Farklı özellikteki P355GH ve 316L çeliklerinin TIG kaynak yöntemi ile birleştirilmesinin mekanik ve mikroyapısal özellikler bakımından incelenmesi

Investigation of the joining dissimilar P355GH and 316L steels with different properties by TIG welding method in terms of mechanical and microstructural properties

PDF İndir

  1. Tez No: 758537
  2. Yazar: BETÜL NUR GÜZEY
  3. Danışmanlar: DR. ÖĞR. ÜYESİ GÜRKAN İRSEL
  4. Tez Türü: Yüksek Lisans
  5. Konular: Makine Mühendisliği, Metalurji Mühendisliği, Mechanical Engineering, Metallurgical Engineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2022
  8. Dil: Türkçe
  9. Üniversite: Trakya Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Makine Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Makine Mühendisliği Bilim Dalı
  13. Sayfa Sayısı: 88

Özet

Bu tez çalışmasında, yüksek ısı ve basınca dayanıklı P355GH ve östenitik paslanmaz 316L çeliklerinin Tungsten inert gaz (TIG) kaynak yöntemi ile birleştirilmesi mikroyapı, mekanik özellikler ve birleşim verimliliği bakımından araştırıldı. İki farklı metalin kaynak ile birleşimi için test plakaları hazırlandı ve kaynaklandı. Kaynaklanan plakalardan test numuneleri tel erozyon yöntemi ile kesildi. Kaynak bölgesi, ısı tesiri altında kalan bölgeler ve esas metaller için kapsamlı testler gerçekleştirildi. Metalografik karakterizasyon araştırmasında; optik mikroskop (OM), alan emisyonlu taramalı elektron mikroskobu (FESEM), enerji dağılımlı X-ışını spektroskopisi (EDX/EDS), X-ray difraksiyonu (XRD) analizleri gerçekleştirildi. Kaynaklı birleşim ve birleştirilen malzemelerin mekanik özelliklerini tespit etmek için Vickers mikrosertlik, eğme, Charpy V-Notch darbe, çekme testleri gerçekleştirildi. Optik incelemede P355GH ana metalin ortalama tane boyutu 5.13 ± 1 µm, 316L ana metalin ortalama tane boyutu ise 16.33 ± 5 µm olarak ölçülmüştür. XRD analizi sonucunda kaynak bölgesinin mikroyapısında delta ferrit fazı tespit edilmiştir. Vickers mikrosertlik değerleri, en yüksek kaynak merkezinde 268 ± 15 HV tespit edildi. 316L ana metalde 217.8 ± 12 HV, P355GH ana metaline ait sertlik değeri ise 195.7 ± 11 HV olarak ölçülmüştür. Çekme testinde, enine kaynak birleşiminde gözlemlenen en yüksek çekme dayanımı 593.92 ± 06 MPa değerindedir ve 316L bölgesinden kopma gerçekleşmiştir. Boyuna kaynak birleşiminde ise en yüksek çekme dayanımı 584.85 ± 07 MPa'dır. 316L çekme dayanımı 595.90 ± 08 MPa olarak ölçülürken, P355GH çekme dayanımı 601.49 ± 05 MPa olarak ölçülmüştür. Eğme testinde, eğme kuvvetleri 316L için 30.006 ± 8 kN P355GH için 36.324 ± 12 kN olarak tespit edildi. Enine ve boyuna kaynaklı numunelerde ise sırasıyla eğme kuvvetleri 34.331 ± 10 kN ve ise 32.966 ± 11 kN olarak ölçüldü. TIG kaynağı 316L ve P355GH metallerinin birleşiminde tokluk, yüksek plastik şekil değiştirme kabiliyeti, %101.10 oranında yüksek birleşim verimliliği gibi üstün özellikler gösterdi.

Özet (Çeviri)

This thesis investigates the joining of high temperature and pressure resistant P355GH and austenitic stainless 316L steels by Tungsten inert gas (TIG) welding method in terms of microstructure, mechanical properties, and joint efficiency. Test plates were prepared and welded for the joining of two different metals by welding. Test specimens from the welded plates were cut by wire electrical discharge machining. Extensive tests were carried out for the weld zone, heat affected zones and base metals. In metallographic characterization research, optical microscope (OM), field emission scanning electron microscope (FESEM), energy dispersive X-ray spectroscopy (EDX/EDS), X-ray diffraction (XRD) analyzes were performed. Vickers microhardness, bending, Charpy V-Notch impact, tensile tests were performed to determine the mechanical properties of the welded joint and the joined materials. In the optical examination, the average grain size of the P355GH base metal was 5.13 ± 1 µm, and the mean grain size of the 316L base metal was 16.33 ± 5 µm. As a result of XRD analysis, delta ferrite phase was determined in the microstructure of the source region. Vickers microhardness values were determined as 268 ± 15 HV at the highest weld center. The hardness value of 316L base metal was 217.8 ± 12 HV, and the hardness value of P355GH base metal was measured as 195.7 ± 11 HV. In the tensile test, the highest tensile strength observed in the transverse weld joint was 593.96 ± 06 MPa and fracture occurred in the 316L region. In the longitudinal weld joint, the highest tensile strength is 584.85 ± 07 MPa. The tensile strength of 316L was measured as 595.90 ± 08 MPa, while the tensile strength of P355GH was measured as 601.49 ± 05 MPa. In the bending test, the bending forces were determined as 30.006 ± 8 kN for the 316L and 36.324 ± 12 kN for the P355GH. Bending forces were measured as 34.331 ± 10 kN and 32.966 ± 11 kN for transverse and longitudinal welded specimens, respectively. TIG weld metal showed superior properties such as toughness, high plastic deformation ability, high joint efficiency of 101.10% in the combination of 316L and P355GH metals.

Benzer Tezler

  1. Tez No

    624676

    Farklı özellikteki nikel-titanyum kök kanal eğelerinin kök kanalında mikro çatlak oluşturma etkisinin in vitro incelenmesi

    In vitro evaluation of the effect of different nickel titanium root canal instruments on microcrack induction

    BERTAN KESİM

    Diş Hekimliği Uzmanlık

    Türkçe

    Türkçe

    2015

    Diş HekimliğiErciyes Üniversitesi

    Endodonti Ana Bilim Dalı

    PROF. DR. BURAK SAĞSEN

  2. Tez No

    890369

    Farklı özellikteki sularda (Tatlı su ve deniz suyu) yetiştirilen gökkuşağı alabalığı/Türk somonu (Oncorhynchus mykiss) ile atlantik somonunun (Salmo salar) kalite ve besin değeri yönünden karşılaştırılması

    Comparison of rainbow trout/Turkish salmon (Oncorhynchus mykiss) and atlantic salmon (Salmo salar) growed in waters with different characteristics (Fresh water and sea water) in terms of quality and nutritional value

    DİLA BEŞEN

    Yüksek Lisans

    Türkçe

    Türkçe

    2024

    Gıda MühendisliğiAdana Alparslan Türkeş Bilim Ve Teknoloji Üniversitesi

    Gıda Mühendisliği Ana Bilim Dalı

    DOÇ. DR. MURAT REİS AKKAYA

  3. Tez No

    95867

    Correlation between differentproperties of batıçim limestone quarries

    Farklı özellikteki batıçim kireçtaşları arasındaki korelasyon

    HAYYER YALNIZ

    Yüksek Lisans

    İngilizce

    İngilizce

    2000

    Maden Mühendisliği ve MadencilikDokuz Eylül Üniversitesi

    Maden Mühendisliği Ana Bilim Dalı

    DOÇ. DR. TURGAY ONARGAN

  4. Tez No

    434049

    Farklı özellikteki duvar akışlı dizel partikül filtrelerinin basınç kaybına etkilerinin incelenmesi

    Investigation of different types of wall flow diesel particulate filters' effects on pressure drop

    YUNUS ÖZKAN

    Yüksek Lisans

    Türkçe

    Türkçe

    2016

    Makine MühendisliğiSakarya Üniversitesi

    Otomotiv Mühendisliği Ana Bilim Dalı

    PROF. DR. İBRAHİM ÖZSERT

  5. Tez No

    701629

    Farklı özellikteki mikrofonlardan ve akıllı telefonlardan elde edilen parametrelerin sağlıklı ve disfonik sesi ayırt etmedeki tanısal performanslarının karşılaştırılması

    Diagnostic performances of parameters derived from different microphones and smartphones in discrimination between healthy and dysphonic voice

    MUHAMMET ENES CEYLAN

    Yüksek Lisans

    Türkçe

    Türkçe

    2021

    Kulak Burun ve BoğazÜsküdar Üniversitesi

    Dil ve Konuşma Terapistliği Ana Bilim Dalı

    DR. ÖĞR. ÜYESİ MEHMET EMRAH CANGİ

Geri Dön