In vitro evaluation of fracture resistance of crown restorations fabricated from different hybrid ceramic materials
Farklı hibrit seramik materyalleri ile hazırlanan restorasyonların kırılma dirençlerinin in vitro olarak değerlendirilmesi
- Tez No: 596574
- Danışmanlar: Assoc. Prof. Dr. BUKET EVREN
- Tez Türü: Yüksek Lisans
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: CAD\CAM, Hibrit seramikler, kırılma direnci, Dental materyaller, Dental porselen, Dental restorasyon, Dental stres analizi, İn vitro, CAD\CAM, Hybrid ceramics, Fracture resistance, Dental materials, Dental porcelain, Dental restoration, Dental stress analysis, In vitro
- Yıl: 2019
- Dil: İngilizce
- Üniversite: Marmara Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Amaç: Bu çalışmanın amacı, CAD\CAM sisteminde farklı hibrit seramik malzemelerden üretilen kron restorasyonların kırılma direncini değerlendirmektir. Gereç ve Yöntemler: Çekilmiş 45 molar diş, her biri 15 örnek içeren, rastgele 3 gruba ayrıldı. Çıkarıler dişler, otopolimerize edici akrilik reçine bloklarına yerleştirildi. Tüm dişler standart diş kesim prosedürlerine göre chamfer bitiş çizgisile hazırlandı. CAD/CAM sistemi (CEREC Omnicam Sistemi, Salzburg, Österreich) ile dijital ölçüler alındi. Taramadan sonra, 45 diş 3 gruba ayrıldı. kron restorasyonları 3 farklı CAD / CAM bloğundan (IPS e.max CAD, Vita Enamic ve GC Cerasmart) üretildi. Restorasyonların simantasyonundan sonra kırılma direnci üniversal test cihazı (Shimadzu product, Kyoto 604-8511, Japan) ile ölçüldü. Veriler toplandıktan sonra sonuçlar istatistiksel olarak değerlendirildi. Bulgular: Sonuçların analizi tüm gruplar arasında istatistiksel olarak anlamlı fark gösterdi (P <0.05). CeraSmart grubu, E-max (2614.47 ± 578.79) ve VitaEnamic gruplarına (1687.90 ± 570.91) kıyasla en yüksek ortalama kırılma yükü ortalamasını (3135.74 ± 860.91) göstermiştir. Sonuçların analizi Cerasmart ve E-max gruplarının istatistiksel olarak benzer kırık yüklerine sahip olduklarını ve Vita grubundan daha yüksek olduğunu gösterdi. Sonuç: CAD \ CAM sistemiyle üretilen hibrit malzemeler mükemmel kırılma direnci gösterdi.
Özet (Çeviri)
Aim: Compared to conventional materials, polymer/ceramic hybrid composites have the potential to tailor the desirable properties that individual component can offer. The aim of this study is to evaluate the fracture resistance of crown restorations fabricated from different hybrid ceramic materials in CAD\CAM system. Materials and Methods: 45 extracted molar teeth were divided into 3 groups randomly, each group containing 15 specimens. All teeth were placed in autopolymerizing acrylic resin blocks and they were prepared according to standard tooth preparation procedures with a chamfer finish line. Digital impressions were taken with CAD/CAM system (CEREC Omnicam System, Salzburg, Österreich). After scanning crown restorations were fabricated from 3 different CAD/CAM blocks (IPS e.max CAD, Vita Enamic, and GC Cerasmart). After cementation of the restorations, fracture resistance was measured with a universal testing machine (Shimadzu product, Kyoto 604-8511, Japan). After collecting the data, the results were evaluated statistically. Results: Analysis of the results showed statistically significant difference between all the groups (P<0.05). CeraSmart group exhibited the highest mean fracture load mean (3135.74±860.91) compared to E-max (2614.47±578.79) and VitaEnamic groups (1687.90±570.91). Analysis of the results showed that Cerasmart and E-max groups had statistically similar fracture loads and higher than Vita group. Conclusion: Hybrid materials fabricated with CAD\CAM system showed excellent fracture resistance.
Benzer Tezler
- Farklı yöntemlerle üretilen hibrit seramik blokların kanal tedavili dişlerin restorasyonunda kırılma dayanımı üzerine etkisinin değerlendirilmesi: İn vitro çalışma
Evaluation of the effect of hybrid ceramic blocks produced by different methods on the fracture resistance of root canal–treated teeth restorations: An in vitro study
EZGİCAN BEKTAŞ
Diş Hekimliği Uzmanlık
Türkçe
2026
Diş HekimliğiEge ÜniversitesiEndodonti Ana Bilim Dalı
DOÇ. DR. BURCU ŞEREFOĞLU POLAT
- Üç farklı teknikle üretilen posterior adeziv restorasyonların mekanik özelliklerinin İn-vitro incelenmesi
In-vitro evaluation of the mechanical properties of posterior adhesive restorations fabricated using three different techniques
GÖZDE ACAR
Diş Hekimliği Uzmanlık
Türkçe
2025
Diş HekimliğiEge ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. CEM PEŞKERSOY
- CAD/CAM ve preslenebilir tüm seramik sistemleri ile yapılan kronların marjinal ve internal uyumlarının in vivo ve in vitro karşılaştırmalı olarak araştırılması
In vivo and ın vitro evaluation of marginal and ınternal fit of all-ceramic crowns fabricated with cad/cam and pressable systems
ASLI AKIN
Doktora
Türkçe
2011
Diş HekimliğiEge ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. SUNA TOKSAVUL
- Farklı endodontik post-kor sistemler ile restore edilmiş dişlerde kök kırılma dayanımlarının İn Vitro olarak değerlendirilmesi
Evaluation of root fracture strength in teeth restored with different endodontic post-core systems:In Vitro study.
ÖMER FARUK YENİLMEZ
Doktora
Türkçe
2025
Diş Hekimliğiİstanbul ÜniversitesiEndodonti Ana Bilim Dalı
DR. ÖĞR. ÜYESİ TURGUT YAĞMUR YALÇIN
- Eklemeli ve eksiltmeli yöntemlerle üretilen geçici restorasyonların internal-marjinal uyumlarının ve kırılma dayanımlarının karşılaştırılması
Comparison of internal and marginal fit and fracture resistance of provisional restorations fabricated using additive and subtractive methods
OĞUZHAN KAYA
Diş Hekimliği Uzmanlık
Türkçe
2026
Diş HekimliğiFırat ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. EYYÜP ALTINTAŞ