Farklı yüzey bitirme işlemleri uygulanan CAD/CAM seramik materyallerinin yüzey pürüzlülüğü ve bükülme dayanımının değerlendirilmesi
Evaluation of surface roughness and flexural strength of CAD/CAM ceramic materials subjected to different surface finishing procedures
- Tez No: 968234
- Danışmanlar: PROF. DR. ALİ KEMAL ÖZDEMİR
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Bükülme Dayanımı, CAD/CAM Seramikleri, Yüzey Pürüzlülüğü, CAD/CAM Ceramics, Flexural Strength, Surface Roughness
- Yıl: 2025
- Dil: Türkçe
- Üniversite: Biruni Üniversitesi
- Enstitü: Lisansüstü Eğitim Enstitüsü
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Protetik Diş Tedavisi Bilim Dalı
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu in vitro çalışmada, CAD/CAM lityum disilikat ve monolitik zirkonya disklere uygulanan farklı klinik yüzey bitirme protokollerinin yüzey pürüzlülüğü (Ra) ve iki eksenli bükülme dayanımı (FS) üzerindeki etkileri ile termal yaşlandırma sonrasındaki mikroyapısal değişimleri değerlendirmek amaçlandı. ISO 6872 standardına uygun biçimde hazırlanan 12 mm çaplı, 1.2 mm (kontrol) ve 1.3 mm (deney) kalınlıklı toplam 80 disk örnek (40 zirkonya, 40 lityum disilikat) dört alt gruba ayrıldı: Kontrol, Mekanik Cila (M), Glaze (G) ve Mekanik Cila + Glaze (MG) (n = 10). Deney gruplarında oklüzal uyumlamayı taklit eden 0.10 mm'lik aşındırma yapıldı; M ve MG gruplarında üç-aşamalı polisaj kitleri kullanıldı; G ve MG grupları IPS Ivocolor glaze ile pişirildi. Tüm numuneler 5 000 termal siklus (5 ± 1 °C / 55 ± 1 °C, 30 s daldırma) ile yaşlandırıldı. Ra değerleri temaslı profilometreyle, mikroyapı JEOL NeoScope JCM-5000 SEM'de ×500, ×1000, ×1500 büyütmelerde, FS ise ISO 6872'de tanımlı üç-top üzerinde piston test düzeneğinde (Shimadzu AGS-X, 1 mm/dk) ölçüldü. Veriler Shapiro–Wilk, Levene, tek ve iki faktörlü ANOVA, Tukey HSD ve Pearson korelasyon testleriyle analiz edildi (α = 0.05). Zirkonyada G ve MG işlemleri en düşük yüzey pürüzlülüğü değerlerini sağlamış olup, bu iki işlem arasında istatistiksel olarak anlamlı bir fark bulunmamaktadır (p=.910). E.max'ta, MG grubunun yüzey pürüzlülüğü M grubuna göre anlamlı düzeyde daha düşüktür (p ≤ 0.001); ancak glaze (p = .381) ve kontrol (p = .972) gruplarıyla anlamlı fark göstermemektedir. Zirkonyada en yüksek eğilme dayanımı mekanik cila işleminde; E.max'ta ise kontrol grubunda gözlenmiştir (p<0.001). Ra ve FS arasındaki ilişki zirkonyada orta düzeyde pozitif (p=.003), lityum disilikatta ise zayıf ve ters yönlü (p=.054) bulunmuştur. Bu sonuçlar, yüzey işlemlerinin etkinliğinin kullanılan seramiğe göre değiştiğini ve optimal klinik sonuçlar için materyal özelliklerinin dikkate alınması gerektiğini vurgulamaktadır.
Özet (Çeviri)
This in vitro study aimed to evaluate the effects of different clinical surface finishing protocols applied to CAD/CAM lithium disilicate and monolithic zirconia discs on surface roughness (Ra) and biaxial flexural strength (FS), as well as microstructural changes after thermal aging. A total of 80 disc specimens (40 zirconia, 40 lithium disilicate) with 12 mm diameter and thicknesses of 1.2 mm (control) and 1.3 mm (experimental) were prepared in accordance with ISO 6872 and divided into four subgroups: Control, Mechanical Polishing (M), Glaze (G), and Mechanical Polishing + Glaze (MG) (n = 10). In the experimental groups, a 0.10 mm reduction was performed to simulate occlusal adjustment; three-step polishing kits were used in the M and MG groups; and the G and MG groups were glazed with IPS Ivocolor. All specimens underwent 5,000 thermal cycles (5 ± 1 °C / 55 ± 1 °C, 30 s immersion). Ra was measured with a contact profilometer; microstructure was examined using a JEOL NeoScope JCM-5000 SEM at ×500, ×1000, and ×1500 magnifications; and FS was tested with a piston-on-three-ball fixture (Shimadzu AGS-X, 1 mm/min) per ISO 6872. Data were analyzed using Shapiro–Wilk, Levene, one- and two-way ANOVA, Tukey HSD, and Pearson correlation tests (α = 0.05). In zirconia, G and MG produced the lowest Ra values with no significant difference between them (p = .910). In lithium disilicate (E.max), MG showed significantly lower Ra than M (p ≤ .001), while differences from G (p = .381) and control (p = .972) were not significant. The highest FS was observed in mechanically polished zirconia, whereas in lithium disilicate the control group showed the highest strength (p < .001). The Ra–FS relationship was moderately positive in zirconia (p = .003) and weak and inverse in lithium disilicate (p = .054). These results indicate that the effectiveness of surface treatments is material-dependent, and optimal clinical outcomes require consideration of each ceramic's intrinsic properties.
Benzer Tezler
- Farklı yüzey işlemlerinin cad-cam materyallerin yüzey pürüzlülüğü ve renk stabilitesi üzerine etkilerinin değerlendirilmesi
Effect of different surface finishing procedures on the surface roughness and color stability of cad-cam materials
BURCU AÇAR
Diş Hekimliği Uzmanlık
Türkçe
2016
Diş HekimliğiGazi ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. FERHAN EĞİLMEZ
- CAD/CAM materyallerine uygulanan farklı polisaj metotlarının streptococcus mutans adezyonuna etkisi
Effect of different polishing methods on streptococcus mutans adhesion of CAD/CAM materials
NAZLI HİLAL GÜVENER
Diş Hekimliği Uzmanlık
Türkçe
2020
Diş HekimliğiBezm-İ Alem Vakıf ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. ÖZLEM KARA
- CAD-CAM tam seramik materyallerin renk, translusensi ve pürüzlülükleri üzerine polisaj ve glaze ışlemlerinin etkisinin değerlendirilmesi
Evaluation of the effect of polishing and glaze techniques on the color, translucency and surface roughness of CAD-CAM all-ceramic materials
SENA KAMACI ERGÜL
Diş Hekimliği Uzmanlık
Türkçe
2020
Diş HekimliğiHacettepe ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. SÜLEYMAN CUMHUR ALTINTAŞ
- Rezin nanoseramik esaslı materyalin bazı fiziksel özelliklerinin değerlendirilmesi
Evaluation of some the physical properties of resinnanoceramic based material
NEVRA NUR ÇİFTÇİ
Diş Hekimliği Uzmanlık
Türkçe
2023
Diş HekimliğiGazi ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. ÖZGÜL KARACAER
- Bazı esterlerin kinetik incelenmesi ve termodinamik parametrelerin belirlenmesi
Kinetic study and detesmination of thermodnamic parameters of some esters
İBRAHİM TAŞ
Yüksek Lisans
Türkçe
1986
Kimya MühendisliğiUludağ ÜniversitesiKimya Ana Bilim Dalı
PROF. DR. MUSTAFA CEBE