İki farklı rezin içerikli pit ve fissür örtücünün farklı modlarda adeziv sistem ile uygulanmasının mikrosızıntı üzerine etkisi
In Vitro evaluation of microleakage in two resin-based pit and fissure sealants applied with a universal adhesive in different etching modes
- Tez No: 969188
- Danışmanlar: DR. ÖĞR. ÜYESİ BEYZA ECEM ALKAÇ EKİCİ
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Adeziv sistem, diş çürüğü, mikrosızıntı, pit ve fissür örtücü, universal adeziv, Adhesive system, dental caries, microleakage, pit and fissure sealant, universal adhesive
- Yıl: 2025
- Dil: Türkçe
- Üniversite: Kütahya Sağlık Bilimleri Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Pedodonti Ana Bilim Dalı
- Bilim Dalı: Pedodonti Bilim Dalı
- Sayfa Sayısı: Belirtilmemiş.
Özet
Amaç: Bu in vitro çalışmada, dolduruculu ve doldurucusuz iki farklı rezin içerikli pit ve fissür örtücünün farklı modlarda universal adeziv sistem ile uygulanmasının mikrosızıntı değerleri üzerine etkisinin incelenmesi amaçlanmıştır. Gereç ve Yöntem: Farklı nedenlerle çekilmiş 84 adet daimi üçüncü molar diş, randomize olarak iki ana gruba ayrılmıştır. Grup A'da dolduruculu (Helioseal F Plus), Grup B'de ise doldurucusuz (Clinpro) pit ve fissür örtücü kullanılmıştır. Ardından gruplar randomize olarak, uygulama teknikleri açısından farklılıklar gösteren üç alt gruba ayrılmıştır (n=14). Hazırlanan örnekler 5-55°C aralığında 1000 devir termal siklus uygulamasından sonra %0,5'lik bazik fuksin solüsyonunda 24 saat bekletilmiştir. Örneklerden bukkolingual kesitler alınarak stereomikroskop altında 40X büyütmede mikrosızıntı değerleri incelenmiştir. Veriler R programı WRS2 paketi ve IBM SPSS V23 programı kullanılarak analiz edilmiştir. Normal dağılıma uygunluk Shapiro-Wilk Testi ile incelenmiştir. Üç ve üzeri gruplara göre normal dağılıma uyan değerlerin karşılaştırılmasında Tek Yönlü Varyans Analizi, gruplara göre normal dağılıma uymayan değerlerin karşılaştırılmasında Kruskal Wallis Testi kullanılmıştır. İkili gruplara göre normal dağılıma uyan değerlerin karşılaştırılmasında Bağımsız Örnekler t Testi, normal dağılıma uymayan değerlerin karşılaştırılmasında ise Mann Whitney U Testi kullanılmıştır. Mine yüzeyine ön asit uygulaması ve pit ve fissür örtücü tipinin etkisinin değerlendirilmesinde İki Yönlü Robust ANOVA analizi kullanılmıştır. Anlamlılık düzeyi p<0,05 olarak belirlenmiştir. Bulgular: Yapılan değerlendirmelerde, uygulama tekniğinden bağımsız olarak pit ve fissür örtücü tipinin mikrosızıntı değerleri üzerinde istatistiksel olarak anlamlı etkiye sahip olmadığı bulunmuştur (p=0,616). Pit ve fissür örtücü materyal tipinden bağımsız olarak, uygulama teknikleri değerlendirildiğinde, mikrosızıntı değerleri arasında istatistiksel olarak anlamlı farklılık bulunmuştur (p<0,001). Buna göre, minede ön asitleme ve universal adeziv kullanımı ile mikrosızıntı değerlerinde azalma gözlendiği saptanmıştır. Sonuç: Bu çalışmanın sınırları dahilinde elde edilen bulgular, minede ön asitleme ile universal adeziv kullanımının ve bundan bağımsız olarak minenin asitle pürüzlendirilmesinin önemini bir kez daha vurgulamaktadır. Pit ve fissür örtücü materyaller ve uygulama tekniklerini inceleyen uzun dönem takipli çalışmaların klinisyenlere yol gösterici olacağı düşünülmektedir.
Özet (Çeviri)
Aim: The aim of this in vitro study is to evaluate the microleakage values of two different resin-based pit and fissure sealant materials, by applying them using universal adhesive system in different etching modes. Material and Method: Eighty-four extracted permanent third molars, removed for various reasons, were randomly divided into two groups. Group A received a filled (Helioseal F Plus), and Group B received an unfilled sealant (Clinpro). Each main group was further randomly divided into three subgroups based on different application techniques (n=14). The specimens underwent 1000 thermal cycles between 5–55°C and were then immersed in 0.5% basic fuchsin solution for 24 hours. Buccolingual sections were obtained and examined under a stereomicroscope at 40X magnification to assess microleakage. Data were analyzed using the R software (WRS2 package) and IBM SPSS V23. Normality was evaluated with the Shapiro Wilk test. For data that were normally distributed across three or more groups, one way ANOVA was used. The Kruskal-Wallis test was used for non-normally distributed data. For comparisons between two groups, independent samples t-test was applied for normally distributed data, and the Mann-Whitney U test for non normally distributed data. Two-way robust ANOVA was used to evaluate the effects of enamel pre-etching and sealant type. The significance level was determined as p<0.05. Results: There was no statistically significant effect of sealant type on microleakage values, regardless of application technique (p=0.616). However, significant differences were found between application modes, independent of sealant type (p<0.001). Enamel pre-etching followed by universal adhesive application resulted in reduced microleakage. Conclusions: Within the limitations of this study, the findings emphasize the importance of enamel pre-etching combined with universal adhesive application, as well as the independent significance of enamel surface etching. Long-term follow up studies investigating various pit and fissure sealant materials and application techniques are warranted to better guide clinicians.
Benzer Tezler
- Polimerizasyon öncesi ısıtma işleminin fissür örtücülerin akışkanlığına etkisi
The effect of heating before polymerization on the flowability of fissure sealant
İSMAİL SEFA ÇAKIR
Diş Hekimliği Uzmanlık
Türkçe
2022
Diş HekimliğiZonguldak Bülent Ecevit ÜniversitesiPedodonti Ana Bilim Dalı
DOÇ. DR. EBRU HAZAR BODRUMLU
- Kavitasyonsuz fissür alanlarında kullanılan farklı ajanların çürük gelişimi ve klinik performans açısından değerlendirilmesi: randomize kontrollü klinik çalışma
Evaluation of caries progression and clinical performance of different agents on non-cavitated fissure areas: Randomized controlled clinical trial
SELMA EMIN OGLOU
Diş Hekimliği Uzmanlık
Türkçe
2021
Diş Hekimliğiİzmir Katip Çelebi ÜniversitesiÇocuk Diş Hekimliği Ana Bilim Dalı
DOÇ. DR. EBRU KÜÇÜKYILMAZ
- Fissür örtücü olarak kullanılan materyallere diş fırçalamanın etkisinin in-vitro incelenmesi
The effect of toothbrushing on materials used as fissure sealants: An in-vitro study
EDANUR GÖKCE MEYDAN
Diş Hekimliği Uzmanlık
Türkçe
2020
Diş HekimliğiAfyonkarahisar Sağlık Bilimleri ÜniversitesiÇocuk Diş Hekimliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ MEHMET ÜNAL
- Evaluation of Bisphenol-A release from different fissure sealant materials In Vitro
Farklı fissür örtücü materyallerinde Bisfenol-A salınımının In Vitro olarak incelenmesi
GÜLFEM ÇAVUŞOĞLU ÇARPAR
Doktora
İngilizce
2024
Diş HekimliğiYeditepe ÜniversitesiÇocuk Diş Hekimliği Ana Bilim Dalı
PROF. DR. DİDEM ÖZDEMİR ÖZENEN
- Yeni sürmüş çürüksüz daimi birinci molar dişlerde farklı içerikli fissür örtüleme materyallerinin klinik etkinliklerinin değerlendirilmesi
Clinical efficacy of different fissur sealant materials in the newly erupted non-carious first permanent molars
DERYA NAZLI SHAKIR
Diş Hekimliği Uzmanlık
Türkçe
2021
Diş Hekimliğiİzmir Katip Çelebi ÜniversitesiPedodonti Ana Bilim Dalı
DOÇ. DR. MERVE AKÇAY