Çimentolu yongalevha endüstrisinde inovasyon; plastikli çimentolu yongalevha üretiminin fiziksel ve mekaniksel bazı özellikler üzerine etkilerinin belirlenmesi
Innovation in cement bonded particleboard industry; determination of the effects of plastic cement bonded particleboard production on some physical and mechanical properties
- Tez No: 930810
- Danışmanlar: PROF. DR. HASAN HÜSEYİN TAŞ
- Tez Türü: Doktora
- Konular: İnşaat Mühendisliği, Civil Engineering
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2025
- Dil: Türkçe
- Üniversite: Isparta Uygulamalı Bilimler Üniversitesi
- Enstitü: Lisansüstü Eğitim Enstitüsü
- Ana Bilim Dalı: İnşaat Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 95
Özet
Bu tez çalışmasının amacı, hedef yoğunluğu (d) 1.30 g/cm3 olan plastikli çimentolu yongalevha (PÇY) geliştirmektir. Bu amaçla, hammadde Kızılçam yerine farklı oranlarda Genleştirilebilir Polistiren (GPS) hammadde plastik ve Polipropilen Elyaf (PP), Polyester Elyaf (PYS), Cam Elyaf (CE), Poliüretan (PU) atık plastik ikamelerinden çalışma deseni oluşturulmuştur. Laboratuvar şartlarında çimentolu yongalevhalar üretilerek fiziksel ve mekaniksel bazı özellikleri standartlarına uygun deneysel çalışmalarla belirlenmiştir. Deney sonuçları, IBM SPSS-2023, çoklu varyans analizi (ANOVA) ve DUNCAN istatistik programlarıyla analiz edilmiştir. İstatistiklere göre, %10-15-20 karışım oranına sahip tüm deney grupları ile %25PYS ve PU deney grubu yongalevhalar TS EN 634-2 standarlarını sağlamıştır. En düşük Su Alma (SA), Kalınlığa Şişme (KŞ), Rutubet (R) değerleri sırasıyla %6.49-0.53-6.03 oranları ile %25GPS deney grubundan, en düşük ısı iletkenlik değeri (Iİ) 0.167 W/m°K ile %25PU deney grubundan, en yüksek eğilme dayanımı (ED) ve eğilmede elastikiyet modülü (EM) 11.22-7813 N/mm2 ile %15PYS deney grubundan, en yüksek vida tutunma direnci (VTD) 1451 N ile %15GPS deney grubundan elde edilmiştir. Plastiklerin, yapısal özellikleri ile karışım oranlarına göre matrisde değişen yayılımlarının, mekanik bağlanma mekanizmaları üzerindeki etkileri, levhaların en kesit ve yüzey SEM görüntülerinden incelenerek yapılan değerlendirmelerin deney sonuçlarını desteklediği görülmüştür. Genel olarak tez çalışmasının sonuçları, TS EN 634-2 standartlarını sağlayan plastikli çimentolu yongalevhalar üretilebildiğini, üretiminde atık PP, PYS, CE, PU plastik kullanımının çevresel faydalar sağlayacağını, hammadde GPS'nin su yalıtımında, PU'nun ise ısı yalıtımında levhalara üstün performans sunduğunu göstermiştir.
Özet (Çeviri)
The aim of this thesis is to develop plastic cement bonded particleboards (PCP) with a target density (d) of 1.30 g/cm3. For this purpose, a study pattern was created from different ratios of Expandable Polystyrene (EPS) raw material plastic and Polypropylene (PP), Polyester (PYS), Glass Fiber (GF), Polyurethane (PU) waste plastic substitutes instead of Red Pine. Cement bonded particleboards were produced under laboratory conditions and some physical and mechanical properties were determined by experimental studies in accordance with the standards. Experimental results were analyzed by IBM SPSS-2023, multiple analysis of variance (ANOVA) and DUNCAN statistical programs. According to the statistics, all experimental groups with %10-15-20 mixture ratio and %25PYS and PU experimental group particleboards met TS EN 634-2 standards. The lowest Water Absorption (WA), Thickness Swelling (TS), Moisture Content (MC) values were obtained from %25EPS experimental group with %6.49-0.53-6.03 and the lowest thermal conductivity value (TC) was 0.167 W/m°K from %25PU experimental group, the highest modulus of rupture (MOR) and modulus of elasticity (MOE) were obtained from %15PYS experimental group with 11.22-7813 N/mm2, the highest screw holding strength (SHS) was obtained from %15EPS experimental group with 1451 N. The effects of the structural properties of the plastics and their varying distribution in the matrix according to the mixture ratios on the mechanical bonding mechanisms were examined from the cross-sectional and surface SEM images of the plates and the evaluations made were found to support the experimental results. In general, the results of thesis study showed plastic cement bonded particleboards that meet TS EN 634-2 standards can be produced, the use of waste PP, PYS, GF, PU plastics in production will provide environmental benefits, the raw material EPS offers superior performance in waterproofing and PU in thermal insulation.
Benzer Tezler
- İçme suyu arıtma çamurunun çimentolu yonga levha üretiminde kullanımı
The use of drinking water sludge in wood cement particleboard production
MUSTAFA ASLAN
Yüksek Lisans
Türkçe
2007
Ormancılık ve Orman MühendisliğiKaradeniz Teknik ÜniversitesiOrman Endüstri Mühendisliği Ana Bilim Dalı
PROF.DR. HÜLYA KALAYCIOĞLU
- Uçucu kül kullanımının çimentolu yongalevhaların bazı özellikleri üzerine etkisi
Effects of fly ash on some properties of cemented particle boards
ELVAN ÜRÜN
Yüksek Lisans
Türkçe
2021
Ormancılık ve Orman MühendisliğiArtvin Çoruh ÜniversitesiOrman Endüstri Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ HÜSNÜ YEL
- Bazı üretim faktörleirnin çimentolu yongalevhaların özelllikleri üzerine etkileri
Effects of some manufacturing factors on the properties of cement bonded particleboards
HÜSNÜ YEL
Doktora
Türkçe
2015
Ağaç İşleriKaradeniz Teknik ÜniversitesiOrman Endüstri Mühendisliği Ana Bilim Dalı
PROF. DR. HÜLYA KALAYCIOĞLU
- A study on the utilization of waste cement-bonded wood particle board as a raw material and a secondary fuel in cement manufacturing
Atık çimentolu yonga levhanın çimento üretiminde hammadde ve ikincil yakıt olarak kullanılması üzerine çalışma
MUSTAFA YILMAZ
Yüksek Lisans
İngilizce
2012
Mühendislik BilimleriOrta Doğu Teknik ÜniversitesiÇimento Mühendisliği Ana Bilim Dalı
PROF. DR. ABDULLAH ÖZTÜRK
PROF. DR. MUSTAFA TOKYAY
- Atık elma dallarından üretilen çimentolu yonga levhanın mekanik ve fiziksel özelliklerinin incelenmesi
Investigation of mechanical and physical properties of cement bonded particleboard produced from waste branch of apple chips
KAAN ACAR
Yüksek Lisans
Türkçe
2019
Mühendislik BilimleriSüleyman Demirel ÜniversitesiYapı Eğitimi Ana Bilim Dalı
DOÇ. DR. HASAN HÜSEYİN TAŞ