Farklı yüzey işlemleri uygulanan lityum disilikat seramiklerin tamir materyaline bağlanma dayanımının değerlendirilmesi

Evaluation of the shear bond strength between repair material and lithium disilicate ceramics subjected to different surface treatments

PDF İndir

  1. Tez No: 962977
  2. Yazar: BURCU YILDIRIM
  3. Danışmanlar: PROF. DR. CEMAL AYDIN
  4. Tez Türü: Diş Hekimliği Uzmanlık
  5. Konular: Diş Hekimliği, Dentistry
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2025
  8. Dil: Türkçe
  9. Üniversite: Gazi Üniversitesi
  10. Enstitü: Diş Hekimliği Fakültesi
  11. Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: Belirtilmemiş.

Özet

Bu çalışmanın amacı, farklı yüzey işlemleri uygulanan lityum disilikat seramiklerin tamir materyaline makaslama bağlanma dayanımını değerlendirmektir. Bu kapsamda üç farklı CAD-CAM lityum disilikat seramiği olan GC Initial LiSi (GC), CEREC Tessera (CEREC), IPS e.max CAD (EMAX) kullanılarak toplam 180 örnek hazırlandı. Tüm örneklere termal siklus uygulandı. Örnekler frezle pürüzlendirme, alüminyum oksit ile kumlama ve %5 hidroflorik asitle pürüzlendirme olmak üzere üç farklı yüzey işlemine tabi tutuldu. Yüzey pürüzlülükleri ölçüldü ve tamir kompoziti uygulandı. Örneklerin yarısı ilave olarak termal yaşlandırmaya maruz bırakıldı. Lityum disilikat örnekler ve tamir kompoziti arasındaki makaslama bağlanma dayanımı test edildi. Farklı lityum disilikat seramikler ve yüzey işlemlerinin Ra ölçüm değeri üzerindeki etkisi iki yönlü faktöriyel ANOVA ile, farklı lityum disilikat seramikler, yüzey işlemleri ve yaşlandırma uygulanma durumunun makaslama bağlanma dayanım üzerindeki etkisi üç yönlü faktöriyel ANOVA ile incelendi. Yüzey pürüzlülüğü (Ra) en yüksek kumlama grubunda, makaslama bağlanma dayanımı ise yaşlandırılmayan GC seramiğinde HF asidi uygulanan grupta ölçüldü. En düşük bağlanma dayanımı, frez ile pürüzlendirilen ve yaşlandırılan EMAX seramikte görüldü. Yaşlandırmanın, bağlanma dayanımını tüm gruplarda belirgin şekilde azalttığı saptandı. Başarısızlık tipleri seramik türü, yüzey işlemi ve yaşlandırma durumuna göre farklılık gösterdi. Yaşlandırma sonrası adeziv kırık oranlarında genel bir artış gözlendi; ancak EMAX seramikte HF uygulamasını takiben yaşlandırma sonrasında karma tip kırıklar daha baskın hale geldi.

Özet (Çeviri)

The aim of this study is to evaluate the shear bond strength between repair composite and lithium disilicate ceramics subjected to different surface treatments. For this purpose, a total of 180 specimens were prepared using three different CAD-CAM lithium disilicate ceramics: GC Initial LiSi (GC), CEREC Tessera (CEREC), and IPS e.max CAD (EMAX). All specimens underwent thermal cycling. They were divided into three surface treatment groups: surface roughening with a diamond bur, sandblasting with aluminum oxide particles, and etching with 5% hydrofluoric acid. Surface roughness (Ra) was measured, and repair composite was applied. Half of the specimens were additionally subjected to thermal aging. Shear bond strength between the lithium disilicate ceramics and the repair composite was tested. The effects of ceramic type and surface treatment on Ra values were analyzed using two-way factorial ANOVA, while the effects of ceramic type, surface treatment, and aging on shear bond strength were evaluated using three-way factorial ANOVA. Surface roughness was highest in the sandblasted group, while the highest shear bond strength was observed in the non-aged GC group treated with hydrofluoric acid. The lowest bond strength was found in the aged EMAX specimens treated with a diamond bur. Aging significantly reduced bond strength across all groups. Failure modes varied depending on the ceramic type, surface treatment, and aging condition. A general increase in adhesive failure rates was observed after aging. However, in the EMAX group, mixed failures became predominant after hydrofluoric acid treatment followed by aging.

Benzer Tezler

  1. Tez No

    555862

    İndirekt laminate veneer restorasyonlara uygulanan farklı tamir yaklaşımlarının makaslama bağlanma kuvveti ile değerlendirilmesi

    Evaluation of shear bond strength of different repair procedures applied to indirect laminate veneers

    ABDELRAHMAN WASFI FAYEZ MUSTAFA

    Doktora

    Türkçe

    Türkçe

    2019

    Diş HekimliğiGazi Üniversitesi

    Diş Hastalıkları ve Tedavisi Ana Bilim Dalı

    DOÇ. DR. SUAT ÖZCAN

  2. Tez No

    202

    Bazı esterlerin kinetik incelenmesi ve termodinamik parametrelerin belirlenmesi

    Kinetic study and detesmination of thermodnamic parameters of some esters

    İBRAHİM TAŞ

    Yüksek Lisans

    Türkçe

    Türkçe

    1986

    Kimya MühendisliğiUludağ Üniversitesi

    Kimya Ana Bilim Dalı

    PROF. DR. MUSTAFA CEBE

  3. Tez No

    252

    İzmir'de bazı yolların kapatılarak yaya bölgeleri oluşturma da kent peyzajını geliştirme açısından yeniden planlanması üzerinde araştırmalar

    Başlık çevirisi yok

    BAHAR TÜRKYILMAZ

    Yüksek Lisans

    Türkçe

    Türkçe

    1985

    Şehircilik ve Bölge PlanlamaEge Üniversitesi

    Şehir ve Bölge Planlama Ana Bilim Dalı

  4. Tez No

    7

    Testosteron dihidrotestosteron ve östrojenin benign prostat hiperplazisindeki etyolojik rolleri

    The roles of testosterone, dihydrotestosterone and estradiole on the etiology of benign prostatic hyperplasia

    HALUK TOKUÇOĞLU

    Tıpta Uzmanlık

    Türkçe

    Türkçe

    1986

    ÜrolojiGazi Üniversitesi

    Üroloji Ana Bilim Dalı

  5. Tez No

    10

    Süt formüllerinin tüketim uygulamaları ve süt formüllerinin C vitamini içeriği ile pH değerleri

    Başlık çevirisi yok

    GÖNÜL VAROL

    Yüksek Lisans

    Türkçe

    Türkçe

    1986

    Besin Hijyeni ve Teknolojisiİstanbul Üniversitesi

    Çocuk Gelişimi Ana Bilim Dalı

    DOÇ. DR. TÜRKAN KUTLUAY

Geri Dön