Zirkonya seramik, lityum disilikat cam seramik ve zirkonya ile güçlendirilmiş lityum silikat cam seramiklere uygulanan farklı yüzey işlemlerinin, kompozit rezinlerin tamir bağlanma dayanımı üzerine etkisi
The effect of different surface treatments on repair bond strength of resin composite to zirconia ceramic, lithium disilicate glass ceramic and zirconia reinforced lithium silicate glass ceramic
- Tez No: 426974
- Danışmanlar: PROF. DR. GÜLFEM ERGÜN
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: CAD/CAM, yüzey işlemleri, hidroflorik asit, kumlama, lazer, kompozit rezin, makaslama bağlanma dayanımı, Dental bonding, Dental stres analizi, Kompozit reçineler, Lazerler, Yüzey özellikleri, CAD/CAM, surface treatments, hydrofluoric acid, sandblasting, laser, resin composite, shear bond strengt, Dental bonding, Dental stress analysis, Composite resins, Sanding, Lasers, Surface properties
- Yıl: 2016
- Dil: Türkçe
- Üniversite: Gazi Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışmanın amacı; kompozit rezinlerin 3 farklı CAD/CAM bloğuna (monolitik veya iki farklı veneer seramiği ile veneerlenmiş olarak lityum disilikat cam seramik, itriyum ile stabilize zirkonyum oksit seramik ve zirkonya ile güçlendirilmiş lityum silikat cam seramikler) makaslama bağlanma dayanımları üzerine yüzey işlemlerinin etkilerini termosiklus sonrasında değerlendirmektir. Test materyalleri yüzey işlem tekniğine göre sekiz alt gruba ayrılmıştır (Grup 1: hidroflorik asit + silan + bond, Grup 2: kumlama + silan + bond, Grup 3: lazer + silan + bond, Grup 4: hidroflorik asit + silan, Grup 5: kumlama + silan, Grup: 6: lazer + silan, Grup 7: silan + bond, Group 8: silan). Ek olarak, iki farklı bağlanma sistemi kullanılmıştır. Sonrasında, kompozit rezin tüm örnek yüzeylerine uygulanmıştır. Ardından, örnekler 370C'de 24 saat distile suda bekletilmiştir. Örneklerin yarısı termosiklusa maruz bırakılmıştır ve diğer yarısı 370C'de distile suda bekletilmiştir. Sonrasında, örnekler makaslama bağlanma dayanımı testine tabi tutulmuştur. Kırık tipleri, optik mikroskop ve SEM kullanılarak değerlendirildi. Veriler, Mann Whitney U, Kruskal Wallis ve post-hoc testler ile analiz edildi (p<0,05). İstatistiksel analizler; seramik tipinin, yüzey işlemi tekniğinin ve termosiklusun makaslama bağlanma dayanımı değerleri üzerinde belirgin etkiye sahip olduğunu göstermiştir (p<0,05). Ancak, veneerleme işlemi makaslama bağlanma dayanımı değerlerini etkilememiştir (p=0,046). Kompozit rezinlerin farklı CAD/CAM seramik yüzeylerine tamir bağlanma kapasitelerinin arttırılması için uygun yüzey işlemlerinin kullanılması önerilmektedir.
Özet (Çeviri)
The aim of this study was to evaluate the effect of surface treatments on the shear bond strength of resin composites to three different CAD/CAM blocks (lithium disilicate glass ceramic, yttrium stabilized zirconia ceramic and zirconia reinforced lithium silicate glass ceramic as monolithic or veneered with two different veneering ceramics) following thermocycling. The tested materials were divided into eight subgroups according to the surface treatment technique (Group 1: hydrofluoric acid + silane + bond, Group 2: sandblasting + silane + bond, Group 3: laser + silane + bond, Group 4: hydrofluoric acid + silane, Group 5: sandblasting + silane, Group: 6: laser + silane, Group 7: silane + bond, Group 8: silane). In addition, two different adhesive systems were used. Then resin composite was applied to the surfaces of all specimens. Afterwards, they were stored in distilled water for 24 hours at 370C. The half of the specimens were exposed to thermocycling procedure and the other half were stored in distilled water at 370C. Then specimens were subjected to universal testing machine for shear bond strength test. Failure modes were examined using an optical microscope and SEM. The data were analyzed with Mann Whitney U, Kruskal Wallis and post-hoc tests (p<0,05). Statistical analysis revealed that the ceramic type, surface treatment technique and thermocycling had significant effects on the shear bond strength values (p<0,05). However, veneering procedure had not affected the shear bond strength values (p=0,046). To improve the repair bonding capability of resin composites to different CAD/CAM ceramics, use of appropriate surface treatments are suggested.
Benzer Tezler
- Zirkonya seramik ve zirkonya ile güçlendirilmiş lityum disilikat cam seramiklere uygulanan farklı yüzey işlemlerinin, rezin simanların bağlanma dayanımı üzerine etkisi
The effect of different surface treatments applied to zirconia ceramic and zirconia reinforced lithium dissilicate glass ceramics on the bonding strength of resin cements
ÖZGE GÜRGENLİ
Diş Hekimliği Uzmanlık
Türkçe
2023
Diş HekimliğiSivas Cumhuriyet ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. HAKAN DEMİR
- Farklı alt yapı ve üst yapı oranlarının tüm seramik sistemlerinde bağ dayanımına etkisinin mekanik yöntemlerle araştırılması
Evaluating the effect of various core and veneer ratio to all ceramic systems bond strength by mechanic methods
CENNET ELÇİN SAĞIRKAYA
Doktora
Türkçe
2010
Diş HekimliğiEge ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. CELAL ARTUNÇ
- Farklı yöntemlerle üst yapıları hazırlanan zirkonya destekli kron restorasyonlarının kırılma dayanımlarının araştırılması
Evaluation of the fracture strength of zirconia supported crown restorations veneered with different methods
BURCU KANAT
Doktora
Türkçe
2013
Diş HekimliğiEge ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. MEHMET ALİ GÜNGÖR
- Güncel CAD/CAM seramik bloklarında farklı yüzey işlemlerinin makaslama bağlanma dayanımına etkisinin incelenmesi
Evaluation of different surface treatments to shear bond strength on current CAD/CAM blocks
ONUR ETÖZ
Diş Hekimliği Uzmanlık
Türkçe
2015
Diş HekimliğiOndokuz Mayıs ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. MURAT KURT
- Er:YAG lazerin farklı seramiklerden transmisyonu
Transmission of Er:YAG laser through different ceramics
FADİME ZEHRA DOLGUN
Doktora
Türkçe
2016
Diş HekimliğiGaziantep ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
YRD. DOÇ. DR. FATİH SARI
PROF. DR. ASUDE DİLEK NALBANT