtained by digital and conventional methods
CEREN AYGÜZEN
Doktora
Türkçe
2021
Diş Hekimliğiİstanbul Medipol ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DR. ÖĞR. ÜYESİ HALENUR BİLİR
DOÇ. DR. HALUK BARIŞ KARA
- Farklı yöntemler ile üretilmiş geçici restorasyonlarda: dijital olarak; uyum, doğruluk, kararlılık ve okluzal aşınmanın değerlendirilmesi: İn-vitro çalışma
In temporary restorations made with different methods: digitally; evaluation of fit, accuracy, stability and occlusal wear: İN-vitro study
SUAT GÜNGÖR
Diş Hekimliği Uzmanlık
Türkçe
2022
Diş HekimliğiNecmettin Erbakan ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DR. ÖĞR. ÜYESİ MEHMET ESAD GÜVEN