Kompozit ambalaj atıklarından elde edilen PolyAl ile poliolefin masterbatchlerin hazırlanmasında kullanılacak uyumlaştırıcı sentezi ve PPRC boru üretimi
Synthesis of compatibilizer to be used in the preparation ofpolyolefin masterbatches and PPRC pipe production with PolyAl obtained from composite packaging waste
- Tez No: 946635
- Danışmanlar: DOÇ. DR. GÖKHAN CEYHAN
- Tez Türü: Yüksek Lisans
- Konular: Mühendislik Bilimleri, Engineering Sciences
- Anahtar Kelimeler: Poliolefin, PPRC, PolyAl, Kompozit Boru, Polimer Uyumlaştırıcı, Poliolefin, PPRC, PolyAl, Composite Pipe, Polymer compatibilizer
- Yıl: 2025
- Dil: Türkçe
- Üniversite: Kahramanmaraş Sütçü İmam Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Malzeme Bilimi ve Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu tezin amacı, geri dönüştürülmüş alüminyum partiküllerle takviye edilmiş poliolefin bazlı PolyAl malzemesinin üretim süreçlerini ve performans özelliklerini değerlendirmektir. Çalışmada, PPRC boru üretiminde kullanılan PolyAl katkılı kompozit yapıların üretim süreçleri ve kalite kontrol testleri kapsamında çekme, kopma, eğilme ve yüzey analizi testleri uygulanmıştır. Mekanik ve termal özelliklerin belirlenmesinde TS EN ISO 1133-1, ASTM D790/ISO 178 ve ISO 15874 standartları esas alınmıştır. Gerçekleştirilen çekme testlerinde, PE-Uyumlaştırıcı-PolyAl masterbatch'in, uyumlaştırıcı bulunmayan Pe-PolyAl (A1) yapısına göre %64 oranında daha yüksek mukavemet sağladığı tespit edilmiştir. Eğilme testlerinde kompozit yapının dayanımında artış gözlenmiştir. Yüzey analizlerinde, ara katmanda uyumlaştırıcı katkı bulunan numunelerde yüzey bütünlüğü korunmuş, mikro çatlak oluşumu gözlemlenmemiştir. Kimyasal direnç ve boru basınç testlerinde ISO 1167 ve ASTM D1598 standartlarına uygun değerlendirmeler yapılmış, PolyAl katkılı ve çok katmanlı yapının yüksek sıcaklık ve agresif kimyasal ortamlarda stabilitesini koruduğu belirlenmiştir. Bu bulgular, geri dönüştürülmüş PolyAl ve özgün uyumlaştırıcı senteziyle elde edilen kompozit yapıların, PPRC boru üretiminde ilgili mekanik ve kimyasal standartları sağladığını göstermektedir. Literatürde yer alan benzer çalışmalardan farklı olarak, bu tezde geri dönüştürülmüş alüminyumun endüstriyel ölçekte doğrudan uygulama potansiyeli ve uyumlaştırıcı katkıyla değerlendirilmiş, performans artışı sayısal olarak ortaya konmuştur.
Özet (Çeviri)
The aim of this thesis is to evaluate the production processes and performance characteristics of PolyAl material, which is based on polyolefin and reinforced with recycled aluminum particles. In this study, tensile, fracture, flexural, and surface analysis tests were conducted as part of the production processes and quality control tests of PolyAl-reinforced composite structures used in PPRC pipe manufacturing. Determination of mechanical and thermal properties was based on TS EN ISO 1133-1, ASTM D790/ISO 178, and ISO 15874 standards. In the tensile tests, it was determined that the PE-Compatibilizer-PolyAl masterbatch provided 64% higher strength compared to the Pe-PolyAl (A1) structure without compatibilizer. An increase in the flexural strength of the composite structure was observed in the flexural tests. Surface analyses showed that in samples containing compatibilizer in the intermediate layer, surface integrity was maintained and microcrack formation was not observed. In chemical resistance and pipe pressure tests, evaluations were carried out in accordance with ISO 1167 and ASTM D1598 standards, and it was determined that the PolyAl-reinforced and multilayer structure maintained its stability under high temperature and aggressive chemical environments. These findings demonstrate that the composite structures obtained with recycled PolyAl and original compatibilizer synthesis meet the relevant mechanical and chemical standards in PPRC pipe production. Unlike similar studies in the literature, this thesis evaluated the direct industrial-scale application potential of recycled aluminum together with compatibilizer contribution, and quantitatively revealed the performance improvement.
Benzer Tezler
- Ambalaj atıklarından elde edilen adsorbanlar aracılığıyla sulardan fosfor gideriminin incelenmesi
Investigation of phosphorus removal from water through adsorbents obtained from packaging waste
BÜŞRA KAVGACI
Yüksek Lisans
Türkçe
2022
Çevre MühendisliğiGiresun ÜniversitesiÇevre Bilimleri ve Teknolojileri Ana Bilim Dalı
PROF. DR. SAİT MALKONDU
- Production and characterization of biodegradable nanofibrous mats for food packaging applications
Gıda paketleme uygulamalari için biyolojik olarak parçalanabilir nanolifli matlarin üretimi ve karakterizasyonu
SALIH BIRHANU AHMED
Doktora
İngilizce
2025
Makine MühendisliğiKarabük ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
DOÇ. DR. HARUN ÇUĞ
DOÇ. DR. YASİN AKGÜL
- Gıda atıklarından farklı bitkisel katkı maddeleri kullanarak yenilebilir film üretimi
Edible film production using different herbal additives from food waste
BERİKA GİRGİN
Yüksek Lisans
Türkçe
2023
Kimya MühendisliğiYıldız Teknik ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
DOÇ. DR. NURCAN TUĞRUL
- Sustainable food packaging from hazelnut and artichoke agro-waste: Biodegradable film development using cellulosic and phenolic-rich extracts
Fındık ve enginar tarımsal atıklarından sürdürülebilir gıda ambalajı: Selülozik ve fenolik bileşenlerce zengin ekstraktlar kullanılarak biyobozunur film geliştirilmesi
İLAYDA HIZIR KADI
Doktora
İngilizce
2026
Gıda Mühendisliğiİstanbul Teknik ÜniversitesiGıda Mühendisliği Ana Bilim Dalı
PROF. DR. BERAAT ÖZÇELİK
- Kekik yağı ilave edilmiş tavuk jelatini/kitosan bazlı yenilebilir ambalaj film üretimi ve karakterizasyonu
Production and characterization of chicken gelatin/chitosan based edible packaging film with thyme oil
SÜMEYRA SELİN CESUR
Yüksek Lisans
Türkçe
2025
Gıda MühendisliğiBolu Abant İzzet Baysal ÜniversitesiKanatlı Hayvan Yetiştiriciliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ AYDIN ERGE