AISI W1 ve L2 takım çeliklerinde düşük sıcaklık menevişlemesinin sertlik ve tokluk üzerine etkisi
Effect of low tempereture tempering on hardness and toughness of AISI W1 and L2 tool steels
- Tez No: 93538
- Danışmanlar: DOÇ. DR. BURHANETTİN İNEM
- Tez Türü: Yüksek Lisans
- Konular: Eğitim ve Öğretim, Metalurji Mühendisliği, Education and Training, Metallurgical Engineering
- Anahtar Kelimeler: Takım çelikleri, Menevişleme, Sertlik ve Darbe direnci, Darbe dayanımı, Isıl işlem, Sertlik, Sıcaklık, Tavlama, Tool steels, Tempering, Hardness and Impact energy, Impact strength, Heat treatment, Hardness, Temperature, Annealing
- Yıl: 2000
- Dil: Türkçe
- Üniversite: Gazi Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Metalurji Eğitimi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
AISI Wi ve L2 TAKIM ÇELİKLERİNDE DUŞUK SICAKLIK MENEVİŞLEMESİNİN SERTLİK ve TOKLUK ÜZERİNE ETKİSİ (Yüksek Lisans Tezi) Cemhan ONUR GAZİ ÜNİVERSİTESİ FEN BİLİMLERİ ENSTİTÜSÜ Ekim 2000 ÖZET Bu çalışmada AISI Wı ve L2 takım çeliklerinde sertleştirme ve menevişleme sonrası sertlik ve tokluk değişmeleri teorik ve deneysel olarak araştırılmıştır. Malzemelerden hazırlanan çekme ve U-çentik numuneleri 850°C'de 5 dakika östenitlenmiş, Wı suda, L2 yağda sertleştirilerek 120°C'de 1, 3, 5, 7, 9 ve 11 saat sürelerde menevişlenmiştir. Menevişlemenin ilk yedi saatlik bölümünde sertlik düşerken en yüksek tokluk, süneklik, darbe enerjisi ve çekme mukavemetlerine ulaşılmıştır. Dokuz ve on bir saat süre ile menevişlenmiş numunelerde sertlik artarken, dayanım ve darbe direncinde ani düşüşler meydana gelmiştir. Yedi saatlik menevişleme sonrası oluşan e ve T| karbürlerin 9 ve 11 saatlik menevişlemede martensit plakaları arasında kalıntı östenit içerisinde ince uzun parçacılar halinde düzenlenmeleri sertlikte artış sağlarken dayanım ve darbe direncinde ani düşüşlere sebep olmuşlardır. Bilim Kodu : 626.19.00
Özet (Çeviri)
11 EFFECT OF LOW TEMPERATURE TEMPERING ON HARDNESS and TOUGHNESS of AISI Wi and L2 TOOL STEELS (M. Sc. Thesis) Cemhan ONUR GAZİ UNIVERSITY INSTITUTE OF SCIENCE AND TECHNOLOGY October 2000 ABSTRACT In this study, changes in hardness and toughness of AISI Wi and L2 steels after hardening and tempering were investigated theoretically and experimentally. Tensile and U-notch specimens obtained from the bulk material were austenitised at 850°C for 5 minute, then Wi steel quenched at water and L2 steels quenched in oil and both Wi and L2 steels tempered at 120°C for 1, 3, 5, 7, 9, 11 hours. Hardness decreased in the period of first seven hours during tempering period but highest values of toughness, Impact energy and tensile strength were obtained. Hardness increased at tempering for 9 and 1 1 hours but toughness, ductility, tensile strength and impact energy decreased suddenly, e and rj carbides formed after tempering for 7 hours aligned together with remained austenite as longitudinal plates between martensite plates after tempering for 9 and 11 hours, therefore hardness increased but strength and impact energy suddenly decreased. Science code : 626.19.00
Benzer Tezler
- Çeltik kabuklarının yalıtım malzemesi olarak kullanılması
Başlık çevirisi yok
B.CİHAN ÇELEBİ
Yüksek Lisans
Türkçe
1986
Makine MühendisliğiUludağ ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
DOÇ. DR. MEHMET KIRBIYIK
- Mikrobiyoloji laboratuvarlarında kaza nedeni oluşan enfeksiyonlar
Başlık çevirisi yok
ŞENAY TÜRE
Yüksek Lisans
Türkçe
1986
MikrobiyolojiGazi ÜniversitesiKazaların Çevresel ve Teknik Araştırması Ana Bilim Dalı (disiplinlerarası)
PROF. DR. KAZIM KURTAR
- Sabit yatakta gaz fazına ısı transferinin incelenmesi
Başlık çevirisi yok
UĞUR ÇETİNKAYA
Yüksek Lisans
Türkçe
1987
Kimya MühendisliğiEge ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
DOÇ. DR. ERDEN ALPAY
- Kültür mantarı yetiştiriciliğinin ekonomik analizi ve yapılabilirliği
Başlık çevirisi yok
NECDET ÖZBİLGİN
- Soya fasulyelerinin ısı ile tedavi edilerek Soybean mosaic virus'tan arındırılması
Inactivation of Soybean mosaic virus by heat treatment on soybean cultivars
SEVGİ ÖZCAN ERDİMAN