Farklı metal primer ve opakerlerin titanyum alaşım ile indirekt laboratuvar kompoziti bağlantısına etkisinin değerlendirilmesi

Effect of different metal primers and opaquers on shear bond strength between titanium alloy and indirect laboratory composites

  1. Tez No: 429177
  2. Yazar: AYŞE YALNIZ
  3. Danışmanlar: PROF. DR. ENDER KAZAZOĞLU
  4. Tez Türü: Doktora
  5. Konular: Diş Hekimliği, Dentistry
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2014
  8. Dil: Türkçe
  9. Üniversite: Yeditepe Üniversitesi
  10. Enstitü: Sağlık Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 172

Özet

Işıkla sertleşen indirekt kompozitlerin, diş dokularına benzer aşınma direnci, laboratuvar işlemleri ile tamirinin kolay olması ve tatmin edici estetiğinden dolayı kullanımı yaygınlaşmıştır. Metal alt yapı ile kompozit arasında kalıcı bir bağlantı sağlayabilmek zordur. Bu nedenle makro veya mikromekanik retansiyon oluşturmak için retansiyon incileri, kumlama gibi mekanik; silika kaplama ve fonksiyonel monomer sistemleri gibi kimyasal bağlantı yöntemleri vardır. İndirekt kompozit materyali ile titanyum alaşımlar arasındaki bağlantının başarısıyla ilgili tartışmalı ve sınırlı sonuçların varlığı bu iki materyalin bağlantısının temel dizaynı ile ilgili eksiklik olduğunu göstermektedir. Çalışmamızın amacı farklı metal primer ve opakerlerin, titanyum alaşım ile indirekt laboratuvar kompoziti bağlantısına etkisinin değerlendirilmesidir. Çalışmamızda 4 farklı indirekt kompozit sistemi kullanıldı ve 380 adet Ti6Al4V örnekler hazırlandı; Grup 1; 80 adet GC Metal Primer II, Grup 2; 100 adet Shofu ML Link, Grup 3; 100 adet Ivoclar Vivadent SR Link, Grup 4; 100 adet Bisco Z-Prime metal primer grupları oluşturuldu. 10 mm çapında ve 5 mm kalınlığındaki Ti6Al4V örneklerinin yüzey kumlama işlemi, kalem uçlu kumlama cihazıyla 50 μm Al2O3 partikülleri ile gerçekleştirildi. Grup 1'in 8 alt grubu, grup 2, 3 ve 4'ün ise 10'ar tane alt grupları vardır. Toplamda 10'ar örnekten 38 alt grup vardır. Alt gruplar ikiye ayrılırak 19 alt gruba termal siklus işlemi uygulandı, 19 alt gruba ise uygulanmadı. Deney için tüm örnek hazırlığı tamamlandıktan sonra kesme aygıtıyla 1 mm/dak. hızda kesme işlemi yapıldı. Niceliksel verilerin karşılaştırılmasında ve parametrelerin gruplar arası karşılaştırmalarında two-way ANOVA ve one-way ANOVA testi; farklılığa neden çıkan grubun tespitinde Tukey HSD testi kullanıldı. Parametrelerin iki grup arası karşılaştırmalarında Student t-test kullanıldı. Çalışmamızın sonucunda, deney gruplarına ait bağlanma kuvvetleri incelendiğinde; 38 grup içinde en yüksek bağlanma kuvveti değeri; Ti_6 Al_4 V alaşıma, Bisco Z Prime ve GC Gradia opakeri kullanılarak, GC Gradia indirekt kompozitinin bağlandığı termal siklus uygulanan grupta elde edilirken (Grup 4.3a: 13.74 ± 2,09 MPa), en düşük bağlanma kuvveti değeri ise; Ti_6 Al_4 V alaşıma, Ivoclar SR Link ve Bisco Tescera opakeri kullanılarak, GC Gradia indirekt kompozitinin bağlandığı termal siklus uygulanan grupta (Grup 3.3a: 3,29 ± 0,52 MPa) elde eldi. Metal primer gruplarının makaslama kuvvetleri arasında istatistiksel olarak anlamlı bir farklılık bulunmadı (p>0.05). Opakerlerin makaslama kuvvetleri arasında istatistiksel olarak anlamlı farklılık bulundu (p

Özet (Çeviri)

Indirect light-cured composite resins have been extensively used in tooth restoration because they can provide acceptable aesthetics, wear resistance similar to tooth structure, and are easy to manipulate in the laboratory and to repair. However, durable bonding between composite resins and metal frameworks has been challenge. Macro or micro mechanical retention on the metal substructures such as beads, loops and pits, or sandblasting and etching, were the only mechanisms for bonding composite materials to metallic substrates. However, recent developments resulting in chemical bonding have been achieved, including silicoating systems and functional monomers systems. Controversial and limited studies concerning adhesive performance between indirect composite and titanium alloys has led to the lack of an informed design rationale for bonding composite materials to titanium alloys. The current study evaluated the effect of different metal primers and opaquers on the bond strength between titanium alloy (Ti6Al4V) and indirect laboratory composites. For the present study, 4 diffent indirect composite systems and 380 Ti6Al4V samples were used. Groups were created by metal primer brands and divided into 4 main groups; Group 1 (GC, Metal Primer II) was consisted of 80, Group 2 (Shofu, ML Link) was consisted of 100, Group 3 (Ivoclar Vivadent, SR Link) was consisted of 100, Group 4 (Bisco, Z-Prime) was consisted of 100 samples. 10 mm diameter and 5 mm thickness Ti_6 Al_4 V alloy samples (as machined) were sandblasted with 50 μm Al2O3 particles. Group 1 was consisted of 8 subgroups and Group 2, 3 and 4 were consisted of 10 subgroups, totally there were 38 subgroups each have 10 samples. After sample preparations, thermal cycle application was performed to only 19 subgroups before testing and the remaining 19 subgroups were directly tested after by a shear bond strength machine with a 1 mm/min crosshead speed was used. Mean shear bond strengths and standard deviations were calculated. Statistical analysis of the data for all groups was accomplished by one-way ANOVA. Shear bond strengths differences between different groups were evaluated with two-way ANOVA. Multiple comparisons were made with Tukey's HSD test and Student t-test was used for the comparision of parameters between two groups. As a result, when evaluating the 38 test groups, the group which was prepared by Bisco Z Prime as metal primer, GC Gradia as opaquer, GC Gradia as indirect composite resin and thermal cycle procedure were applied showed the highest (Group 4.3a: 13.74 ± 2,09 MPa) value and the group which was prepared by Ivoclar SR Link as metal primer, Bisco Tescera as opaquer, GC Gradia as indirect composite resin and thermal cycle procedure were applied showed the lowest (Grup 3.3a: 3,29 ± 0,52 MPa) value. There was no significant difference between shear bond strengths of metal primer groups (p>0.05). There was significant differences between shear bond strengths of opaquer groups (p

Benzer Tezler

  1. Bir rezin simanın dört farklı metal alaşıma bağlanma dayanımına metal primelerin etkisi

    Effect of metal primers on bond strenght of a resin cement to 4 different metal alloys

    SONER KAHVECİOĞLU

    Doktora

    Türkçe

    Türkçe

    2006

    Diş HekimliğiSelçuk Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    PROF.DR. FİLİZ AYKENT

  2. Hareketli bölümlü protezlerde metal-akrilik rezin bağlanma dayanımı ve kenar sızıntısına metal primerlerin etkisi

    The effect of primers on shear bond strength and microleakage between removable partial denture metal-acrylic resins

    MEHMET BÜLBÜL

    Doktora

    Türkçe

    Türkçe

    2007

    Diş HekimliğiSelçuk Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    PROF.DR. BÜLENT KESİM

  3. Konus kuronlarda metal primer ile metal ve plastik sekonder kuronlarda tutunma kuvvetinin in vitro olarak incelenmesi

    In Vitro evaluation of retention in conical crowns with metal primer crown and metal and plastics based seconder crowns

    ÖZLEM ERDEM SAYIKLI

    Doktora

    Türkçe

    Türkçe

    1998

    Diş Hekimliğiİstanbul Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    PROF. DR. M. BABÜR CANİKLİOĞLU

  4. Farklı braket-kompozit kaide bağlantı yöntemlerinin, lingual braket tutuculuğuna olan etkilerinin in vitro olarak incelenmesi

    In vitro investigation of various bracket-composite base treatment methods on bond strength of lingual orthodontic brackets.

    BURAK AKSU

    Doktora

    Türkçe

    Türkçe

    2007

    Diş Hekimliğiİstanbul Üniversitesi

    Ortodonti Ana Bilim Dalı

    PROF. YILDIZ ÖZTÜRK ORTAN

  5. Yeni pirazinoporfirazinlerin sentezi ve özelliklerinin incelenmesi

    Synthesis of new pyrazinoporphyrazines and investigation of their propertiies

    RABİA ZEYNEP USLU KOBAK

    Doktora

    Türkçe

    Türkçe

    2009

    Kimyaİstanbul Teknik Üniversitesi

    Kimya Ana Bilim Dalı

    PROF. DR. AHMET GÜL