SiCp takviyeli etial 171 (AlSi10Mg) alüminyum alaşım matrisli kompozitten basınçlı pres döküm yöntemiyle parça üretimi ve mekanik özelliklerinin incelenmesi

Production of etial 171 (AlSi10Mg) aluminium alloy based SiCp reinforced metal matrix composite piece by die casting method and investigation of mechanical properties

PDF İndir

  1. Tez No: 268863
  2. Yazar: HARUN BAYAR
  3. Danışmanlar: YRD. DOÇ. DR. ÇETİN KARATAŞ
  4. Tez Türü: Yüksek Lisans
  5. Konular: Makine Mühendisliği, Teknik Eğitim, Mechanical Engineering, Technical Education
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2009
  8. Dil: Türkçe
  9. Üniversite: Gazi Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Makine Eğitimi Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 123

Özet

SiCp TAKVİYELİ ETİAL 171 (AlSi10Mg) ALÜMİNYUM ALAŞIM MATRİSLİ KOMPOZİTTEN BASINÇLI PRES DÖKÜM YÖNTEMİYLE PARÇA ÜRETİMİ VE MEKANİK ÖZELLİKLERİNİN İNCELENMESİ(Yüksek Lisans Tezi)Harun BAYARGAZİ ÜNİVERSİTESİFEN BİLİMLERİ ENSTİTÜSÜAralık 2009ÖZETBu çalışmada, SiC parçacık takviyeli alüminyum esaslı kompozit malzeme Vorteks metodu ile üretilmiş ve aynı anda metal enjeksiyon makinesinde basınç altında kalıplanmıştır. Takviye malzemesi olarak 64 ?m boyutunda SiC parçacıkları hacimce %10 oranında ilave edilmiştir. Metal matris malzemesi metal enjeksiyon dökümüne uygun olan Etial 171 alüminyum alaşımı seçilmiştir. (Çekme ve Charpy darbe deneyi numuneleri beş farklı basınç altında; takviyesiz alaşım ve kompozit malzemeden beşer adet olmak üzere toplam on farklı parametrede üretilmiştir.) Metal enjeksiyon makinesi basınç değerleri 50, 100, 150, 200, 250 kg/cm2; enjeksiyon basıncı değerleri 313, 625, 938, 1250, 1563 kg/cm2 uygulanmıştır. Döküm sıcaklığı 670-680 ?C arasında gerçekleşmiştir. Çekme ve Charpy çentik deney numunelerinin dökümü için metal enjeksiyon kalıbı üretilmiştir. Numuneler üzerinde çekme deneyi, Charpy çentik darbe deneyi, sertlik ölçümü, optik mikroskopta mikroyapı incelemesi, gözenek ölçümleri yapılmıştır. SiC parçacık ilavesi ile kompozit numunelerin sertliği artmıştır. Kompozit numunelerin ortalama sertlik değeri 96 BHN, takviyesiz numunelerin ortalama sertlik değeri 86 BHN ölçülmüştür. Darbe deneylerinde alaşıma SiC parçacık ilavesi kompozit numunelerin darbe tokluğunu düşürmüştür. Kompozit numunelerin ortalama darbe tokluğu 3,51 J, takviyesiz alaşım numunelerinin 3,87 J ölçülmüştür. Kompozit numunelerin; çekme mukavemeti ortalama 233 MPa, akma mukavemeti ortalama 153 MPa, takviyesiz numunelerin; çekme mukavemeti ortalama 279 MPa, akma mukavemeti ortalama 186 MPa ölçülmüştür. Ayrıca enjeksiyon basıncının artmasıyla gözenek miktarının % 0,2'ye kadar düştüğü gözlenmiştir.Bilim kodu : 708.3.028Anahtar kelimeler : SiCp, metal matrisli kompozit, Vorteks yöntemi, parçacık,basınçlı pres döküm, Al alaşımıSayfa adedi : 105Tez Yöneticisi : Yrd. Doç. Dr. Çetin KARATAŞ

Özet (Çeviri)

PRODUCTION OF ETİAL 171 (AlSi10Mg) ALUMINIUM ALLOY BASED SiCp REINFORCED METAL MATRIX COMPOSITE PIECE BY DIE CASTING METHOD AND INVESTIGATION OF MECHANICAL PROPERTIES(M.Sc. Thesis)Harun BAYARGAZİ UNIVERSITYINSTITUTE OF SCIENCE AND TECHNOLOGYDecember 2009ABSTRACTIn this study, aluminum based SiCp reinforced metal matrix composite materials had been produced by vortex method and at the same time these materials were moulded under high pressure by die casting machine. The aluminium material was reinforced with 10 vol. % of SiC particles with an average size of 64?m. Etial 171 which is suitable for die casting, was chosen as a metal matrix. By this method; samples were produced at ten different parameters under five different pressures; five samples were produced as Al-alloy, other five samples were produced as metal matrix composites. Die casting machine pressure and inside pressure of mould values were 50, 100, 150, 200, 250 kg/cm2; 313, 625, 938, 1250, 1563 kg/cm2. The casting temperatures were between 670 and 680 ?C. Die casting mould was produced to be casted Charpy and tensile samples. Tensile strength test, Charpy impact test, hardness test, investigation of microstructure by optical microscope and porosity test were performed on those samples. Composite samples? hardness were increased after adding SiC particles. It was observed that; composite samples? hardness average value is 96 BHN, unreinforced alloy samples? hardness average value is 86 BHN. It was observed that; composite samples? tensile and yield strengths average values are 233 MPa and 153 MPa, unreinforced alloy samples? tensile and yield strengths average values are 279 MPa and 186 MPa. It was observed that increasing the pressure of injection causes decreasing porosity value is % 0,2.Scence code : 708.3.028Key Words : SiCp, metal matrix composite, Vortex method, particle, diecasting, Al-alloyPage number : 105Adviser : Assist. Prof. Dr. Çetin KARATAŞ

Benzer Tezler

  1. Tez No

    125815

    Al/SiC kompozitlerin infiltrasyon yöntemi ile üretimi ve özelliklerinin araştırılması

    Investigation of production and wear behavior of Al/SiC composites by vacuum infiltration technique

    MEHMET ACILAR

    Doktora

    Türkçe

    Türkçe

    2002

    Metalurji MühendisliğiGazi Üniversitesi

    Metal Eğitimi Ana Bilim Dalı

    YRD. DOÇ. DR. FERHAT GÜL

    PROF. DR. YUSUF ŞAHİN

  2. Tez No

    184428

    Savurma döküm yöntemiyle metal matriksli kompozit malzeme üretiminin araştırılması

    Investigation of metal matrix composite materials production by centrfugal casting

    ERSAN MERTGENÇ

    Yüksek Lisans

    Türkçe

    Türkçe

    2004

    Metalurji MühendisliğiAfyon Kocatepe Üniversitesi

    Metal Eğitimi Ana Bilim Dalı

    YRD. DOÇ. DR. YILMAZ YALÇIN

  3. Tez No

    79228

    Vorteks yöntemiyle üretilen partikül takviyeli alüminyum matriksli kompozit malzemenin mikroyapısal karakterizasyonu ve ısıl işlemleri

    Başlık çevirisi yok

    EBRU KARAGÖZ

    Yüksek Lisans

    Türkçe

    Türkçe

    1998

    Metalurji MühendisliğiYıldız Teknik Üniversitesi

    Metalurji Mühendisliği Ana Bilim Dalı

    PROF. DR. MÜZEYYEN MARŞOĞLU

  4. Tez No

    39525

    Alümina fiber takviyeli Al-si metal matriksli kompozitlerin üretimi ve mikroyapı-özellik ilişkilerinin incelenmesi

    production of alumina fiber reinforced Al-si metal matrix composites and the investigation of their microstructure-propetry relation ships

    HATEM AKBULUT

    Doktora

    Türkçe

    Türkçe

    1994

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    PROF.DR. FEVZİ YILMAZ

  5. Tez No

    493601

    Parçacık takviyeli Al matrisli kompozitlerin yorulma çatlak ilerleme hızı ve yorulma çatlak ilerleme mekanizmaları

    Fatigue crack growth rate and fatigue crack growth mechanisms i̇n particle reinforced Al matrix composites

    EŞREF ÇAKIR

    Yüksek Lisans

    Türkçe

    Türkçe

    2016

    MeteorolojiErciyes Üniversitesi

    Sivil Havacılık Ana Bilim Dalı

    YRD. DOÇ. DR. ADEM KARCI

Geri Dön