Tek renk rezin kompozitlerin tamir bağlanma dayanımı üzerine farklı rezin kompozitlerin kullanımının ve yaşlandırmanın etkisinin in vitro olarak incelenmesi

In vitro investigation of the effect of different resin composites and aging on the repair bond strength of single shade resin composites

PDF İndir

  1. Tez No: 950984
  2. Yazar: SERRA YAREN YEŞİL
  3. Danışmanlar: PROF. DR. OYA BALA
  4. Tez Türü: Diş Hekimliği Uzmanlık
  5. Konular: Diş Hekimliği, Dentistry
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2025
  8. Dil: Türkçe
  9. Üniversite: Gazi Üniversitesi
  10. Enstitü: Diş Hekimliği Fakültesi
  11. Ana Bilim Dalı: Restoratif Diş Tedavisi Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: Belirtilmemiş.

Özet

Bu çalışmanın amacı, farklı tek renk rezin kompozitlerin (Omnichroma (OM), Essentia Universal (EU), Vittra APS Unique (VAU), Charisma Diamond ONE Shade (CDO) ve Zenchroma (ZC)) tamir bağlanma dayanım değerlerini karşılaştırmak ve bu rezin kompozitlerin tamir bağlanma dayanımı üzerine farklı rezin kompozitlerin kullanımının ve yaşlandırmanın etkisinin in vitro olarak incelemektir. Çalışmada teflon kalıplar kullanılarak, test edilen tek renk rezin kompozitlerin her birinden 40 adet olacak şekilde toplam 200 adet örnek hazırlandı. Hazırlanan örneklere 5-55 °C'de 10.000 defa ısısal döngü testi uygulandıktan sonra, örneklerin yüzeyleri 320 gritlik silikon karpit kâğıt ile zımparalandı. Takiben, örnek yüzeylerine kumlama yapıldı, silan ve sonrasında üniversal adeziv (Scotchbond Universal Plus) self-etch modunda uygulandı. Test edilen tek renk rezin kompozitlerin her biri için hazırlanan örnekler her grupta 20 adet örnek olacak şekilde öncelikle iki farklı gruba ayrıldı. Daha sonra, hazırlanan örnek yüzeylerinin üzerine tam ortasında olacak şekilde tygon tüp yerleştirildi. Tüplerin içerisine test örneğinin hazırlanmasında kullanılan tek renk rezin kompozitin kendisi veya nano-dolduruculu rezin kompozit (Filtek Ultimate-FU) yerleştirilerek tamir uygulaması yapıldı. Takiben, her bir tek renk rezin kompozit için hazırlanan örnekler her grupta 10 adet olacak şekilde iki farklı gruba ayrıldı. Gruplardan birine tamir uygulamasından sonra ısısal döngü testi uygulanmadı. Diğer gruba ise 5-55 °C arasında değişen, 10.000 döngü ısısal döngü testi tekrar uygulandı. Bu uygulamadan sonra, örneklerin tamir bağlanma dayanımı universal test cihazı kullanılarak ölçüldü. Bağlanma dayanım testinden sonra, örneklerin kopma yüzeyindeki kırılma tipi stereomikroskopta incelendi ve kırılma tipleri kaydedildi. Ayrıca, örnek yüzeylerinde alüminyum oksit ile kumlama ve yaşlandırma sonrasında oluşan değişim taramalı elektron mikroskop (SEM-EDS) ile incelendi. Çalışmada elde edilen bulguların istatistiksel analizi 0,05 anlamlılık düzeyinde Kruskal Wallis testi ile ve tüm grupların ikili karşılaştırılmasında Mann Whitney U testi kullanılarak gerçekleştirildi. Çalışmada ısısal döngüye tabi tutulmayan ve örnek hazırlamada kullanılan materyalin kendisiyle tamir uygulaması yapılan grupta en yüksek ortalama bağlanma dayanım değerlerinin CDO ile tamir materyali olarak FU'in kullanıldığı gruplarda ise ZC ile elde edildiği görüldü (p<0,05). Isısal döngü uygulandığında ise yine en yüksek ortalama bağlanma dayanım değerleri CDO ile tamir materyali olarak FU'in kullanıldığı gruplarda ise EU ile hazırlanan örneklerden elde edildi (p<0,05). Test edilen tek renk rezin kompozitlerin hem ısısal döngü testinin uygulandığı hem de uygulanmadığı durumlarda, tamir bağlanma dayanım değerlerinin kullanılan tamir materyaline göre farklılık gösterdiği görüldü. Ayrıca, tamir bağlanma dayanım değerlerinin ısısal döngü testi uygulaması sonrası anlamlı derecede azalma eğilimi gösterdiği saptandı (p<0,05). Bu çalışmanın sınırlamaları dahilinde, tek renk rezin kompozitlerin tamir bağlanma dayanım değerleri üzerinde test edilen rezin kompozitlerin ve tamir materyali olarak kullanılan rezin kompozitin yapısal özellikleri ile birlikte tamir uygulaması sonrası yaşlandırma uygulamasının etkisinin olduğu vurgulanabilir.

Özet (Çeviri)

The aim of this study is to compare the repair bond strength values of different single shade resin composites (Omnichroma (OM), Essentia Universal (EU), Vittra APS Unique (VAU), Charisma Diamond ONE Shade (CDO), and Zenchroma (ZC)) and to investigate in vitro the effects of using different resin composites and aging on the repair bond strength of these resin composites. In the study, a total of 200 samples were prepared using teflon molds, with 40 samples in each of the single shade resin composites tested. After subjecting the prepared samples to 10.000 thermal cycle tests at 5-55 °C, the surfaces of the samples were sanded with 320-grit silicon carbide paper. Subsequently, the sample surfaces were sandblasted, silane was applied, and then universal adhesive (Scotchbond Universal Plus) was applied in self-etch mode. The samples prepared for each of the single shade resin composites tested were first divided into two different groups, with 20 samples in each group. Then, a tygon tube was placed in the center of the prepared sample surfaces. The repair was performed by placing either the single-shade resin composite itself or the nano-filled resin composite (Filtek Ultimate-FU) used in the preparation of the test sample into the molds. The samples prepared for each single-shade resin composite were further divided into two different groups, with 10 samples in each group. One group was not subjected to a thermal cycle test after the repair application. The other group was subjected to a thermal cycle test with 10.000 cycles ranging from 5 to 55 °C. After this application, the repair bond strength of the samples was measured using a universal testing machine. After the bond strength test, the fracture type on the fracture surface of the samples was examined under a stereomicroscope, and the fracture types were recorded. Additionally, the changes on the sample surfaces after sandblasting with aluminum oxide and aging were examined using a scanning electron microscope (SEM-EDS). The statistical analysis of the findings obtained in the study was performed using the Kruskal-Wallis test at a significance level of 0.05 and the Mann-Whitney U test for pair-wise comparisons of all groups. In the study, the highest mean bond strength values were obtained with CDO in the group that was not subjected to thermal cycling and in which the same material used for sample preparation was also used for the repair, while in the groups where FU was used as the repair material, the highest values were observed with ZC (p<0.05). When thermal cycling was applied, the highest mean bond strength values were again obtained with CDO, and in the groups where FU was used as the repair material, the highest values were achieved with specimens prepared using EU (p<0.05). When the obtained mean repair bond strength values were compared according to the repair material used, it was observed that the repair bond strength values of the single-shade resin composites tested differed according to the repair material used, both in cases where the thermal cycling test was applied and where it was not applied. Additionally, it was determined that the repair bond strength values showed a significant decrease after the thermal cycling test (p<0.05). Within the limitations of this study, it can be emphasized that the structural properties of the tested resin composites, the resin composite used as the repair material, and the aging application after the repair procedure have an effect on the repair bond strength values of single-shade resin composites.

Benzer Tezler

  1. Tez No

    740848

    Investigation of the microstructural and mechanical properties of Al/TiB2 composites produced by cold spray additive manufacturing

    Soğuk sprey eklemeli imalat yöntemi ile üretilen Al/TiB2 kompozitlerinin mikroyapı ve mekanik özelliklerinin incelenmesi

    NERGİZ İLHAMİ MERT

    Yüksek Lisans

    İngilizce

    İngilizce

    2022

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. MURAT BAYDOĞAN

  2. Tez No

    763790

    Farklı yüzey hazırlık işlemleri uygulanan indirekt restoratif materyallerin üniversal renk kompozitlerle tamirinin değerlendirilmesi

    Evaluation of the repair of indirect restorative materials with different surface treatments and universal shade composites

    BÜŞRA KARABULUT GENÇER

    Doktora

    Türkçe

    Türkçe

    2022

    Diş HekimliğiMarmara Üniversitesi

    Restoratif Diş Tedavisi Ana Bilim Dalı

    DOÇ. DR. BİLGE TARÇIN

  3. Tez No

    897669

    Farklı protetik materyallerin tamirinde kullanılan tek-renkli kompozit rezinlerin optik özelliklerinin değerlendirilmesi

    Evaluation of optical properties of single-color composite resins used in repair of different prosthetic materials

    İLAYDA AYVAZ

    Diş Hekimliği Uzmanlık

    Türkçe

    Türkçe

    2024

    Diş HekimliğiPamukkale Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    DOÇ. DR. IŞIL KARAOKUTAN

  4. Tez No

    254

    Cam ve plastik seraların sonbahar domates üretimi yönünden karşılaştırılması

    Başlık çevirisi yok

    ERGUN DURAN

    Yüksek Lisans

    Türkçe

    Türkçe

    1985

    ZiraatEge Üniversitesi

    Bahçe Bitkileri Ana Bilim Dalı

    PROF. DR. AYTEN SEVGİCAN

  5. Tez No

    8

    Eksternal etmoidektomiler

    Başlık çevirisi yok

    ERCÜMENT AKMAN

    Tıpta Uzmanlık

    Türkçe

    Türkçe

    1987

    Kulak Burun ve BoğazGazi Üniversitesi

    Kulak Burun Boğaz Ana Bilim Dalı

    PROF.DR. NECMETTİN AKYILDIZ

Geri Dön