Farklı 3D yazıcı rezinlerin renk stabilitelerinin karşılaştırılması
Comparison of color stability of different 3-D printed resins
- Tez No: 943292
- Danışmanlar: DOÇ. DR. SERDAR AKARSU
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: 3B yazıcı, CAD/CAM, kompozit rezin, renklenme, CNC frezeleme, Nanokompozitler, Üç boyutlu yazıcı, 3D printer, CAD/CAM, composite resin, staining, CNC milling, Nanocomposites, Three dimensional printer
- Yıl: 2025
- Dil: Türkçe
- Üniversite: Ordu Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Restoratif Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Zootekni Bilim Dalı
- Sayfa Sayısı: Belirtilmemiş.
Özet
Amaç: Bu çalışmanın amacı iki farklı 3 boyutlu yazıcı rezin, bir CAD/CAM rezin nanoseramik blok ve bir nanohibrit kompozit rezinin uzun dönem kahve solüsyonunda bekletildikten sonra renk stabilitelerini karşılaştırmaktır. Gereç ve Yöntem: Bu çalışmada rezin nanoseramik CAD/CAM blok (Grup CS, Cerasmart, GC Europe), nanohibrit kompozit rezin (Grup CME, Clearfil Majesty Esthetic, Kuraray) ve iki farklı 3 boyutlu yazıcı rezini (Grup VS, VarseoSmile Crown plus, BEGO ve Grup CT, Crowntec (CT, Saremco), SaremcoDental AG) kullanıldı. Her materyalden 8 mm çapında 2 mm kalınlıkta 20 numune olmak üzere toplam 80 disk şeklinde numune hazırlandı. Numuneler 30 gün boyunca her gün 45 dakika kahve solüsyonunda bekletildi. Kahve solüsyonu her gün yenisiyle değiştirildi. Numuneler günün geri kalanında distile suda bekletildi. Renk değişimi aynı gözlemci tarafından spektrofotometre (VITA Easyshade® Advance V, Vita Zahnfabrik, Bad Sackingen,Germany) ile 1.gün, 7.gün, 14.gün ve 1.ay sonunda kaydedildi. Renk farklılığını belirlemede CIEL*a*b* renk sistemi kullanıldı. Veriler one way ANOVA istatistiksel analiz ile değerlendirildi. Post hoc testi olarak Tukey testi kullanıldı. p anlamlılık değeri <0.05 kabul edildi. Bulgular: 30.günün sonunda, en az renk değişikliği Grup VS (ΔE=4.69)'de bulunurken, en fazla renk değişimi Grup CS (ΔE=5.60)'deydi. Gruplar arasında istatistiksel olarak anlamlı bir fark yoktu (p=0.69). Sonuçlar: 3B yazıcı rezinlerin renk değişikliği, CAD/CAM nanohibrit seramik bloklar ve kompozit rezinle benzerdi. Ancak tüm gruplarda renk değişimi klinik olarak kabul edilir değerin üzerindeydi (ΔE>1.8). 3 boyutlu yazıcılar ve eklemeli imalat rezinleri için daha fazla çalışmaya ihtiyaç vardır.
Özet (Çeviri)
Aim: The aim of this study was to compare the color stability of two different 3D printing resin blocks, a CAD/CAM resin nanoceramic block and a nanohybrid composite resin after long-term exposure to coffee. Material and Method: Resin nanoceramic CAD/CAM block (Group CS, Cerasmart, GC Europe), resin composite (Group CME, Clearfil Majesty Esthetic, Kuraray), and two different 3D printing resins (Group VS, VarseoSmile Crown plus, BEGO and Group SC, Crowntec (CT,Saremco), SaremcoDental AG) were used in this study. A total of 80 disk-shaped samples were prepared, 20 samples of each material with a diameter of 8 mm and a thickness of 2 mm. The samples were immersed in coffee solution for 45 minutes each day for 30 days. The coffee solution refreshed every day. The samples were kept in distilled water for the rest of the day. Color change was recorded by the same observer with a spectrophotometer (VITA Easyshade® Advance V, Vita Zahnfabrik, Bad Sackingen, Germany) at the end of day 1, week 1, week 2 and month 1. CIELa*b* color system was used to determine color difference. Data were evaluated with one-way ANOVA statistical analysis. Tukey tests was used as post hoc tests. p significance value was accepted as <0.05. Results: At the end of day 30, the least color change was found in Group VS (ΔE=4.69), while the most color change was in Group CS (ΔE=5.60). There was no statistically significant difference between the groups (p=0.69). Conclusions: The color change of 3D printed resins was similar to CAD/CAM nanohybrid ceramic CAD/CAM blocks and composit resin. However, the color change in all groups was above the clinically acceptable value (ΔE>1.8). More studies are needed for 3D printers and additive manufacturing resins.
Benzer Tezler
- CADCAM bloklarla 3D printer rezinlerin renk stabilizasyonu açısından kıyası
The comparison of CAD/CAM blocks and 3D-printed resins in terms of color stability
CANSU UYSAL
Diş Hekimliği Uzmanlık
Türkçe
2024
Diş HekimliğiMarmara ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
PROF. DR. CAFER TÜRKMEN
- Gastrik asidin 3 boyutlu yazıcı sistemleri ile üretilmiş daimi restoratif materyallerin mikrosertlik, yüzey pürüzlülüğü ve renk değişimi üzerine etkisi
Effect of gastric acid on microhardness, surface roughness, and color change of permanent restorative materials produced with 3D printer systems
AYÇANUR AYBİKE TURNA YETİŞ
Diş Hekimliği Uzmanlık
Türkçe
2025
Diş HekimliğiSivas Cumhuriyet ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
PROF. DR. ÖZDEN ÖZEL BEKTAŞ
- Üç boyutlu yazıcıyla farklı rezinler kullanılarak üretilen braketler ile seramik braketlerin renk stabilitesinin In Vitro ortamda karşılaştırılması
Comparison of color stability of brackets produced using different resins with a 3D printer and ceramic brackets: An In Vitro study
YAVUZ SELİM GENÇ
- Yeşil sentez gümüş nanopartikül katkılı nanofiber ile güçlendirilmiş polimetilmetakrilat (PMMA) rezin kompozitlerin üretilmesi ve antimikrobiyal ve mekanik aktivitelerinin değerlendirilmesi
Production of polimethylmethacrylate (PMMA) resin composites with green synthesis silver nanoparticles doped nanofiber and evaluation of their antimicrobial and mechanical activities
MERYEM ERDOĞDU
Doktora
Türkçe
2024
Diş HekimliğiNecmettin Erbakan ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. ALİ RIZA TUNÇDEMİR
- UV ışınına duyarlı kompozit reçinelerin sentezi, karakterizasyonu ve stereolitografi (SLA)-3D yazıcı reçinesi olarak kullanılabilirliğinin araştırılması
Synthesis and characterization of UV light sensitive composite resins and investigation of applicability as stereolithography (SLA)-3D printer resin
NURAN ÇELİKÇİ
Doktora
Türkçe
2022
Mühendislik BilimleriKahramanmaraş Sütçü İmam ÜniversitesiMalzeme Bilimi ve Mühendisliği Ana Bilim Dalı
PROF. DR. MEHMET TÜMER
DR. ÖĞR. ÜYESİ CENGİZ AYHAN ZIBA