Farklı fırınlama protokollerinin zirkonya ile güçlendirilmiş lityum silikat cam seramiklerin kırılma dayanımına ve optik özelliklerine etkisi
Effects of different firing protocols on the flexural strength and optical properties of zirconia-reinforced lithium silicate glass ceramics
- Tez No: 937462
- Danışmanlar: PROF. DR. GÖKHAN AKGÜNGÖR
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: CAD/CAM, tek seans, zirkonya güçlendirilmiş lityum silikat cam seramikler, sinterleme, lityum disilikat, CAD/CAM, chair-side, zirconia-reinforced lithium silicate glass ceramics, sintering, lithium disilicate
- Yıl: 2024
- Dil: Türkçe
- Üniversite: İstanbul Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Protetik Diş Tedavisi Bilim Dalı
- Sayfa Sayısı: Belirtilmemiş.
Özet
Günümüz diş hekimliğinde CAD-CAM sistemlerinde yaşanan teknolojik gelişmeler tek seansta hasta başında üretilen restorasyonların kullanımında artışa neden olmuştur. Bu amaçla geliştirilen birçok tam seramik materyalden biri de lityum disilikat cam seramik bloklar ve bu materyalin yüzde 10'luk zirkonya ile güçlendirilmiş hali ZLS cam seramik bloklardır. Çalışmamızda; tam sinterize ve yarı sinterize olmak üzere iki çeşit ZLS blok ve bunlara ek olarak LS bloklar kullanılmıştır. Tam sinterize ZLS bloklar farklı fırınlama ve bitirme prosedürleri uygulanarak hazırlanmış, yarı sinterize ZLS ve LS bloklar ise üretici talimatlarına uygun şekilde hazırlanmıştır. Tüm örnek grupları önce bir spektrofotometre kullanılarak ışık geçirgenliği değerleri bakımından optik olarak daha sonrasında ise universal bir test cihazında kırma testi uygulanarak mekanik dayanım bakımından karşılaştırılmıştır. Verilerin istatistiksel analizi için; Shaphiro Wilk, ANOVA ve LSD testleri uygulanmıştır. p<0,05 olması durumunda farklılıklar istatistiksel olarak anlamlı kabul edilmiştir. Tam sinterize ZLS blok örnek grupları kendi aralarında karşılaştırıldığında fırınlanan ve fırınlanmayan örnekler arasında mekanik açıdan istatistiksel olarak anlamlı bir farklılık görüldüğü gibi, LS bloklar ve hem yarı hem tam sinterize ZLS bloklar arasında da anlamlı bir fark tespit edilmiştir. (p<0,05) Ayrıca ışık geçirgenliği bakımından, yarı sinterize ZLS blokların diğer örnek gruplarından anlamlı şekilde daha düşük ortalama değer gösterdiği görülmüştür. (p<0,05) Çalışmanın sonuçları doğrultusunda, materyale zirkonya ilave edilmesinin optik özellikleri etkileyen bir durum olmadığı ancak mekanik dayanım konusunda olumlu bir etki yarattığı görülmüştür. Ayrıca tam sinterize ZLS bloklarda ise üretici talimatlarına göre sadece mekanik cila yaparak restorasyonun tamamlandığı restorasyonların, fırınlama uygulanan restorasyonlara göre daha düşük mekanik dayanım göstermiştir.
Özet (Çeviri)
In our study, two types of ZLS blocks that are fully sintered and partially sintered, as well as LS blocks, were used. The fully sintered ZLS blocks were prepared by applying different firing and finishing procedures, while the partially sintered ZLS and the LS blocks were prepared according to the manufacturer's instructions. All sample groups were first compared in terms of optical properties by measuring their light transmittance values using a spectrophotometer, and then in terms of mechanical strength through fracture testing using a universal testing machine. For the statistical analysis of the data, Shapiro-Wilk, ANOVA, and LSD tests were applied. Differences were considered statistically significant when p<0.05. When the fully sintered ZLS block sample groups were compared among themselves, a statistically significant difference in mechanical strength was observed between the fired and unfired samples, and a significant difference was also found between the LS blocks and both partially and fully sintered ZLS blocks (p<0.05). Additionally, in terms of light transmittance, it was observed that the partially sintered ZLS blocks had significantly lower mean values compared to the other sample groups (p<0.05). Based on the results of the study, it was found that the addition of zirconia to the material did not affect optical properties but had a positive impact on mechanical strength. Furthermore, it was revealed that restorations completed with only mechanical polishing according to the manufacturer's instructions in fully sintered ZLS blocks, showed lower mechanical strength compared to those subjected to firing.
Benzer Tezler
- Monolitik zirkonya restorasyonlarının tekrarlayan fırınlamaları ile renk, yüzey özelliği ve faz değişiminin incelenmesi
The investigation of color, surface properties, and phase transformation in monolithic zirconia restorations after repeated firings
HÜSEYİN ERKAN KARADAĞ
- Çoklu dişeti çekilme defektlerinde titanyum ile hazırlanan trombositten zengin fibrin ve bağ dokusu grefti uygulamalarını içeren tedavi protokollerinin karşılaştırılması
A comparative clinical evaluation of titanium prepared platelet rich fibrin and subepithelial connective tissue graft for management of multiple gingival recession defects
BİLGE CANSU UZUN
- Sabit ortodontik tedavi sonrası farklı oral hijyen protokollerinin diş eti iyileşmesi üzerindeki etkisinin incelenmesi
Comparison of different oral hygiene protocols in gingival recovery after fixed appliance treatment
GÜLCAN DANACI KAYA
- Molar insizör hipomineralizasyonundan etkilenmiş daimi dişlerde farklı hassasiyet giderici tedavi protokollerinin başarıdüzeylerinin değerlendirilmesi
Evaluation of the effectiveness of various desensitizing treatment protocols in permanent teeth affected by molar incisor hypomineralization
SAODAT RAUPOVA
Diş Hekimliği Uzmanlık
Türkçe
2025
Hacettepe ÜniversitesiÇocuk Diş Hekimliği Ana Bilim Dalı
Yükleniyor...
- Farklı yüzey temizleme işlemi uygulanmış güncel termoplastik kaide materyalinin yüzey pürüzlülüğü ve renk değişiminin incelenmesi
Investigation of surface roughness and color stability of the current thermoplastic denture base material with different surface cleaning process
ÜMMÜ HABİBE ERDAĞ
Diş Hekimliği Uzmanlık
Türkçe
2020
Zonguldak Bülent Ecevit ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
Yükleniyor...