Titanyum alaşımlarında plastik şekil verme sonrası lazer kaynak işleminin mekanik ve boyutsal davranışlar üzerine etkisi

Mechanical and dimensional effect of laser welding process performed before and after plastic forming on titanium alloys

PDF İndir

  1. Tez No: 599918
  2. Yazar: SAMİ SEVİNÇ
  3. Danışmanlar: DOÇ. DR. RUKİYE ERTAN
  4. Tez Türü: Yüksek Lisans
  5. Konular: Makine Mühendisliği, Metalurji Mühendisliği, Mechanical Engineering, Metallurgical Engineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2019
  8. Dil: Türkçe
  9. Üniversite: Bursa Uludağ Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Otomotiv Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 85

Özet

Bu çalışmada; %98,9 saflıktaki Titanyum Grade 2 ile alaşımlı Titanyum Grade 5 (Ti-6Al-4V) titanyum sac malzemelere (25x33x1 mm) oda sıcaklığında, 500 º C ve 850 º C de olmak üzere farklı sıcaklıklarda plastik şekil verilmiştir. Plastik şekil verme işlemi saclar iki farklı gruba ayrılarak yapılmıştır; Birinci grup saclar önce giyotin ile ortadan ikiye ayrılmış, daha sonra Nd: YAG lazer ile kesilen yerlerden kaynatılmış, sonrasında fırında ısıtılmış ve son olarak da plastik şekil verilmiştir. İkinci grup saclar ise, önce fırında ısıtılmış, sonra plastik şekil verilmiş, daha sonra giyotin ile ortadan ikiye ayrılmış ve son olarak Nd: YAG lazer ile kesilen yerlerden kaynatılmıştır. Oda sıcaklığında plastik şekil verilecek parçalar ısıtma işlemine tabi tutulmamıştır. Kaynak işlemlerinde aynı tip parçalar birbiriyle kaynatıldığı gibi farklı Grade sahip olan malzemelerde birbiriyle kaynatılmıştır. Yapılan bu işlemler sonucunda farklı sıcaklıklarda ısıtılmış, kaynak ile birleştirilmiş Titanyum Grade 2 ve Titanyum Grade 5 parçalar elde edilmiştir. Kaynak işlemi, hazırlanan iş parçaların yarısına plastik şekil verme öncesi, diğer yarısına ise plastik şekil verme sonrası yapılmıştır. Tüm iş Parçaları 3d tarama yöntemi ile taranmış ve cad ortamına aktarılarak nominal parçaya göre meydana gelen atıklığı ölçülmüş ve karşılaştırmalar yapılmıştır. İş parçaları üzerinden ASTM E8 e göre numuneler hazırlanıp çekme testleri yapılmış ve sonuçları kıyaslanmıştır.

Özet (Çeviri)

In this study; 98.9% purity of Grade 2 and alloyed Grade 5 (Ti-6Al-4V) titanium sheet materials (25x33x1 mm) were plastically formed at different temperatures like 25 º C, 500 º C and 850 º C. Plastic forming process was made by dividing the sheets into two different groups; The first group of sheets were firstly cut into two parts by guillotine, as the second step they were joined by laser welding method, then heat treated and finally plastic shaped. The second group of sheets were first heat-treated, then plastically shaped, then cut into two parts with the guillotine and finally laser welded. Heat treatment wasn't applied to the parts which would be plastically shaped at room temperature. In welding processes, the same type of parts are welded to each other as well as to different grade materials. As a result of these processes, parts of Grade 2 and Grade 5 were heat treated and welded together. One-Half these parts were welded before plastic forming and the other half parts are welded after plastic forming. To see the spring back rate, All parts were scanned by 3d scanning method and transferred to CAD environment in order to measure deviation from the nominal part and also to compare them to each other. Additionally, all samples complying with ASTM E8 standard have been prepared and tensile tests were performed. Again the results have been compared to each other. As a conclusion of all these analyzes, we have questioned if welding of heat treated titanium materials should be done before plastic forming or after.

Benzer Tezler

  1. Tez No

    830385

    Dalma elektro erozyon yöntemi ile ticari saflıkta titanyum alaşımında mikro yüzey desenlerinin elde edilmesi ve yüzey özelliklerinin incelenmesi

    Obtaining of micro surface patterns and investigation of surface properties in Cp-Ti alloy by electrical discharge machining method

    ALPEREN KÜRŞAT BALTA

    Yüksek Lisans

    Türkçe

    Türkçe

    2023

    Makine MühendisliğiKocaeli Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    DOÇ. DR. EGEMEN AVCU

  2. Tez No

    596956

    Bimetal kompozitlerin metal talaşlarıyla üretimi ve karakterizasyonu

    Production and characterization of bimetal composites by metal shavings

    RIDVAN GECÜ

    Doktora

    Türkçe

    Türkçe

    2019

    Metalurji MühendisliğiYıldız Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. AHMET KARAASLAN

  3. Tez No

    75153

    Bilgisayar yardımıyla süper alaşım malzeme verileri ve tasarım kriterleri kütüphanesi oluşturulması

    Başlık çevirisi yok

    M.ÇAĞLAYAN TAŞÇIOĞLU

    Yüksek Lisans

    Türkçe

    Türkçe

    1998

    Makine Mühendisliğiİstanbul Teknik Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    DOÇ. DR. MEHMET DEMİRKOL

  4. Tez No

    199072

    Thermomechnical characterization of Ti-rich tini shape memory alloys

    Ti zengin tini şekil bellekli alaşımların ısıl mekanik karakterizasyonu

    FATİH YAŞAR

    Yüksek Lisans

    İngilizce

    İngilizce

    2006

    Metalurji MühendisliğiOrta Doğu Teknik Üniversitesi

    Metalurji Mühendisliği Ana Bilim Dalı

    PROF. DR. ŞAKİR BOR

  5. Tez No

    721937

    Investigating the effect of low heating-cooling rate and the thermomechanical treatments on the shape memory behavior of NiTiHf alloys

    Yavaş ısıtma-soğutma hızının ve termomekanik işlemlerin NiTiHf alaşımlarının şekil hafıza davranışları üzerine etkisinin incelenmesi

    OĞULCAN AKGÜL

    Yüksek Lisans

    İngilizce

    İngilizce

    2022

    Makine MühendisliğiHacettepe Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    PROF. DR. BENAT KOÇKAR

Geri Dön