Farklı yüzey işlemlerinin dört farklı monolitik CAD/CAM materyallerinin aşınma miktarına etkisinin in vitro olarak değerlendirilmesi

In vitro evaluation of the effect of different surface treatments on the wear amount of four different monolithic CAD/CAM materials

  1. Tez No: 844923
  2. Yazar: ZEYNEP ARIKAN
  3. Danışmanlar: PROF. DR. YASEMİN ÖZKAN
  4. Tez Türü: Doktora
  5. Konular: Diş Hekimliği, Dentistry
  6. Anahtar Kelimeler: dayanım-gradyanlı monolitik zirkonya, zirkonya ile güçlendirilmiş lityum silikat, lityum disilikat, aşınma, strength-gradient monolithic zirconia, zirconia-reinforced lithium silicate, lithium disilicate, wear
  7. Yıl: 2023
  8. Dil: Türkçe
  9. Üniversite: Marmara Üniversitesi
  10. Enstitü: Sağlık Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 135

Özet

Amaç: Bu çalışmanın amacı, cilalanmış ve glazelenmiş olmak üzere iki farklı yüzey bitim tekniğine göre hazırlanan hibrit nanoseramik, zirkonya ile güçlendirilmiş lityum silikat, lityum disilikat ve dayanım gradyanlı monolitik zirkonya olmak üzere dört farklı monolitik CAD/CAM materyallerinin 1 yıllık çiğneme döngüsündeki aşınma miktarlarını değerlendirmektir. Gereç ve Yöntem: Tüm materyallerden örnekler 7x7x3 mm boyutlarında olacak şekilde disk formunda hazırlandı ve her materyal mekanik cilalanmış ve glazelenmiş olmak üzere iki alt gruba (n=12) ayrıldı. Aşınma miktarını belirlemek için örnekler lazer tarayıcı cihazı (SD Mechatronik Lazer Tarayıcı LAS-20, Münih, Almanya) ile tarandı. Örneklere, dual akslı bir çiğneme simülatöründe (SD Mechatronik Çiğneme Simülatörü CS-4.2, Münih, Almanya) 1 yıllık klinik kullanıma eş değer olan 240 000 döngü uygulandı. Çiğneme simülatöründe dinamik yükleme yapıldıktan sonra örnekler lazer tarayıcı ile tekrar tarandı. Elde edilen veriler Geomagic Control (3D Systems Inc., Rock Hill, ABD) programına aktarılarak aşınma ölçümleri hesaplandı. Verilerin analizinde Kruskal Wallis testi kullanıldı. Bulgular: İncelenen materyallerin tümünün aşınma miktarları arasında istatistiksel olarak anlamlı farklılık tespit edildi. Dayanım gradlı monolitik zirkonya, lityum disilikat ve hibrit nanoseramik materyallerinin cilalanmış ve glazelenmiş örnekleri arasında fark bulunamazken, glazelenmiş zirkonya ile güçlendirilmiş lityum silikatın aşınma miktarı cilalanmış zirkonya ile güçlendirilmiş lityum silikatınkinden düşük tespit edildi. Sonuç: Materyallerin aşınma dirençleri, mikro-yapılarından ve yüzey bitim özelliklerinden etkilenmektedir.

Özet (Çeviri)

Purpose: The aim of this study is to evaluate the wear amounts of four different monolithic CAD/CAM materials, that are prepared in two different surface finishing techniques after one year of dynamic loading. Material and Method: Samples from all materials were prepared in disk form with dimensions of 7x7x3 mm, and each material was divided into two subgroups (n = 12) as mechanically polished and glazed. The samples were scanned with a laser scanner device (SD Mechatronik Laser Scanner LAS-20, Munich, Germany). Samples were subjected to 240 000 cycles, in a dual-axle chewing simulator (SD Mechatronik Chewing Simulator CS-4.2, Munich, Germany). After dynamic loading, the samples were scanned again. The obtained data were transferred to the Geomagic Control (3D Systems Inc., Rock Hill, USA) program and wear measurements were calculated. Results: A statistically significant difference was detected between the wear amounts of all examined materials. While no difference was found between polished and glazed samples of strength graded monolithic zirconia, lithium disilicate and hybrid nanoceramic materials, the wear rate of lithium silicate reinforced with glazed zirconia was determined to be lower than that of lithium silicate reinforced with polished zirconia. Conclusion: The wear resistance of materials is affected by their microstructure and surface finish properties.

Benzer Tezler

  1. Titanyum altyapı üzerinde kullanılan seramik abutmentların bağlantısına farklı universal adeziv sistemlerin etkisi

    The effect of different universal adhesive systems on the bonding of ceramic abutments and titanium bases

    HÜSNİYE YILDIRIM

    Diş Hekimliği Uzmanlık

    Türkçe

    Türkçe

    2020

    Diş HekimliğiOrdu Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    DR. ÖĞR. ÜYESİ AYÇA TULGA

  2. Monolitik zirkonya yüzeylerde farklı bitirme işlemlerinin fırçalama abrazyonuna dayanımının değerlendirilmesi

    Evaluation of the resistance to brushing abrasion of different polishing methods on monolithic zirconia surfaces

    ÖMER BAYAR

    Doktora

    Türkçe

    Türkçe

    2023

    Diş HekimliğiBaşkent Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    DOÇ. DR. ÖZLEM ORMAN

  3. Farklı yüzey işlemlerinin ve yapay yaşlandırmanın y-tzp zirkonya seramiklerin faz dönüşümüne ve eğilme dayanımına etkisi

    Effect of different surface treatments and artificial aging on the phase transformation and flexural strength of y-tzp zirconia ceramics

    YENER OKUTAN

    Doktora

    Türkçe

    Türkçe

    2015

    Diş HekimliğiSelçuk Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    DOÇ. DR. MÜNİR TOLGA YÜCEL

  4. Zirkon yüzeyler ile seramik braketler arasındaki kopma dirençlerine farklı yüzey pürüzlendirme yöntemlerinin etkisi

    Comparison of shear bond strength of ceramic brackets to zirconia surfaces using different surface treatment methods

    NURCAN KUTUCU DÜLGER

    Doktora

    Türkçe

    Türkçe

    2023

    Diş HekimliğiEge Üniversitesi

    Ortodonti Ana Bilim Dalı

    PROF. DR. AYNUR ARAS

  5. Sol-jel yöntemi uygulanarak ZrO2 ile yüzey modifikasyonu yapılmış LiMn2o4 yapısının sentezlenmesi ve katot aktif malzemesi olarak incelenmesi

    SOL-JEL YÖNTEMİ UYGULANARAK ZrO2 İLE YÜZEY MODİFİKASYONU YAPILMIŞ LiMn2O4 YAPISININ SENTEZLENMESİ VE KATOT AKTİF MALZEMESİ OLARAK İNCELENMESİ

    MEHMET EMRE ÇETİNTAŞOĞLU

    Yüksek Lisans

    Türkçe

    Türkçe

    2016

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    DOÇ. DR. ÖZGÜL KELEŞ