Sepiyolitten karbo-termal indirgeme ve nitrürleme yoluyla silisyum nitrür (Si3N4) seramik tozu üretimi parametrelerinin araştırılması

Investigation of parameters relating to silicon nitride (Si3N4) powder production from sepiolite by carbo-thermal reduction and nitridation

  1. Tez No: 55167
  2. Yazar: HALİL ARIK
  3. Danışmanlar: PROF.DR. SÜLEYMAN SARITAŞ
  4. Tez Türü: Doktora
  5. Konular: Eğitim ve Öğretim, Makine Mühendisliği, Education and Training, Mechanical Engineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 1996
  8. Dil: Türkçe
  9. Üniversite: Gazi Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Makine Eğitimi Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 133

Özet

SEPİYOLİTTEN KARBO-TERMAL İNDİRGEME VE NİTRÜRLEME YOLUYLA SİLİSYUM NİTRÜR (Si3N4) SERAMİK TOZU ÜRETİMİ PARAMETRELERİNİN ARAŞTIRILMASI (DOKTORA TEZİ) HALİL ARIK GAZİ ÜNİVERSİTESİ FEN BİLİMLERİ ENSTİTÜSÜ MAYIS 1996 ÖZET Bu çalışmada, sepiyotitten karbo-termal indirgeme ve nitrürleme yoluyla Sİ3N4 seramik tozu üretimi parametreleri araştırılmıştır. Sepiyolit, Dünya rezervlerinin %70'i Türkiyede bulunan yarım birim hücre için ideal formülü Mg8 Sİ12 O30 (OH)4 (OH2)4 8H20 olan bir magnezyum hidrosilikat kil mineralidir. Sİ3N4 seramik tozu üretimi için, Ankara - Polatlı güneyindeki Türktaciri bölgesinden alınan kahverengi sepiyolit hidrometalurjik (liç) metodu ile zenginleştirilerek büyük oranda dolamitten arındırılmıştır. 100 Meş elek altı zenginleştirilmiş kahverengi sepiyolit 325 Meş elek altı karbon karası ile C/SİO2 molar oranlan 1.5,3,4,5 ve 7.5 olacak şekilde karıştırılmıştır. Karıştırma-öğütme işlemi 5 saat süreyle atumina bilyalı döner tambur içerisinde yapılmıştır. Karışım numuneler grafit kayıklar içinde atmosfer kontrollü tüp fırında değişik sıcaklıklarda (1200-1 300-1 400-1 450°C) ve deney sürelerinde (2-4-8-16 saat) akış debisi 4.5 cm3/dak olan azot (N2) gazı akışı altında karbo-termal indirgeme ve nitrürleme (KTİN) işlemine tabi tutulmuştur. KTİN sonrası elde edilen bütün numunelerin XRD analizleri yapılarak dönüşümler ve miktarları, SEM-EDX analizleri yapılarak ta dönüşümlerin morfolojik yapısı ve kimyasal bileşimi belirlenmiştir. Yapılan analizler 1400 °C'de C/SİO2 molar oranı 4 olan ve 16 saat KTİN işlemi gören numunede % 100'e yakın Si3N4 dönüşümü olduğunu göstermiştir. Bilim kodu : 225.01.00.225.01.01 Anahtar Kelimeler : Sepiyolit, Nitrür Seramikler, Si3N4, Karbo-Termal İndirgeme Sayfa Adedi : 143 Tez Yöneticisi : Prof.Dr. Süleyman SARITAŞ IV

Özet (Çeviri)

INVESTIGATION OF PARAMETERS RELATING TO SILICON NITRIDE (Sİ3N4) POWDER PRODUCTION FROM SEPIOLITE BY CARBO-THERMAL REDUCTION AND NITRIDATION Ph. D Thesis Halil ARIK GAZİ UNIVERSITY INSTITUTE OF SCIENCE AND TECHNOLOGY May 1996 ABSTRACT In this work, investigation of parameters relating to silicon nitride (Si3N4) powder production from sepiolite by carbo-thermal reduction and nitridation was investigated. About 70% of World reserves for sepiolite is in Turkey. It is a magnesium hydro-silicate clay mineral with half unit cell ideal formula of Mga Sİ12 O30 (OH)4 (OH2)4 8H20. Sepiolite from Ankara - Polatlı - Türktaciri area was concentrated using hydro-metallurgical leach method. In this way about 10 % dolomite present in the brown sepiolite was disolved and 100% pure sepiolite was obtained. Minus 100 mesh sepiolite was mixed with minus 325 mesh carbon black with C/Si02 molar ratios of 1.5, 3.0, 4.0, 5.0 and 7.5. Mixing was carried out by milling for 5 hours in a ball mill with alumina balls. 5 grams of these mixtures were placed in graphite boats and then located at the centre of controlled atmosphere tube furnace with alumina tube. Carbo- thermal reduction and nitridation was carried out under 4.5 cm3/min N2 gas flow. Treatment temperatures were 1200-1300-1400 and 1450 °C and times were 2-4-8-16 hours. All reaction products were analysed by XRD and SEM- EDX; morphologies and chemical compositions were determined. Results showed that after 16 hours of treatment at 1400 °C with C/Si02 molar ratio of 4, transformation to Si3N4 formation was nearly 1 00%. Science Code : 225.01.00.225.01.01 Key Words : Sepiolite, Nitride Ceramics, Si3N4, Carbo-Termal Reduction Number of Pages : 143 Supervisor : Prof. Dr. Süleyman S ARITAŞ V

Benzer Tezler

  1. Sepiyolitten silisyum nitrür (Si3N4) tipi teknolojik seramik malzeme üretimi ve karakterizasyonu

    Production of silicon nitride (Si3N4) type technological ceramic material from sepiolite and its characterization

    CENGİZ BAĞCI

    Doktora

    Türkçe

    Türkçe

    2007

    Metalurji MühendisliğiGazi Üniversitesi

    Metal Eğitimi Ana Bilim Dalı

    DOÇ. DR. HALİL ARIK

  2. Seçilmiş doğal, sentezlenmiş ve ticari adsorban materyallerin ham yağ ağartma kapasitelerinin araştırılması

    Başlık çevirisi yok

    ELİF YÜCETEPE

    Yüksek Lisans

    Türkçe

    Türkçe

    2022

    Gıda MühendisliğiÇanakkale Onsekiz Mart Üniversitesi

    Gıda Mühendisliği Ana Bilim Dalı

    PROF. DR. EMİN YILMAZ

  3. Granit bünyesinde sepiyolit katkısı kullanılarak teknik özelliklerinin incelenmesi

    Investigation of technical properties of granite tile body using sepiolite additive

    ÖZGE ERTÜRK

    Yüksek Lisans

    Türkçe

    Türkçe

    2007

    Seramik MühendisliğiAfyon Kocatepe Üniversitesi

    Seramik Mühendisliği Ana Bilim Dalı

    YRD. DOÇ. DR. TANER KAVAS

  4. Sivrihihar Yenidoğan (Eskişehir) sepiyolitleri kullanılarak ince karo imalat olanaklarının araştırılması

    Tile manufacture utilizing Sivrihisar Yenidoğan (Eskişehir) sepiolites

    VELİ UZ

    Yüksek Lisans

    Türkçe

    Türkçe

    1999

    Maden Mühendisliği ve MadencilikDumlupınar Üniversitesi

    Maden Mühendisliği Ana Bilim Dalı

    DOÇ. DR. İSKENDER IŞIK

  5. Seramik filtre üretimi

    Production of ceramic filter

    KÜRŞAT SAVAŞ

    Yüksek Lisans

    Türkçe

    Türkçe

    2002

    Metalurji MühendisliğiGebze Yüksek Teknoloji Enstitüsü

    Malzeme Bilimi ve Makine Mühendisliği Ana Bilim Dalı

    YRD. DOÇ. DR. E. BÜLENT HEKİMBAŞI