1,5 ve 3,0 T manyetik rezonans görüntüleme sistemlerinin dental metal alaşımların ve zirkonyumun karakteristik özelliklerine ve seramikle bağlantısına etkisinin incelenmesi

Effects of 1,5 and 3,0 t magnetic resonance imaging (MRİ) systems on the characteristic properties of dental metal alloys and zirconium, and their ceramic adhesion

PDF İndir

  1. Tez No: 452321
  2. Yazar: NURTEN BAYSAL
  3. Danışmanlar: DOÇ. DR. SİMEL AYYILDIZ
  4. Tez Türü: Diş Hekimliği Uzmanlık
  5. Konular: Diş Hekimliği, Dentistry
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2015
  8. Dil: Türkçe
  9. Üniversite: GATA
  10. Enstitü: Sağlık Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 164

Özet

1,5 ve 3,0 T Manyetik Rezonans Görüntüleme (MRG) sistemlerinin dental metal alaşımların ve zirkonyumun karakteristik özelliklerine ve seramikle bağlantısına etkisinin incelenmesi. Bu çalışmada MRG sistemindeki iyonize olmayan radyo dalgalarının ve manyetik alanın, sabit protetik restorasyonlarda kullanılan dental metal alaşımlar ile zirkonyum alt yapı materyallerinin karakteristik özelliklerine ve alt yapılar ile seramik arasındaki bağlantı direncine olan etkilerinin incelenmesi amaçlanmıştır. Çalışmada CoCr, NiCr, ZrO2 ve Ti materyallerinden, farklı üretim teknikleri ile disk (12mm çap 1mm kalınlık) (n=20) ve dikdörtgen prizması (2x2x4 mm3) (n=15) şeklinde örnekler üretildi. Disk şeklinde üretilen örneklerin üzerine seramik (r=6mm, h=4mm) pişirildi. 1 haftalık hızlandırılmış yaşlandırma işlemi sonrası 1,5 ve 3,0 T MRG cihazında 30 dakika süre ile beyin MRG sekansları uygulanarak instron test cihazında makaslama bağlantı direnci test edildi. Çalışmada ayrıca dikdörtgen prizması şeklinde üretilen örneklere de aynı MRG prosedürü uygulanarak SAXS cihazı ile nano-kristaliografik yapıları, profilometre ile yüzey pürüzlülükleri ve Vickers mikrosertlik cihazı ile sertlik ölçümleri yapıldı. MRG uygulamaları sonucunda yüzey pürüzlülüğünde CoCr_Dk - CoCr_Db (1,77-2,31 µm), CoCr_Da - CoCr_Db (1,95-2,31 µm) ve Ti_k – Ti_a (0,78-1,34 µm) grupları arasında artış görülmüştür (p0.05). Vickers mikrosertlik değerlerinde CoCr_Dk - CoCr_Db (438-334 HV1) ile CoCr_Da - CoCr_Db (459-334 HV1) grupları arasında azalma görülürken NiCr_k - NiCr_b (328-391 HV1) ile NiCr_a - NiCr_b (311-391 HV1) grupları arasında artış görülmüştür (p>0.05). Ancak CoCr_L, Ti ve Zr örnek grupları içerisinde anlamlı fark bulunmamıştır (p>0.05). CoCr_D örnek grupları için makaslama bağlanma direncinde CoCr_Dk (21,75 MPa) grubuna göre CoCr_Da (24,1 MPa) grubunda artış, CoCr_Db (19,47 MPa) grubunda azal-ma ve CoCr_Db (19,47 MPa) grubunda, CoCr_Da (24,1 MPa) grubuna göre azalma görülmüştür (p0.05). SAXS analizi ise materyal-lerin, manyetik alan ve non iyonize radyo dalgalarından etkilendiğini, bu etkilenimlerin de materyallerin sertlik, pürüzlülük ve seramikle bağlanma di-rençlerinde farklılıklara neden olduğunu göstermektedir. Sonuçlar, MRG uygulamalarının özellikle metal destekli sabit protetik restorasyonlarda metal-seramik bağlantısında görülen başarısızlık nedenle-rinden birisi olabileceğini göstermektedir.

Özet (Çeviri)

Effects of 1,5 and 3,0 T Magnetic Resonance Imaging (MRI) sys-tems on the characteristic properties of dental metal alloys and zirco-nium, and their ceramic adhesion. The aim of this study was to analyze the effects of non-ionizing radio frequency signals and magnetic field of MRI on the characteristic properties and framework-ceramic adhesion of the materials that are used in fixed partial dentures. For the study, Co-Cr, Ni-Cr, ZrO2 and Ti specimens were produced in the shape of disk (12mm diameter, 1mm thickness) and rectangular prism (4x2x2 mm) by using different fabrication methods. Ceramic was applied to the disk shaped samples (r=6mm, h=4mm). The veneered specimens sub-jected to ageing for a week, then they were rondomly divided into three groups (n=20). Later, 1st and 2nd groups were exposed to 1,5 and 3,0 T MRI brain secans for 30 minutes respectively while the 3rd group (control group) was not exposed to MRI. Shear bond strengths of these specimens were measured with a universal test machine. The same MRI procedure was ap-plied to the rectangular prism specimens. Nano-cristaliografic structures of these rectangular prism specimens were analyzed with Small Angle X-ray Scattering (SAXS), and their surface rougness and Vickers hardness were measured. The surface rougness of CoCr_Dk - CoCr_Db (1,77-2,31 µm), CoCr_Da - CoCr_Db (1,95-2,31 µm) ve Ti_k – Ti_a (0,78-1,34 µm) groups were increased after MRI exposure (p0.05). The Vickers hardness numbers of CoCr_Dk - CoCr_Db (438-334 HV1), CoCr_Da - CoCr_Db (459-334 HV1) groups were decreased, and NiCr_k - NiCr_b (328-391 HV1), NiCr_a - NiCr_b (311-391 HV1) groups were increased (p0.05). The shear bond strength of CoCr_Da (24,1 MPa) group was increased while CoCr_Db (19,47 MPa) group was decreased with regard to CoCr_Dk (21,75 MPa) group and also NiCr_a (18,16 MPa) was decreased while NiCr_b (28,03 MPa) was increased with regard to NiCr_k (21,29 MPa) group (p0.05). The SAXS analysis of the specimens indicated that the nano-cristaliografic structures of the materials were influenced by the magnetic field and non-ionizing radio frequency signals which causes changes on the hardness, roughness and metal-ceramic adhesion of the specimens. The results indicated that the MRI systems can be a reason for the failure of metal-ceramic adhesion in fixed partial dentures.

Benzer Tezler

  1. Tez No

    791166

    Prostat kanseri tanısında PI-RADS ve likert skorlama sistemlerinin karşılaştırılması ve radyolog tecrübesinin sistemlerin doğruluğuna olan katkısı

    The comparison of the pi-rads and likert scoring systems in the diagnosis of prostate cancer and the investigation of the contribution of radiologist expertise on the accuracy of these systems

    ALİ CAN TOPALOĞLU

    Tıpta Uzmanlık

    Türkçe

    Türkçe

    2022

    Radyoloji ve Nükleer TıpSağlık Bilimleri Üniversitesi

    Radyoloji Ana Bilim Dalı

    DOÇ. DR. GÖKHAN SÖKER

  2. Tez No

    637001

    Controlled release system including nanoparticles that can be used for hypothyroidism treatment

    Hipotiroidi tedavisinde kullanılabilecek nanopartikül içerikli kontrollü salım sistemi

    CEREN KUTLU KAYA

    Doktora

    İngilizce

    İngilizce

    2020

    Biyomühendislikİstanbul Teknik Üniversitesi

    Nanobilim ve Nanomühendislik Ana Bilim Dalı

    PROF. DR. FATMA NEŞE KÖK

  3. Tez No

    874473

    MEMS sensor platform for vital monitoring under mri and intraocular pressure measurement

    Yaşamsal işaretlerin ve göz içi basıncın ölçülmesine yönelik MEMS basınç ölçer platformunun geliştirilmesi

    PARVIZ ZOLFAGHARI

    Doktora

    İngilizce

    İngilizce

    2023

    Elektrik ve Elektronik Mühendisliğiİstanbul Teknik Üniversitesi

    Elektronik ve Haberleşme Mühendisliği Ana Bilim Dalı

    DOÇ. DR. ONUR FERHANOĞLU

  4. Tez No

    791252

    Normal popülasyonda miyokardiyal T1, T2 ve T2* değerlerinin yaş, cinsiyet ve kardiyak segmentlere göre analizi

    Analysis of myocardial T1, T2, and T2* values in normal population by age, gender, and cardiac segments

    ÇAĞRI ÖZCAN

    Tıpta Uzmanlık

    Türkçe

    Türkçe

    2023

    Radyoloji ve Nükleer TıpSağlık Bilimleri Üniversitesi

    Radyoloji Ana Bilim Dalı

    PROF. DR. HASAN YİĞİT

  5. Tez No

    453960

    Cyberknife synchrony® solunum takip sisteminin polimer jel dozimetre ile üç boyutlu performans analizi

    Three dimensional performance analysis of cyberknife synchrony® respiratory tracking system using polymer gel dosimeter

    MERYEM CANSU ŞAHİN

    Yüksek Lisans

    Türkçe

    Türkçe

    2017

    Fizik ve Fizik MühendisliğiHacettepe Üniversitesi

    Radyasyon Onkolojisi Ana Bilim Dalı

    DOÇ. DR. PERVİN HÜRMÜZ

Geri Dön