Kitosan nanopartiküllerinin kalsiyum silikat içerikli kök kanal dolgu materyallerinin kök kanalına bağlanma dayanımı ve smear tabakasının uzaklaştırılması üzerine etkisinin incelenmesi
Evaluation of the effect of chitosan nanoparticles on the push-OUT bond strength of calcium-silicate based cements and the removal of smear layer
- Tez No: 661655
- Danışmanlar: PROF. DR. HESNA SAZAK ÖVEÇOĞLU
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Kitosan, nanopartiküller, smear tabakası, push-out bağlanma dayanımı, kalsiyum silikat simanlar, Chitosan, nanoparticles, smear layer, push-out bond strength, calcium silicate cements
- Yıl: 2020
- Dil: Türkçe
- Üniversite: Marmara Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Endodonti Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 88
Özet
Amaç: Bu çalışmanın amacı, kitosan nanopartiküllerinin ve %17 EDTA'nın iki farklı kalsiyum silikat içeriklisimanın (MTA Plus ve Biodentine) kök kanalına“push-out”bağlanma dayanımı ve smear tabakasının uzaklaştırılması üzerine etkisinin incelenmesidir. Gereç ve Yöntem: Çalışmamızda 46 adet tek köklü üst insan kanin dişi kullanılmıştır. Dişlerin kuronları uzaklaştırıldıktan sonra, kök kanalları ProTaper Next döner eğeleri ile X3'e kadar genişletilmiştir. 40 adet dişten 1 mm kalınlığında olmak üzere 2şer adet, toplam 80 adet kesit alınmıştır. Daha sonra alınan kesitler, uygulanan final şelasyon solüsyonu ve silikat esaslı simana göre 4 farklı gruba ayrılmıştır(n=20): Grup Ⅰ: kitosan nanopartikülleri-MTA, Grup Ⅱ: kitosan nanopartikülleri-Biodentine, Grup Ⅲ: EDTA-MTA ve Grup Ⅳ: EDTA-Biodentine olacak şekilde gruplandırılmıştır. Push-out bağlanma dayanımı değerleri universal test cihazı kullanılarak ölçümlenmiştir. Smear tabakasının uzaklaştırılmasını değerlendirmek için, örneklerin yıkama işleminden sonra SEM analizi yapılmıştır. Bulgular: Elde edilen bulgulara göre; kitosan nanopartikülleri grubunun ortalama bağlanma dayanımı değeri EDTA grubuna göre daha yüksekti, ancak iki grup arasında istatistiksel olarak anlamlı bir fark bulunmamıştır (p = 0,132> 0,05). MTA ile Biodentine grupları arasında istatistiksel olarak anlamlı bir fark bulunmuştur (p 0,05). Sonuçlar: Kitosan nanopartiküllerinin smear tabakasının uzaklaştırılmasında alternatif bir şelasyon ajanı olarak kullanılmasını önermekteyiz.
Özet (Çeviri)
Aim: The aim of this study was to evaluate the effect of chitosan nanoparticles and 17% EDTA on the push-out bond strength of two different calcium silicate based cements (MTA Plus ve Biodentine) and the removal of smear layer. Materials and Methods: A total of 46 single-rooted human maxillary canines were decoronated and shaped with ProTaper Next rotary files up to size X3. 40 tooth were sectioned transversally into two sections of 1 mm thick. Following this, 80 slices were randomly divided into 4 groups based on the final irrigant and the calcium silicate cement used (n = 20): Group Ⅰ: chitosan nanoparticles-MTA, Group Ⅱ: chitosan nanoparticlesBiodentine, Group Ⅲ: EDTA-MTA, Group Ⅳ: EDTA-Biodentine. The push-out bond strengths were measured using a Universal testing machine after 7 days of storage. The SEM analysis was done for the remaining 6 teeth after irrigation protocol to evaluate the smear layer removal. Results: According to the bond strength results, the mean value for chitosan nanoparticles when compared to EDTA was higher, but there was no statistically significant difference between the two groups (p=0,132 > 0,05). Statistically significant differences were observed between Biodentine and MTA (p 0.05). Conclusion: The use of chitosan nanoparticles as an alternative chelating agent for smear layer removal seems promising.
Benzer Tezler
- Kitosan-sodyum aljinat biyopolimerik nanopartiküllerinin hazırlanması ve nar kabuklarından ekstrakte edilen antioksidanların enkapsülasyonu
Preparation of chitosan-sodium alginate biopolymeric nanoparticles and encapsulation of antioxidants extracted from pomegranate peels
AYLİN KAZOLUK
Yüksek Lisans
Türkçe
2019
Bilim ve Teknolojiİzmir Katip Çelebi ÜniversitesiNanobilim ve Nanoteknoloji Ana Bilim Dalı
DR. ÖĞR. ÜYESİ AHMET AYKAÇ
- Formulation and in vitro-in vivo evaluation of rosuvastatin calcium incorporated cyclodextrin, solid lipid and chitosan based drug delivery systems
Rosuvastatin kalsiyum içeren siklodekstrin, katı lipit ve kitosan bazlı taşıyıcı sistemlerin hazırlanması ve in vitro-in vivo değerlendirilmesi
FAWAZ NASSER SHEKH AL-HEIBSHY
Doktora
İngilizce
2017
Eczacılık ve FarmakolojiAnadolu ÜniversitesiFarmasötik Teknoloji Ana Bilim Dalı
PROF. DR. MÜZEYYEN DEMİREL
YRD. DOÇ. DR. EBRU BAŞARAN
- Kanser tedavisine yönelik antisens oligonükleotid yüklü polimerik nanopartikül tasarımı ve İn vitro karakterizasyonu
Design and In vitro characterization of antisense oligonucleotide loaded polymeric nanoparticles for cancer therapy
PEZHMAN HOSSEİNİAN AHANGARNEZHAD
Yüksek Lisans
Türkçe
2012
GenetikHacettepe ÜniversitesiNanoteknoloji ve Nanotıp Ana Bilim Dalı
DOÇ. DR. EYLEM GÜVEN ÖZTÜRK
- Manyetik kitosan nanopartiküllerinin hazırlanması, ilaç yüklenmesi ve kemopterapi ajanı olarak kullanılabilirliğinin araştırılması
Preparation of magnetic chitosan nanoparticles, loadi?ng pharmaceutical agent and research as a chemotherapy agent
MERVE VARAN
- Satureja hortensis L. uçucu yağı yüklenmiş kitosan nanopartiküllerinin ve kitosan filmlerin üretimi ve karakterizasyonu
Production and characterization of chitosan nanopartcles and chitosan films loaded with Satureja hortensis essential oil
GİZEM CANSU FEYZİOĞLU
Yüksek Lisans
İngilizce
2016
Gıda MühendisliğiYıldız Teknik ÜniversitesiGıda Mühendisliği Ana Bilim Dalı
YRD. DOÇ. DR. FATİH TÖRNÜK